Misinterpretation of ISO 4049 standard recommendations: Impact on Young's modulus and conversion degree of dental composites

Mechanical Behavior of Repaired Monolithic Crowns: A 3D Finite Element Analysis

This study evaluated the mechanical behavior and risk of failure of three CAD-CAM crowns repaired with different resin composites through a three-dimensional (3D) finite element analysis. Three-dimensional models of different cusp-repaired (conventional nanohybrid, bulk-fill, and flowable resin composites) crowns made of zirconia, lithium disilicate, and CAD-CAM resin composite were designed, fixed at the cervical level, and loaded in 100 N at the working cusps, including the repaired one. The models were analyzed to determine the Maximum Principal and Maximum Shear stresses (MPa). Complementary, an in vitro shear bond strength test (n = 10) was performed to calculate the risk of failure for each experimental group. The stress distribution among the models was similar when considering the same restorative material. The crown material affected the stress concentration, which was higher for the ceramic models (±9 MPa for shear stress; ±3 MPa for tensile stress) than for the CAD-CAM composite (±7 MPa for shear stress; ±2 MPa for tensile stress). The shear bond strength was higher for the repaired CAD-CAM resin composite (±17 MPa) when compared to the ceramics (below 12 MPa for all groups), while the repair materials showed similar behavior for each substrate. The stress distribution is more homogenous for repaired resin composite crowns, and a flowable direct resin composite seems suitable to repair ceramic crowns with less risk of failure.

Experimental Investigations of the Dental Filling Materials: Establishing Elastic Moduli and Poisson's Ratios

The mechanical properties of the dental filling material (DFMs) strongly influence the lifetime and durability of the tooth reparation performed. Among the most significant mechanical characteristics, one has to mention the Poisson's ratio and the elastic modulus (Young's modulus). They, during the cyclic mastication load, can prevent or aid in the prevention of secondary dental decays by provoking micro-cracks, the de-bonding of the filling material from the natural dental tissue, as well as fatigue at the level of their interface. The authors performed a scoping analysis of the nowadays-involved experimental methods, together with a critical review, putting in evidence of their advantages and limits. Based on the developments, they propose a new approach in this sense by involving the electronic speckle pattern interferometry (ESPI)/shearography high-accuracy optical method. They illustrate the advantages of this method in establishment of the elastic modulus, but they also propose a high-accuracy methodology in the estimation of Poisson's ratio. Based on the briefly-illustrated experimental results, one can conclude that ESPI/shearography can become a very useful tool for research, even though it is not a common (nowadays widely applied) method, such as three-point bending or strain gauge methods.

Development of New Experimental Dental Enamel Resin Infiltrants-Synthesis and Characterization

The aim of the present study was to obtain experimental infiltration materials, intended for the treatment of dental white spots, and to investigate them. Two series of infiltrants (P1–P6)/(P1F–P6F) were obtained, based on different monomer mixtures, without/with glass filler (with fluoride release ability). Each infiltrant from the second series contained the same amount of glass powder, and each infiltrant from the (P–PF) group contained the same resin composition. The characteristics of the experimental infiltrants were investigated by degree of conversion (DC), mechanical strength, water sorption (WS), and fluoride release, in addition to residual monomer for (P1F–P6F) infiltrants. The results were compared with those obtained for commercial Icon infiltrant. For the experimental infiltrants, without/with filler, the recorded DC was in the range of 58.27–89.70%/60.62–89.99%, compared with Icon (46.94%) 24 h after polymerization. The release of fluoride depends on the permeability of the polymer matrix, with respect to the water sorption, which may help to diffuse ions in the storage medium but which can also influence the release of residual monomers. The highest flexural strengths were recorded for the (TEGDMA/HEMA/Bis-GMA) infiltrants (133.94 ± 16.389 MPa/146.31 ± 7.032 MPa). The best experimental infiltrants were P2 and P2F (Bis-GMA/HEMA/TEGDMA).

Influence of artificial aging: mechanical and physicochemical properties of dental composites under static and dynamic compression

OBJECTIVE

The aim of the study was to evaluate the influence of filler content, degradation media and time on the mechanical properties of different dental composites after in vitro aging.

MATERIALS AND METHODS

Specimens (1 mm³) of three commercially available composites (GrandioSO®, Arabesk Top®, Arabesk Flow®) with respect to their filler content were stored in artificial aging media: artificial saliva, ethanol (60%), lactic acid (pH 5) and citric acid (pH 5). Parameters (Vickers microhardness, compressive strength, elastic modulus, water sorption and solubility) were determined in their initial state (control group, n = 3 for microhardness, n = 5 for the other parameters) and after 14, 30, 90 and 180 days (n = 3 for microhardness, n = 5 for the other parameters for each composite group, time point and media). Specimens were also characterized with dynamic-mechanical-thermal analysis (compression tests, F =  ± 7 N; f = 0.5 Hz, 1 Hz and 3.3 Hz; t = 0-170 °C).

RESULTS

Incorporation of fillers with more than 80 w% leads to significantly better mechanical properties under static and dynamic compression tests and a better water sorption behavior, even after chemical degradation. The influence of degradation media and time is of subordinate importance for chemical degradation.

CONCLUSION

Although the investigated composites have a similar matrix, they showed different degradation behavior. Since dentine and enamel occur only in small layer thickness, a test specimen geometry with very small dimensions is recommended for direct comparison. Moreover, the use of compression tests to determine the mechanical parameters for the development of structure-compatible and functionally adapted composites makes sense as an additional standard. Clinical relevance Preferential use of highly filled composites for occlusal fillings is recommended.