Fabrication and characterization of remineralizing dental composites containing hydroxyapatite nanoparticles

Evaluation of Mechanical and Elemental Properties of Bioceramic-Coated Orthodontic Brackets and Enamel Surface

OBJECTIVE

 The aim is to coat orthodontic brackets with two different bioactive materials and to compare the mechanical and morphological properties of coated brackets and tooth surfaces.

MATERIALS AND METHODS

 A total of 120 stainless steel brackets were divided equally into three groups, that is, the uncoated brackets and nanohydroxyapatite (nHA)-coated, and nanobioactive glass (nBG)-coated brackets using a spin coater machine. The brackets were bonded on the enamel surface and underwent remineralization/demineralization cycles for days 1, 7, 14, and 30. At each time interval, the bond strength of the brackets was assessed using mechanical loading. An optical and scanning electron microscope (SEM) were used for surface evaluation, and the adhesive remanent index (ARI) values were obtained and quantified.

STATISTICAL ANALYSIS

 One-way analysis of variance using Tukey's test was used to compare the differences among the groups.

RESULTS

 A uniform distribution of nanoparticles occurred on the surfaces of brackets. The shear bond strength (SBS) showed no significant differences in any tested groups on days 1, 7, and 14. However, control and nBG showed a significant difference from nHA at day 30. On days 7, 14, and 30, the nHA group showed the highest SBS values among the groups. For ARI, most samples showed an adhesive nature of failure at the enamel-brackets interface. The images confirmed the presence of coated particles on brackets and remnants of adhesives after SBS.

CONCLUSION

 This study confirmed that the nHA- and nBG-coated brackets have a high potential for application in orthodontics regarding structural and mechanical properties.

Marginal integrity and physicomechanical properties of a thermoviscous and regular bulk-fill resin composites

OBJECTIVES

To evaluate the marginal integrity (MI%) and to characterize specific properties of a thermoviscous bulk-fill resin composite, two regular bulk-fill resin composites, and a non-bulk-fill resin composite.

MATERIALS AND METHODS

VisCalor bulk (VBF), Filtek One Bulk Fill (OBF), and Aura Bulk Fill (ABF) were evaluated. Filtek Z250 XT (ZXT) was used as non-bulk-fill control. MI% was evaluated in standardized cylindrical cavities restored with the composites by using a 3D laser confocal microscope. The following properties were characterized: volumetric polymerization shrinkage (VS%), polymerization shrinkage stress (Pss), degree of conversion (DC%), microhardness (KHN), flexural strength (FS), and elastic modulus (EM). Data were analyzed by one-way and two-way ANOVA, and Tukey HSD post-hoc test (α = 0.05).

RESULTS

VBF presented the highest MI% and the lowest VS% and Pss (p < 0.05). DC% ranged from 59.4% (OBF) to 71.0% (ZXT). ZXT and VBF presented similar and highest KHN than OBF and ABF (p < 0.05). ABF presented the lowest FS (p < 0.05). EM ranged from 5.5 GPa to 7.7 GPa, with the values of ZXT and VBF being similar and statistically higher than those of OBF and ABF (p < 0.05).

CONCLUSIONS

Thermoviscous technology employed by VisCalor bulk was able to improve its mechanical behavior comparatively to regular bulk-fill resin composites and to contribute to a better marginal integrity in restorations built up in cylindrical cavities with similar geometry to a class I cavity as well. Although presenting overall better physicomechanical properties, Z250 XT presented the worst MI%.

CLINICAL RELEVANCE

The marginal integrity, which is pivotal for the success of resin composite restorations, could be improved using VisCalor bulk-fill. The worst MI% presented by Z250 XT reinforces that non-bulk-fill resin composites shall not be bulk-inserted in the cavity to be restored.

