Grinding the intaglio surface of yttria partially- and fully-stabilized zirconia polycrystals restorations: Effect on their fatigue behavior

Optical effect of rapid sintering protocols on different types of zirconia

STATEMENT OF PROBLEM

Rapid sintering protocols are available for the fabrication of zirconia restorations, but whether rapid sintering influences color or translucency is unclear.

PURPOSE

The purpose of this in vitro study was to investigate the effect of different rapid sintering protocols on the color and translucency of cubic and tetragonal zirconias.

MATERIAL AND METHODS

Sixty disk-shaped specimens of 1-mm-thick cubic (DD CubeX2) and tetragonal (DD Bio ZX2) zirconia were investigated. Specimens of each type of zirconia were divided into three groups: conventional, speed, and superspeed sintering protocols. The conventional group of each zirconia type served as the control for calculating color differences. Translucency for each group was assessed by the translucency parameter and contrast ratio. Two-way analysis of variance was used for statistical analysis of the data (α=.05).

RESULTS

The translucency of cubic and tetragonal zirconia decreased after speed and superspeed sintering (P<.001). Superspeed sintering resulted in a greater color change than speed sintering (P<.001).

CONCLUSIONS

Rapid sintering protocols produced a significant effect on the color and translucency of cubic and tetragonal zirconias.

A brief review on fatigue test of ceramic and some related matters in Dentistry

The characteristics of dental ceramics have been extensively studied over the years to provide highly qualified materials for use in prosthetic restorations. The ability to adhere to dental substrates, outstanding aesthetics (translucency, color, and substrate masking ability) and improved mechanical properties provide these materials with optical features and high strength to withstand masticatory stimuli. Different classifications are adopted, and it is generally considered that glass-ceramics have better optical characteristics due to the high glass content, and polycrystalline ceramics have superior strength favored by their densified and organized crystals, hampering crack growth. This knowledge was largely built-up during years of scientific research through different testing methodologies, but mainly employing static loads. It is important to not only take into account the intensity of loads that these materials will be exposed to, but also the effect of the intermittence of cyclic load application leading to mechanical fatigue and the influence of factors related to the crack origin and their propagation under this condition. Furthermore, the bonding surface of ceramic restorations requires surface treatments that improve the bond strength to luting agents; however, these treatments require caution because of their potential to produce defects and affect the structural behavior. Moreover, ceramic restorations often require internal adjustments for proper seating or external adjustments for fitting the occlusal contact with the antagonist. In this sense, finishing/polishing protocols may alter the defect population, as luting agents may also interact by filling in the superficial defects on the restoration intaglio surface. Thus, the balance among all these factors will define the performance of a restorative setup, as well as the posterior exposure to the humid environment and the masticatory stimuli (cyclical loading), which may favor developing slow and subcritical growth of cracks in ceramic materials and the degradation of the bond interface. Therefore, it is essential that the concepts which explain the fatigue mechanism are understood, as well as the crack propagation and failure patterns of restorative ceramic materials.

Should finishing, polishing or glazing be performed after grinding YSZ ceramics? A systematic review and meta-analysis

The present systematic review and meta-analysis aimed to assess the characteristics and consequences of post-processing methods after grinding procedures in YSZ ceramics on its surface roughness and flexural strength. The protocol of this review was made prospectively and is available online in the PROSPERO database (link). Literature searches on PubMed/MEDLINE, EMBASE, Lilacs, Web of Science and Scopus were conducted on December 2022 to select in vitro studies written in English, without publishing-date restrictions, that considered surface characteristics and mechanical properties of YSZ ceramics submitted to grinding and subsequent post-processing surface treatments as an attempt to revert the effect induced by grinding. Two authors independently selected the studies, extracted the data and assessed the risk of bias. Mean differences (Rev-Man 5.1, random effects model, α= 0.05) were obtained by comparing flexural strength and surface roughness values of ground surfaces with at least one post-processing surface treatment (global analysis). Subgroup analyses were performed considering the most prevalent categories of post-processing methods. A total of 33 (out of 4032) studies were eligible and included in the analysis. In the global analysis, ground surfaces showed higher flexural strength than when post-processing methodologies were employed (p< 0.0001). The subgroup analysis showed that only polishing was able to enhance the flexural strength after grinding (p= 0.001); however, when other protocols were used, the ground surface was always superior in terms of flexural strength (p< 0.0001). Post-processing techniques in both the global and sub-group analyses were able to reduce the surface roughness after grinding in YSZ ceramics (p< 0.00001). High heterogeneity was found in all the meta-analyses. Concerning the risk of bias analysis, the included studies had mixed scores for the considered factors. In conclusion, in terms of improving flexural strength and restoring surface roughness after grinding, polishing protocols can be considered the best indication as post-processing treatment after YSZ ceramics adjustments/grinding.

In-lab simulation of CAD/CAM grinding and intaglio surface treatments of 4YSZ monolithic restorations: Effect on its load-bearing capacity under fatigue

OBJECTIVES

To evaluate the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4YSZ simplified restorations.

