Thermal cycling effects on adhesion of resin-bovine enamel junction among different composite resins

Effect of Prolonged Water Aging on the Bond Strength and Marginal Seal of Three Novel Restorative Materials

AIM

To assess and contrast the shear bond strength (SBS) and microbial leakage of Cention-N, Fuji IX, and nanohybrid composite restorative materials after being exposed to prolonged water aging.

MATERIALS AND METHODS

A total of 30 self-curing acrylic blocks were prepared for SBS analysis. Extracted teeth were affixed on the acrylic resin to incorporate the root section. To expose the occlusal dentin, 3 mm of the midcoronal portion was sectioned. The sectioned samples were allocated into the following three groups: Group I: Fuji IX; group II: Filtek Z350; and group III: Cention-N. Cylindrical plastic tubing was used to place each material as directed by the manufacturer and water aging for 7, 14, and 28 days at 37°C. Also, a universal testing machine (UTM) was utilized for testing followed by a scanning electron microscope (SEM). For microleakage analysis, a total of 30 class-V cavities were prepared. The prepared samples were allotted to respective groups; Later, 200 thermocycles at 5°C and 55°C were applied for 30 seconds to mimic the oral environment. The root apices sealed with sticky wax and the exception of a 1-mm around the edges of the restorations were then painted twice with clear nail varnish and submerged in 0.5% basic fuchsin dye at 37°C. Samples were washed, dried, and sectioned longitudinally followed by stereomicroscopic evaluation.

RESULTS

Groups I (0.083), group II (0.083), and group III (0.102) did not show significant variation in the SBS after water degradation. At the end of 28 days of water aging, group III showed 33.3% adhesive failure and 66.7% mixed failure mode. For marginal leakage in group III, the mean and standard deviation (SD) were 334.90 ± 418.454 with the p = 0.001 showing a significant difference compared to groups I and II.

CONCLUSION

Compared to nanohybrid composite and Fuji IX, Cention-N showed a superior SBS after being exposed to water aging and exhibited lesser marginal leakage.

CLINICAL SIGNIFICANCE

Cention-N outperformed in its marginal adaptation with superior shear resistance and can be considered as an alternative bulk filling material.

Preliminary comparison of the remineralization and desensitization effects of a novel mineralized ion-releasing toothpaste and commercially available competitive products

Background/purpose

Toothpaste plays an important role in brushing teeth to maintain oral hygiene and health. The purpose of this study was to develop a new toothpaste containing surface nanocrystal-rich dicalcium phosphate anhydrous (DCPA) powder and to investigate its effect on tooth samples.

Materials and methods

The innovative toothpaste (REALCaP®/Group R) was compared with two commercial toothpastes (BioRepair®/Group B and Sensodyne®/Group S). Brushing cycle tests were performed on bovine tooth slices coated with individual toothpaste and a control group without toothpaste (Group C). Microhardness, roughness, surface structure observation, and X-ray diffraction (XRD) were performed on cycle days 4, 7, and 14 to analyze the impact of the toothpastes on tooth samples.

Reults

Microhardness in the Group R was higher than that of the other groups regardless of the cycle days. Roughness in the Group R increased on days 4 and 7 but decreased on day 14. Roughness in the groups S and B increased with days. Microstructural observation revealed that most exposed dentinal tubules had been sealed in the Group R on day 14. Overlay thickness in the Group R was significantly higher than that in the groups S and B on days 4, 7, and 14. XRD analysis showed no hydroxyapatite (HA) peak in the Group S. The HA peak in the Group R was higher than that in the Group B on day 14.

Conclusion

The innovative toothpaste has better properties than the commercially available products in terms of microhardness, roughness, and effectiveness in sealing dentinal tubules.

Polymerization characteristics of colored compomers cured with different LED units

Aim:

Incomplete polymerization of a resin material used for dental restoration affects the properties of the restoration. We evaluated the structural and mechanical properties of three different colored compomers cured with three different LED units to observe the characteristic changes occurring in different matches.

Methods:

Polytetrafluoroethylene molds (5 mm in diameter and 2 mm in thickness) were used to prepare disk-shaped sample specimens. Nine sample groups (each of five specimens) were prepared, three each of different compomer resin colors (gold, berry, and silver). Samples were cured using three different LED units (Optima, VALO, and Demi Ultra), according to the manufacturers’ instructions. Microstructural properties of samples were characterized by determining the degree of curing using Fourier-transform infrared spectroscopy and by analyzing sample morphology under a scanning electron microscope. The Vickers hardness, compressive strength, and elastic modulus of the samples were measured to investigate their mechanical properties.

Results:

The degrees of curing decreased in the order of silver > berry > gold for all curing units. Conversely, gold compomers exhibited poorer mechanical values than the berry and silver counterparts. The Optima 10 unit yielded slightly higher degrees of curing than the other devices, followed by Demi Ultra and VALO light-curing units, respectively.

Conclusion:

The resin color affected the structural and mechanical properties of the compomers, possibly as a result of the complex interactions and relationships between the irradiation light and resin material, such as light absorbance and reflectance; thus, depending on the color as well as the curing protocol.