Iron and Magnesium Co-substituted Hydroxyapatite Nanoparticles in Orthodontic Composite: A Preliminary Assessment

Aim The study aims to characterize Fe and Mg co-substituted hydroxyapatite nanoparticles (FeMgHAPn) and assess the antimicrobial properties of FeMgHAPn-incorporated orthodontic composite. Materials and methods FeMgHAPn was synthesized using the sol-gel method, and the prepared nanoparticle powder was characterized using Fourier Transform Infrared Spectroscopy (FTIR), energy-dispersive X-ray analysis (EDX)) and scanning electron microscopic (SEM) analysis. The FeMgHAPn was incorporated into a commercially available orthodontic composite in two concentrations (40 and 20 μL), and the structure was examined using SEM. The FeMgHAPn-incorporated composite was tested for its antimicrobial efficacy against Streptococcus mutans, Staphylococcus aureus, and Escherichia coli using the agar-well diffusion method. The zones of inhibition (ZOI) were measured in millimeters (mm). Results The characterization of the FeMgHAPn indicated the successful formation of the nanoparticle without any impurities or byproducts. The high concentration (40 μL) of FeMgHAPn-incorporated orthodontic composite showed the maximum ZOI against all three microbes, followed by the low concentration (20 μL) and the control group. Conclusion The FeMgHAPn-incorporated orthodontic composite showed promising antimicrobial activity against caries-causing S. mutans, S. aureus, and E. coli.

Restorative Dental Resin Functionalized with Calcium Methacrylate with a Hydroxyapatite Remineralization Capacity

The ability of dental materials to induce the mineralization of enamel like hydroxyapatite (HA) is of great importance. In this article, a novel kind of dental restorative material characterized by a mineralization ability was fabricated by photopolymerization. Calcium methacrylate (CMA) was introduced into the classical bisphenol A-glycidyl methacrylate (Bis-GMA) and triethylene glycol dimethacrylate (TEGDMA) dental resin formulation. This functional dental resin (BTCM) was calcium-rich and can be prepared simply by one-step photopolymerization. The influence of CMA on the photopolymerization kinetics, the dental resin's mechanical properties, and its capacity to induce dynamic in situ HA mineralization were examined. Real-time FTIR, compression modulus, scanning electron microscopy, X-ray spectroscopy, MTT assay, and cell attachment test were carried out. The obtained data were analyzed for statistical significance using analysis of variance (ANOVA). Double bond conversion could be completed in less than 300 s, while the compression modulus of BTCM decreased with the increase in CMA content (30 wt%, 40 wt%, and 50 wt%). After being soaked in Ca(NO3)2 and Na2HPO4 solutions alternatively, dense HA crystals were found on the surface of the dental resin which contained CMA. The amount of HA increased with the increase in CMA content. The MTT results indicated that BTCM possesses good biocompatibility, while the cell adhesion and proliferation investigation demonstrated that L929 cells can adhere and proliferate well on the surface of BTM. Thus, our approach provides a straightforward, cost-effective, and environmentally friendly solution that has the potential for immediate clinical use.

An Evaluation of the Mechanical Properties of a Hybrid Composite Containing Hydroxyapatite

There is currently a lack of scientific reports on the use of composites based on UDMA resin containing HAp in conservative dentistry. The aim of this study was therefore to determine the effect of hydroxyapatite content on the properties of a hybrid composite used in conservative dentistry. This paper compares a commercial hybrid composite with experimental composites treated with 2% by weight (b/w), 5% b/w, and 8% b/w hydroxyapatite. The composites were subjected to bending strength, compression, and diametrical compression tests, as well as those for impact strength, hardness, and tribological wear. The obtained results were subjected to statistical analysis. Increased hydroxyapatite was found to weaken the mechanical properties; however, 2% b/w and 5% b/w hydroxyapatite powder was found to achieve acceptable results. The statistical analysis showed no significant differences. HAp is an effective treatment for composites when applied at a low concentration. Further research is needed to identify an appropriate size of HAp particles that can be introduced into a composite to adequately activate the surface and modification its composition.

