Microscale tribological behavior and in vitro biocompatibility of graphene nanoplatelet reinforced alumina

Advanced progress on the significant influences of multi-dimensional nanofillers on the tribological performance of coatings

Over the past two decades, nanofillers have attracted significant interest due to their proven chemical, mechanical, and tribological performances. However, despite the significant progress realized in the application of nanofiller-reinforced coatings in various prominent fields, such as aerospace, automobiles and biomedicine, the fundamental effects of nanofillers on the tribological properties of coatings and their underlying mechanisms have rarely been explored by subdividing them into different sizes ranging from zero-dimensional (0D) to three-dimensional (3D) architectures. Herein, we present a systematic review of the latest advances on multi-dimensional nanofillers for enhancing the friction reduction and wear resistance of metal/ceramic/polymer matrix composite coatings. Finally, we conclude with an outlook for future investigations on multi-dimensional nanofillers in tribology, providing possible solutions for the key challenges in their commercial applications.

Sustainable Microfabrication Enhancement of Graphene Nanoplatelet-Reinforced Biomedical Alumina Ceramic Matrix Nanocomposites

Studies about adding graphene reinforcement to improve the microfabrication performance of alumina (Al₂O₃) ceramic materials are still too rare and incomplete to satisfy sustainable manufacturing requirements. Therefore, this study aims to develop a detailed understanding of the effect of graphene reinforcement to enhance the laser micromachining performance of Al₂O₃-based nanocomposites. To achieve this, high-density Al₂O₃ nanocomposite specimens were fabricated with 0 wt.%, 0.5 wt.%, 1 wt.%, 1.5 wt.%, and 2.5 wt.% graphene nanoplatelets (GNPs) using a high-frequency induction heating process. The specimens were subjected to laser micromachining. Afterward, the effects of the GNP contents on the ablation depth/width, surface morphology, surface roughness, and material removal rate were studied. The results indicate that the micro-fabrication performance of the nanocomposites was significantly affected by the GNP content. All nanocomposites exhibited improvement in the ablation depth and material removal rate compared to the base Al₂O₃ (0 wt.% GNP). For instance, at a higher scanning speed, the ablation depth was increased by a factor of 10 times for the GNP-reinforced specimens compared to the base Al₂O₃ nanocomposites. In addition, the MRRs were increased by 2134%, 2391%, 2915%, and 2427% for the 0.5 wt.%, 1 wt.%, 1.5 wt.%, and 2.5 wt.% GNP/Al₂O₃ nanocomposites, respectively, compared to the base Al₂O₃ specimens. Likewise, the surface roughness and surface morphology were considerably improved for all GNP/Al₂O₃ nanocomposite specimens compared to the base Al₂O₃. This is because the GNP reinforcement reduced the ablation threshold and increased the material removal efficiency by increasing the optical absorbance and thermal conductivity and reducing the grain size of the Al₂O₃ nanocomposites. Among the GNP/Al₂O₃ nanocomposites, the 0.5 wt.% and 1 wt.% GNP specimens showed superior performance with minimum defects in most laser micromachining conditions. Overall, the results show that the GNP-reinforced Al₂O₃ nanocomposites can be machined with high quality and a high production rate using a basic fiber laser system (20 Watts) with very low power consumption. This study shows huge potential for adding graphene to alumina ceramic-based materials to improve their machinability.

Microstructures, mechanical and corrosion properties of graphene nanoplatelet-reinforced zinc matrix composites for implant applications

Zinc (Zn)-based alloys and composites are gaining increasing interest as promising biodegradable implant materials due to their appropriate biodegradation rates and biological functionalities. However, the inadequate mechanical strength and ductility of pure Zn have restricted its application. In this study, Zn matrix composites (ZMCs) reinforced with 0.1-0.4 wt.% graphene nanoplatelets (GNP) fabricated via powder metallurgy were investigated as potential biodegradable implant materials. The microstructures, mechanical properties, and corrosion behaviors of the GNP-reinforced ZMCs were characterized using optical microscopy, scanning electron microscopy combined with energy-dispersive X-ray spectroscopy, Raman spectroscopy, compression testing, and electrochemical and immersion testing in Hanks' balanced salt solution (HBSS). The microstructural study revealed that the GNP was uniformly dispersed in the ZMCs after ball milling and sintering at 420°C for 6 h. The microhardness, compressive yield strength, ultimate compressive strength, and compressive strain of the ZMC-0.2GNP were 69 HV, 123 MPa, 247 MPa, and 23 %, respectively, improvements of ∼ 18 %, 50%, ∼ 28%, and ∼ 15% compared to pure Zn. The corrosion rate of the ZMCs were lower than that of the pure Zn in HBSS, and the ZMC-0.2GNP composite exhibited the lowest corrosion rate of 0.09 mm/y as measured by electrochemical testing. Biocompatibility assessment indicated that the diluted extracts of pure Zn and GNP-reinforced ZMCs with concentrations of 12.5% and 6.25% exhibited no cytotoxicity after cell culturing for up to 5 days, and the diluted extracts of ZMC-0.2 GNP composite revealed more than 90% cell viability after cell culturing of 3 days, showing the satisfying cytocompatibility. STATEMENT OF SIGNIFICANCE: Biodegradable Zn is a promising candidate material for orthopedic implant applications. Nonetheless, the inadequate mechanical strength and ductility of pure Zn limited its clinical application. In this study, Zn matrix composites (ZMCs) reinforced with 0.1-0.4 wt.% graphene nanoplatelets (GNP) were developed via powder metallurgy, and the reinforcing efficacy of GNP on their mechanical properties was investigated. The addition of GNP significantly improved the compressive properties of ZMCs, with the Zn-0.2GNP composite exhibiting the best compressive properties, including 123 MPa compressive yield strength, 247 MPa ultimate compressive strength, and 22.9% compressive strain. Further, the 12.5% concentration extract of the ZMCs exhibited no cytotoxicity after cell culturing for 5 d toward SaOS2 cells.

Enhanced Scratch Performance of Plasma Sprayed Hydroxyapatite Composite Coatings Reinforced with BN Nanoplatelets

In recent years, research on hydroxyapatite (HA) coatings has been driven by the demands of clinical applications. However, the intrinsic brittleness of HA limits its potential in the use for the load-bearing implant. To improve mechanical properties of the HA coating itself, a HA composite coating reinforced with hexagonal boron nitride nanoplatelets (BNNP) was fabricated using plasma spray, and its scratch behavior was investigated in this research. Typical brittle fractures such as microcracks both in and beyond the residual groove and material chipping were observed in the HA coating, while stronger and tougher BNNP/HA coatings exhibited a dominant role in protecting them from scratch damage through resisting plastic deformation and brittle microfracturing. Moreover, easier grain sliding within a splat and splat sliding at the splat boundaries due to the presence of BNNPs, and the nature porosity at different length scales of the as-sprayed HA composite coatings would provide significant self-lubricating effects to reduce the lateral force during scratching and alleviate the contact damage. Therefore, the addition of BNNPs renders HA coating with low scratch friction and enhanced tolerance to surface damage, which is naturally beneficial for the long-term durability and reliability of the implants.

The Promise of 2D Nanolaminated Materials as Protective Solid-State Lubricants

Lubricants are an important part of any tribological system [...]