Roughness evolution of metallic implant surfaces under contact loading and nanometer-scale chemical etching

Sliding Corrosion Fatigue of Metallic Joint Implants: A Comparative Study of CoCrMo and Ti6Al4V in Simulated Synovial Environments

Mechanical contact in a corrosive synovial environment leads to progressive surface damage at the modular interface of the joint implants. The wear debris and corrosion products degrade the synovial fluids and change the lubrication mechanisms at the joints. Consequently, the unstable joint lubrication and corrosion products will further induce the undesirable performance of the joint implants. In this study, the two major joint materials, CoCrMo and Ti6Al4V, were tested during the course of reciprocal sliding contact in simulated synovial liquids. Open circuit potential and coefficient of friction were monitored to describe electrochemical and mechanical responses. Potentiostatic test results illustrated electrochemical damage on both surfaces that modified oxidation chemistry on both surfaces. However, more significant modification of the CoCrMo surface was detected during wear in the simulated joint liquid. Even with a reduced coefficient of friction on the CoCrMo surface in sodium lactate environments, fretting current density drastically increased in corrosive sodium lactate with pH 2. However, the test results from the Ti6Al4V surface presented less coefficient of friction values, and moderate change in fretting current. Therefore, the experimental study concluded that the biocompatibility of Ti6Al4V is superior to that of CoCrMo in the combined effect of mechanical loadings and an electrochemical environment.