New Technological Approaches for Dental Caries Treatment: From Liquid Crystalline Systems to Nanocarriers

Dental caries is the most common oral disease, with high prevalence rates in adolescents and low-income and lower-middle-income countries. This disease originates from acid production by bacteria, leading to demineralization of the dental enamel and the formation of cavities. The treatment of caries remains a global challenge and the development of effective drug delivery systems is a potential strategy. In this context, different drug delivery systems have been investigated to remove oral biofilms and remineralize dental enamel. For a successful application of these systems, it is necessary that they remain adhered to the surfaces of the teeth to allow enough time for the removal of biofilms and enamel remineralization, thus, the use of mucoadhesive systems is highly encouraged. Among the systems used for this purpose, liquid crystalline systems, polymer-based nanoparticles, lipid-based nanoparticles, and inorganic nanoparticles have demonstrated great potential for preventing and treating dental caries through their own antimicrobial and remineralization properties or through delivering drugs. Therefore, the present review addresses the main drug delivery systems investigated in the treatment and prevention of dental caries.

Effects of the Incorporation of Bioactive Particles on Physical Properties, Bioactivity and Penetration of Resin Enamel Infiltrant

Purpose

The resinous infiltrant lacks remineralizing activity. This research aimed to develop and evaluate bioactivity, physico-mechanical properties and penetration of resin infiltrants containing Biosilicate or nanohydroxyapatite.

Methods

Experimental resin infiltrant (ERI; 75/25 wt.% TEGDMA/BisEMA) was divided among the groups Pure Experimental (PE); ERI + Biosilicate 5 or 10% (Bio5; Bio10), ERI + 10% nanohydroxyapatite (Hap10), and Icon (DMG, Germany). Bioactivity was analyzed by SEM, EDS and FT-IR/ATR after soaking in SBF. Degree of conversion (DC), sorption and solubility (SO; SOL), flexural strength, modulus of elasticity (FS; E-modulus), contact angle (CA) and penetration were characterized. Extent of penetration was analyzed by treating white spot lesions (WSL) in human dental enamel samples with the infiltrants and subsequently analyzing specimens by confocal laser scanning microscopy. Data from each test were submitted to ANOVA and Tukey's tests (p < 0.01).

Results

SEM, EDS and FT-IR showed the formation of precipitates and increase in the rates of Ca and P in the groups with bioactive particles, after storage in SBF. Hap10 showed higher DC and CA values than all the other groups. Groups Bio5 and Bio10 showed CA values similar to those of Icon, higher SO and SOL values, and reduction in other properties. All infiltrants were capable of penetrating into the WSLs.

Conclusion

The incorporation of Biosilicate (5 or 10%) or nanohydroxyapatite (10%) into ERI induced mineral deposition on the surface and did not compromise infiltration and penetration into WSLs, however, compromising their physico-mechanical properties.

Bioactive Inorganic Materials for Dental Applications: A Narrative Review

Over time, much attention has been given to the use of bioceramics for biomedical applications; however, the recent trend has been gaining traction to apply these materials for dental restorations. The bioceramics (mainly bioactive) are exceptionally biocompatible and possess excellent bioactive and biological properties due to their similar chemical composition to human hard tissues. However, concern has been noticed related to their mechanical properties. All dental materials based on bioactive materials must be biocompatible, long-lasting, mechanically strong enough to bear the masticatory and functional load, wear-resistant, easily manipulated, and implanted. This review article presents the basic structure, properties, and dental applications of different bioactive materials i.e., amorphous calcium phosphate, hydroxyapatite, tri-calcium phosphate, mono-calcium phosphate, calcium silicate, and bioactive glass. The advantageous properties and limitations of these materials are also discussed. In the end, future directions and proposals are given to improve the physical and mechanical properties of bioactive materials-based dental materials.