METHODS

Ceramic discs (Ø = 10 mm, thickness = 1 mm) were randomly allocated into 6 groups considering: "In-lab simulation of CAD/CAM grinding" (ground or polished) and "intaglio surface treatments": Ctrl (without surface treatment), AlOx (aluminum oxide air abrasion) or GLZ (glaze spray application). The surface roughness of all samples was measured, the treated discs received a ceramic primer, were luted with resin cement onto a dentin analogue material (woven glass-reinforced epoxy resin) and tested under a cyclic fatigue test (step-stress approach, n = 15; 1.4 Hz, 10,000 cycles/step, step-size of 100N starting at 200N until failure). A complementary analysis was performed to corroborate the findings in the fatigue test that the glaze fill defects increase the mechanical properties of the ceramic. To do so, bars (n= 10; 1.0 × 1.0 × 12 mm; considering the groups: N-ID: non-indented; ID: indented; ID-GLZ: indented plus glaze spray application) were indented in a vickers hardness tester to produce a crack pattern, treated with glaze or not, and then submitted to flexural strength tests (FS). Fractographic and topographic analysis were performed.

RESULTS

In-lab simulation of CAD/CAM grinding decreased the fatigue failure load of the 4YSZ ceramic when comparing polished and ground groups, regardless of surface treatment. GLZ induced better fatigue performance compared to the air abrasion, regardless of the grinding condition (ground or polished surface). The results of the flexural strength test corroborated the findings in the fatigue test, as the ID-GLZ group presented superior FS than the ID group, however both had inferior FS than N-ID. There is an inverse association between roughness and fatigue failure load, as the higher the surface roughness, the lower the fatigue failure load. Failures in the fatigue and flexural strength tests started from the face subjected to tensile stresses.

CONCLUSION

In-lab simulation of CAD/CAM grinding had a detrimental effect on the fatigue behavior of 4YSZ and glaze spray induced better 4YSZ performance compared to the air abrasion. The intaglio surface treatments differently influenced the 4YSZ fatigue performance, however, only glaze spray can reverse the damage caused by the grinding.

Influence of high-speed sintering protocols on translucency, mechanical properties, microstructure, crystallography, and low-temperature degradation of highly translucent zirconia

OBJECTIVES

Impacts of high-speed sintering on the optical and mechanical properties, microstructure, crystallography, and low-temperature degradation of commercial yttria-partially stabilized zirconia (Y-PSZ) were investigated.

METHODS

Five commercial Y-PSZ products (KATANA HT, KATANA STML, KATANA UTML, Zpex 4, and Zpex Smile) were investigated. Specimens were sintered following speed-sintering (~90 min) and conventional-sintering protocols (~7 h), and a group of KATANA STML was super-speed-sintered (18 min). Dimensions of the zirconia specimens after sintering were 14.5 mm (diameter) and 1.2 mm (thickness). Translucency was assessed using a colorimeter. Biaxial flexural strength was measured using a universal testing machine, followed by Weibull analysis. Scanning electron microscopy was used for microstructure assessments. X-ray diffraction was used to analyze the crystallography before and after hydrothermal aging. Low-temperature degradation (LTD) tests were performed at 134 °C under 2-3 bar water vapor in an autoclave.

RESULTS

The translucency and flexural strength were not affected significantly by the sintering programs (p > 0.05). The conventionally sintered KATANA STML and speed-sintered Zpex 4 presented the highest and lowest Weibull modulus, respectively. The conventionally-sintered Y-PSZ had a larger average grain size and smaller fraction of fine grains than those of the speed-sintered specimens. The fractographic analysis of the speed- and conventionally sintered Y-PSZ yielded comparable results. The speed-sintered Y-PSZ exhibited a lower c-ZrO₂ content than that of conventionally-sintered Y-PSZ, except for KATANA HT and KATANA STML. LTD tests indicated that some of the speed and conventionally-sintered Y-PSZ exhibited similar monoclinic volume fractions.

SIGNIFICANCE

Speed-sintering programs are acceptable for Y-PSZ zirconia.

Cyclic fatigue tests on non-anatomic specimens of dental ceramic materials: A scoping review

The aim of the present scoping review was to identify and discuss the methods, testing parameters, and characteristics used to induce cyclic fatigue on non-anatomic dental ceramic specimens. In vitro studies written in English which evaluated commercially-available non-anatomic dental ceramic specimens subjected to mechanical cyclic fatigue were selected. The search was performed in the PubMed, Scopus and Web of Science databases. The initial search yielded 1,636 articles, of which 81 were included. Based on the collected data, most of the included studies evaluated dental ceramic specimens cemented to supporting substrate (n= 42; 51.9%); used step-stress (n= 35; 42.2%) accelerated fatigue test, loading frequencies above 10 Hz (n= 31, 35.6%), stainless steel (n = 28, 32.6%) load applicator with spherical shaped tip 40 mm diameter (n= 25, 30.9%); applied only axial loads (n= 77, 95.1%); and considered a wet testing environment (n= 65, 78.3%). The definition of test geometry, method, and testing parameters must be cautiously considered according to the study objective and the scenario that is simulated. Accelerated fatigue tests, load frequencies up to 20 Hz, a 40 mm stainless steel spherical load applicator and a wet testing environment are the major common defined parameters presented in the existing literature. More studies exploring the influence of such factors on fatigue mechanism are necessary.