Composite vs. ionomer vs. mixed restoration of wedge-shaped dental cervical lesions: Marginal quality relative to eccentric occlusal loading

Composite plastering technique (CPT) for anterior and posterior restorations

Composite plastering technique (CPT) is a novel restoration improvement technique for eliminating and re-contouring the marginal defects. Restoration-related interproximal contour deficiencies such as dark triangles beneath the contact point following direct class II restorations, the gaps at the interproximal cavity step following indirect cementations, and the gaps at the interproximal wall following class III restoration layering procedures can be corrected using the CPT. The technique may also be used as a layering step during the free-hand layering in diastema closure restorations. Contour deficiencies on interproximal surfaces which lead to the renewal of restoration and periodontal damages can be prevented by additional direct composite build-up using the CPT. The technique can be performed either immediately after the restoration directly or long after by using the composite repair protocol. It focuses on filling and re-contouring the surface of the deficiency by using a mylar strip actively under rubberdam isolation. Composite is loaded between the strip and the tooth surface and the strip is pulled slightly in palato-buccal or the opposite direction depending on the location of the defect, to fill it by plastering the composite. It may contribute the longevity of the restoration by improving the emergence profile and correcting the interproximal contour. Re-contouring of the interproximal surface defects by CPT is a useful approach to improve the esthetics as well as the function of anterior and posterior direct and indirect restorations which may also prolong the longevity.

B, Garoushi S. Fracture Behavior and Integrity of Different Direct Restorative Materials to Restore Noncarious Cervical Lesions

The purpose of this study was to analyze the fracture resistance and marginal leakage of noncarious cervical lesion (NCCL) restorations made of different restorative materials. Eighty upper premolars were randomly divided into four groups (n = 20/group). Standardized NCCL cavity preparations were performed on the buccal surface of the teeth and then restored with four different materials. Group 1: Packable resin composite (PC); Group 2: Highly flowable resin composite (HF); Group 3: Low flowable resin composite (LF); Group 4: Resin modified glass ionomer cement (RMGIC). After restorations were completed, cyclic and static fracture behavior was evaluated using a loading testing machine. Extra restored teeth were sectioned and then stained (n = 5/group). The specimens were viewed under a stereo microscope and the percentage of microgaps at the tooth–restoration interface was calculated. All restored teeth survived after fatigue loading. There was no statistically significant (p > 0.05) difference between the tested restorations after the static loading test. NCCLs restored with highly filled flowable composite showed the least microleakage among the tested groups (p < 0.05). The investigated restorative materials are acceptable for NCCL restorations in terms of fracture resistance and microleakage.

Repair bond strength and degradation of glass ionomer cements after mechanical and chemical challenges

Aim: Little is known about the reparability of glass ionomer cements (GICs) after storage in acid environments. The aim of this study was to evaluate the solubility and repairability of GICs immersed in acid solutions and subjected to brushing. Methods: Thirty discs of each GIC (Vitremer, VitroFil LC, VitroFil, and Maxxion R) were divided into three immersion groups: distilled water, Coca-Cola, or hydrochloric acid (HCl), then subjected to brushing. The weight of discs was measured before and after the immersions to determine mass alteration. Each disc was repaired, by adding the same brand of GIC over its surface. After immersing the repaired specimens in same solutions, shear bond strengths using universal testing machine were measured. Two-way ANOVA and Tukey’s test was used (α=0.05). Results: Resin-modified GICs degrade after HCl immersion followed by brushing (p<0.05), while self-cured GICs were negatively affected by all challenges (p<0.05). The challenges decreased the repair strength for VitroFil LC (p<0.05), which had higher repair shear bond strength than the other GICs (p<0.05), exhibiting most cohesive failures. Conclusion: Self-cured GICs degraded when immersed in all acid solutions with brushing while resin-modified GICs only degraded following HCl immersion with brushing. Despite exhibiting the best repair results, VitroFil LC was the only GIC that was influenced by all the acid challenges.

Numerical Three-dimensional Finite Element Modeling of Cavity Shape and Optimal Material Selection by Analysis of Stress Distribution on Class V Cavities of Mandibular Premolars

Aim:

Adhesive restoration does not depend primarily on the configuration of the shape of the cavity. Under varying loading conditions, it is essential to know the stress concentration and load transfer mechanism for distinct cavity shapes. The aim of this study was to evaluate and compare the biomechanical characteristics of various cavity shapes, namely oval, elliptical, trapezoidal, and rectangular shapes of class V cavities on mandibular premolars restored with amalgam, glass ionomer cement, and Cention N using three-dimensional (3D) finite element analysis.

Materials and Methods:

A 3D prototype of a mandibular premolar was generated by Digital Imaging and Communications in Medicine (DICOM) images obtained from the cone beam computed tomography and imported to 3D modeling software tool, SpaceClaim. The four distinct load magnitudes of 100, 150, 200, and 250N were applied as a pressure load perpendicular to the lingual plane of the lingual cusp of the occlusal surface (normal load) and at 45° to same (oblique load). The stress distribution patterns and the maximum von Mises stresses were analyzed and compared.

Results:

The occlusal stresses were distributed from the force loading point in an approximate actinomorphic pattern, and when the force load was close to the margin, the stress was much greater.

Conclusion:

Ovoid cavity showed lesser stress concentration and deformation for each of the tested restorative material.