Hydroxyapatite as Remineralization Agent for Children's Dental Care

Children are prone to develop dental caries. This is supported by epidemiological data confirming early childhood caries (ECC) as a highly prevalent disease affecting more than every second child worldwide. ECC is known to result from an imbalance between re- and demineralization where demineralization dominates due to frequent acid production by cariogenic bacteria present in oral biofilms. The application of oral care formulations containing remineralizing agents helps to prevent dental caries. As young children are sensitive and usually swallow (intended or unintended) a majority of toothpaste or other oral care products during daily dental care, all ingredients, especially the actives, should be non-toxic. Biomimetic hydroxyapatite [HAP; Ca5(PO4)3(OH)] is known to have favorable remineralizing properties combined with an excellent biocompatibility, i.e., it is safe if accidently swallowed. Several clinical trials as well as in situ and in vitro studies have shown that HAP remineralizes enamel and dentin. Remineralization occurs due to deposition of HAP particles on tooth surfaces forming mineral-mineral bridges with enamel crystals, but also indirectly through calcium and phosphate ions release as well as HAP's buffering properties in acidic environments (i.e., in plaque). HAP induces a homogenous remineralization throughout the subsurface enamel lesions. This review summarizes the current evidence showing HAP as an effective remineralizing agent in oral care products for children. Additional studies showing also further beneficial effects of HAP such as the reduction of biofilm formation and the relief of hypersensitivity in children with molar incisor hypomineralization (MIH). It can be concluded that HAP is an effective and safe remineralizing agent for child dental care.

Polymeric Dental Nanomaterials: Antimicrobial Action

This review aims to describe and critically analyze studies published over the past four years on the application of polymeric dental nanomaterials as antimicrobial materials in various fields of dentistry. Nanoparticles are promising antimicrobial additives to restoration materials. According to published data, composites based on silver nanoparticles, zinc(II), titanium(IV), magnesium(II), and copper(II) oxide nanoparticles, chitosan nanoparticles, calcium phosphate or fluoride nanoparticles, and nanodiamonds can be used in dental therapy and endodontics. Composites with nanoparticles of hydroxyapatite and bioactive glass proved to be of low efficiency for application in these fields. The materials applicable in orthodontics include nanodiamonds, silver nanoparticles, titanium(IV) and zinc(II) oxide nanoparticles, bioactive glass, and yttrium(III) fluoride nanoparticles. Composites of silver nanoparticles and zinc(II) oxide nanoparticles are used in periodontics, and nanodiamonds and silver, chitosan, and titanium(IV) oxide nanoparticles are employed in dental implantology and dental prosthetics. Composites based on titanium(IV) oxide can also be utilized in maxillofacial surgery to manufacture prostheses. Composites with copper(II) oxide nanoparticles and halloysite nanotubes are promising materials in the field of denture prosthetics. Composites with calcium(II) fluoride or phosphate nanoparticles can be used in therapeutic dentistry for tooth restoration.

Development of New Experimental Dental Enamel Resin Infiltrants-Synthesis and Characterization

The aim of the present study was to obtain experimental infiltration materials, intended for the treatment of dental white spots, and to investigate them. Two series of infiltrants (P1–P6)/(P1F–P6F) were obtained, based on different monomer mixtures, without/with glass filler (with fluoride release ability). Each infiltrant from the second series contained the same amount of glass powder, and each infiltrant from the (P–PF) group contained the same resin composition. The characteristics of the experimental infiltrants were investigated by degree of conversion (DC), mechanical strength, water sorption (WS), and fluoride release, in addition to residual monomer for (P1F–P6F) infiltrants. The results were compared with those obtained for commercial Icon infiltrant. For the experimental infiltrants, without/with filler, the recorded DC was in the range of 58.27–89.70%/60.62–89.99%, compared with Icon (46.94%) 24 h after polymerization. The release of fluoride depends on the permeability of the polymer matrix, with respect to the water sorption, which may help to diffuse ions in the storage medium but which can also influence the release of residual monomers. The highest flexural strengths were recorded for the (TEGDMA/HEMA/Bis-GMA) infiltrants (133.94 ± 16.389 MPa/146.31 ± 7.032 MPa). The best experimental infiltrants were P2 and P2F (Bis-GMA/HEMA/TEGDMA).

Experimental Bioactive Glass-Containing Composites and Commercial Restorative Materials: Anti-Demineralizing Protection of Dentin

The purpose of this in vitro study was to investigate whether different types of experimental and commercial restorative dental materials can protect dentin against acid-induced softening. Experimental composites were prepared with a photocurable mixture of methacrylates and two types of bioactive glass (45S5 and a customized low-Na F-containing formulation). Human dentin samples were prepared from mid-coronal tooth slices and immersed in lactic acid solution (pH = 4.0) at 5 mm from set specimens of restorative material. After 4, 8, 12, 16, 20, 24, 28, and 32 days, surface microhardness of dentin samples and pH of the immersion solution were measured, followed by replenishing of the immersion medium. Microstructural analysis was performed using scanning electron microscopy. The protective effect of restorative materials was determined as dentin microhardness remaining statistically similar to initial values for a certain number of acid additions. Scanning electron microscopy showed a gradual widening of dentinal tubules and proved less discriminatory than microhardness measurements. To produce a protective effect on dentin, 20 wt% of low-Na F-containing bioactive glass was needed, whereas 10 wt% of bioactive glass 45S5 was sufficient to protect dentin against acid-induced demineralization. The anti-demineralizing protective effect of experimental and commercial restoratives on dentin was of shorter duration than measured for enamel in a previous study using the same experimental approach.

The Antioxidant Supplementation with Filipendula ulmaria Extract Attenuates the Systemic Adverse Effects of Nanosized Calcium Phosphates in Rats

The aim of this study was to investigate and compare the systemic toxicity of three nanosized calcium phosphates (CaPs): hydroxyapatite (HA), tricalcium phosphate (TCP), and amorphous calcium phosphate (ACP) in rats. Since those metallic compounds are widely used as bone replacement materials, including their use in oral surgery, CaPs were applied (per os) equimollary (17.8 mg/kg, 11 mg/kg, and 9.65 mg/kg b.w., respectively) for 30 days in order to mimic the previously described release rate from dental composites. Also, we employed antioxidant supplementation with Filipendula ulmaria (FU) extract. All the applied CaPs significantly increased serum calcium, triglycerides, LDL, and LDH, while serum levels of testosterone and LH declined, with no alterations in the liver enzymes. The evaluation of oxidative stress markers (in the liver, kidney, and testicle) showed an increase in TBARS values, while SOD and CAT activities and GSH levels were significantly reduced. The relative gene expression of Bax and Bcl-2 was shifted to proapoptotic action, accompanied by intense characteristic histological changes in architecture in all investigated organs. The toxic effects were most prominent in groups treated by ACP. FU administration attenuated the majority of nanosized CaP-induced adverse effects, thus recommending this therapeutic approach to minimize nano-CaP systemic toxicities.

The Antioxidant Supplementation with Filipendula ulmaria Extract Attenuates the Systemic Adverse Effects of Nanosized Calcium Phosphates in Rats

The aim of this study was to investigate and compare the systemic toxicity of three nanosized calcium phosphates (CaPs): hydroxyapatite (HA), tricalcium phosphate (TCP), and amorphous calcium phosphate (ACP) in rats. Since those metallic compounds are widely used as bone replacement materials, including their use in oral surgery, CaPs were applied (per os) equimollary (17.8 mg/kg, 11 mg/kg, and 9.65 mg/kg b.w., respectively) for 30 days in order to mimic the previously described release rate from dental composites. Also, we employed antioxidant supplementation with Filipendula ulmaria (FU) extract. All the applied CaPs significantly increased serum calcium, triglycerides, LDL, and LDH, while serum levels of testosterone and LH declined, with no alterations in the liver enzymes. The evaluation of oxidative stress markers (in the liver, kidney, and testicle) showed an increase in TBARS values, while SOD and CAT activities and GSH levels were significantly reduced. The relative gene expression of Bax and Bcl-2 was shifted to proapoptotic action, accompanied by intense characteristic histological changes in architecture in all investigated organs. The toxic effects were most prominent in groups treated by ACP. FU administration attenuated the majority of nanosized CaP-induced adverse effects, thus recommending this therapeutic approach to minimize nano-CaP systemic toxicities.

SEM/EDS Evaluation of the Mineral Deposition on a Polymeric Composite Resin of a Toothpaste Containing Biomimetic Zn-Carbonate Hydroxyapatite (microRepair®) in Oral Environment: A Randomized Clinical Trial

Toothpastes containing biomimetic hydroxyapatite have been investigated in recent years; the behavior of this material in the oral environment has been evaluated directly on dental enamel showing a marked remineralizing activity. To propose microRepair^®-based toothpastes (Zn-carbonate hydroxyapatite) for the domiciliary oral hygiene in patients with dental composite restorations, the aim of this study was to evaluate the deposition of Zn-carbonate hydroxyapatite on a polymeric composite resin with Scanning Electron Microscopy/Energy-Dispersive X-ray Spectrometry (SEM/EDS) analysis. Twenty healthy volunteers underwent the bonding of 3 orthodontic buttons on the vestibular surfaces of upper right premolars and first molar. On the surface of the buttons, a ball-shaped mass of composite resin was applied and light-cured. Then, the volunteers were randomly divided into two groups according to the toothpaste used for domiciliary oral hygiene: the Control toothpaste containing stannous fluoride and the Trial toothpaste containing microRepair^®. The buttons were debonded after 7 days (T1—first premolar), after 15 days (T2—second premolar), and after 30 days (T3—first molar) to undergo the SEM/EDS analysis. The deposition of calcium, phosphorus, and silicon was assessed through EDS analysis and data were submitted to statistical analysis (p < 0.05). SEM morphologic evaluation showed a marked deposition of the two toothpastes on the surfaces of the buttons. EDS quantitative analysis showed an increase of calcium, phosphorus, and silicon in both the groups, with a statistically significant difference of calcium deposition at T3 for the Trial group. Therefore, the use of toothpaste containing Zn-carbonate hydroxyapatite could be proposed as a device for domiciliary oral hygiene because the deposition of hydroxyapatite on polymeric composite resin could prevent secondary caries on the margins of restorations.

Fabrication and characterization of low-shrinkage dental composites containing montmorillonite nanoclay

Dental composites are aesthetic materials widely used in Dentistry for replacing hard dental tissues lost due to caries or traumas. The aim of this study was to fabricate low-shrinkage dental composite charged with nanoclay fillers (montmorillonite Cloisite®-MMT) and evaluate their cytotoxicity and physicomechanical properties. Four dental composites were produced from the same organic matrix: Bis-GMA/TEGDMA (30 wt.%). The filler system was constituted of BaSi, SiO₂, and MMT in the following concentrations (wt.%): 93.8/6.2/0, 89.1/5.9/5, 86.7/5.8/7.5, and 84.4/5.6/10 (E₀: 0; E₅: 5%; E_7.5: 7.5%; E₁₀: 10% of MMT nanoclays). The following properties were tested: in vitro cytotoxicity, flexural strength, elastic modulus, volumetric shrinkage, water sorption, water solubility, and hygroscopic expansion. Scanning electron microscopy was used to characterize composites' topography. Data were analyzed by one-way ANOVA and Tukey's HSD post hoc test (p < 0.05). MMT nanoclays did not affect the cytotoxicity. E₅ and E_7.5 groups showed a significant decrease in polymerization shrinkage while maintained the overall physicomechanical properties. The inclusion of 5 and 7.5 wt.% of MMT nanoclays allowed the fabrication of dental composites with low cytotoxicity and low polymerization shrinkage, without jeopardizing the overall behaviour of their physicomechanical properties (flexural strength, elastic modulus, water sorption, water solubility, and hygroscopic expansion). These aspects suggest that the usage of MMT nanoclays could be an effective strategy to formulate new dental composites with clinical applicability.

Varying 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) level improves polymerisation kinetics and flexural strength in self-adhesive, remineralising composites

OBJECTIVES

To assess the influence of systematically varying concentrations of 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) versus 3% 4-META on the polymerisation kinetics and shrinkage, biaxial flexural strength (BFS) and modulus of remineralising composites.

METHODS

Composites were prepared by adding poly(propylene glycol) dimethacrylate (24 wt%), camphorquinone (1 wt%) and MDP (0%, 5%, 10%, 15% and 20 wt%) or 4-META (3%) to urethane dimethacrylate. These were mixed with glass fillers containing 8 wt% monocalcium phosphate and 4 wt% polylysine (powder-liquid ratio of 3:1). Continuous spectral changes, following 20 s light exposure (37 °C), were assessed with an ATR-FTIR to monitor polymerisation kinetics (n = 3). Final extrapolated conversions (D_C,max) were employed to calculate polymerisation shrinkage. BFS and modulus of 24-h dry stored disc specimens (10 × 1 mm; n = 10) were determined using a ball-on-ring jig setup.

RESULTS

Maximum rate of polymerisation and D_C,max increased linearly from 2.5 to 3.5% s^-1 and 67 to 83%, respectively, upon increasing MDP from 0 to 20 wt%. Values with 3% 4-META were 2.6% s^-1 and 78%. Shrinkage was 3.8 ± 0.3% for all formulations. Raising 4-META or MDP from 0 to 3 versus 5%, respectively, increased strength from 106 to 145 versus 136 MPa. A decreasing trend with higher MDP concentrations was noted. Elastic modulus showed no specific trend upon MDP increase.

SIGNIFICANCE

Whilst final conversion levels were enhanced by 3% 4-META or >5% MDP, trends did not correlate with strength. Peak strengths with 3% 4-META or 5% MDP may therefore be due to acidic monomers providing linkage between the hydrophilic, non-silane treated particles and the polymer matrix.

Bacterial adhesion to biomaterials: What regulates this attachment? A review

•

Bacterial adhesion to the surface of dental materials play a significant role in infections.

•

The factors that govern microbial attachment involves different types of physical-chemical interactions and biological processes.

•

Studying bacterial adhesion makes it possible to understand the mechanisms involved in attachment and helps in the search for technologies that promote antibacterial surfaces.

Bacterial attachment to biomaterials is of great interest to the medical and dental field due to its impact on dental implants, dental prostheses, and others, leading to the need to introduce methods for biofilm control and mitigation of infections. Biofilm adhesion is a multifactorial process and involves characteristics relevant to the bacterial cell as well as biological, chemical, and physical properties relative to the surface of biomaterials. Bacteria encountered different environmental conditions during their growth and developed interspecies communication strategies, as well as various mechanisms to detect the environment and facilitate survival, such as chemical sensors or physical detection mechanisms. However, the factors that govern microbial attachment to surfaces are not yet fully understood. In order to understand how bacteria interact with surfaces, as well as to characterize the physical-chemical properties of bacteria adhesins, and to determine their interrelation with the adhesion to the substrate, in recent years new techniques of atomic force microscopy (AFM) have been developed and helped by providing quantitative results. Thus, the purpose of this review is to gather current studies about the factors that regulate microbial adhesion to surfaces in order to offer a guide to studies to obtain technologies that provide an antimicrobial surface.

Dental Applications of Systems Based on Hydroxyapatite Nanoparticles—An Evidence-Based Update

Hydroxyapatite is one of the most studied biomaterials in the medical and dental field, because of its biocompatibility; it is the main constituent of the mineral part of teeth and bones. In dental science, hydroxyapatite nanoparticles (HAnps) or nano-hydroxyapatite (nano-HA) have been studied, over the last decade, in terms of oral implantology and bone reconstruction, as well in restorative and preventive dentistry. Hydroxyapatite nanoparticles have significant remineralizing effects on initial enamel lesions, and they have also been used as an additive material in order to improve existing and widely used dental materials, mainly in preventive fields, but also in restorative and regenerative fields. This paper investigates the role of HAnps in dentistry, including recent advances in the field of its use, as well as their advantages of using it as a component in other dental materials, whether experimental or commercially available. Based on the literature, HAnps have outstanding physical, chemical, mechanical and biological properties that make them suitable for multiple interventions, in different domains of dental science. Further well-designed randomized controlled trials should be conducted in order to confirm all the achievements revealed by the in vitro or in vivo studies published until now.

Fabrication and characterization of remineralizing dental composites containing calcium type pre-reacted glass-ionomer (PRG-Ca) fillers

OBJECTIVE

To fabricate and characterize dental composites with calcium type pre-reacted glass-ionomer (PRG-Ca) fillers.

METHODS

PRG-Ca fillers were prepared by the reaction of calcium fluoroaluminosilicate glass with polyacrylic acid. Seven dental composites were produced from the same organic matrix (70/30wt% Bis-GMA/TEGDMA), with partial replacement of barium borosilicate (BaBSi) fillers (60wt%) by PRG-Ca fillers (wt%): E0 (0) - control, E1 (10), E2 (20), E3 (30), E4 (40), E5 (50) and E6 (60). Enamel remineralization was evaluated in caries-like enamel lesions induced by S. mutans biofilm using micro-CT. The following properties were characterized: degree of conversion (DC%), roughness (Ra), Knoop hardness (KHN), flexural strength (FS), flexural modulus (FM), water sorption (W_sp), water solubility (W_sl), and translucency (TP). Data were analyzed to one-way ANOVA and Tukey's HSD test (α=0.05).

RESULTS

All composites with PRG-Ca induced enamel remineralization. E0 and E1 presented similar and highest DC% than E2=E3=E4=E5=E6. Ra and KHN were not influenced by PRG-Ca fillers (p<0.05). The higher the content of PRG-Ca, the lower FS, FM and TP (p<0.05). W_sp increased linearly with the content of PRG-Ca fillers (p<0.05). E6 presented the highest W_sl (p<0.05), while the W_sl of the other composites were not different from each other (p>0.05).

SIGNIFICANCE

Incorporation of 10-40wt.% of PRG-Ca fillers endowed remineralizing potential to dental composites without jeopardizing the overall behavior of their physicochemical properties. Dental composites with PRG-Ca fillers seems to be a good alternative for reinforcing the enamel against caries development.

The Beneficial Role of Filipendula ulmaria Extract in Prevention of Prodepressant Effect and Cognitive Impairment Induced by Nanoparticles of Calcium Phosphates in Rats

Mineral components of dental composites are used in many medical and dental applications, including preventive, restorative, and regenerative dentistry. To evaluate the behavioural alterations induced by nanosized particles of novel dental composites, by means of depressive level and cognitive functions, experimental groups of rats were chronically administered with nanosized hydroxyapatite (HA), tricalcium phosphate (TCP), and amorphous calcium phosphate (ACP) with or without simultaneous application of Filipendula ulmaria L. (FU) methanolic extract. The significant prodepressant action was observed in groups solely treated with HA and ACP. Besides, prolonged treatment with ACP also resulted in a significant decline in cognitive functions estimated in the novel object recognition test. The adverse impact of calcium phosphates on estimated behavioural functions was accompanied by increased oxidative damage and apoptotic markers in the prefrontal cortex, as well as diminished specific neurotrophin (BDNF) and gabaergic expression. The results of our investigation showed that simultaneous antioxidant supplementation with FU extract prevented calcium phosphate-induced behavioural disturbances, as well as prooxidative and apoptotic actions, with the simultaneous restoration of BDNF and GABA-A receptors in the prefrontal cortex. These findings suggest that FU may be useful in the prevention of prodepressant impact and cognitive decline as early as the manifestation of calcium phosphate-induced neurotoxicity.