Effect of saturation on the viscoelastic properties of dentin

Water absorption in artificial composites: Curse or blessing?

OBJECTIVES

This study evaluated the impact of mutable water uptake on the durability of mechanical properties and the long-term reliability of artificial composites.

METHODS

Three resin-based CAD/CAM restorative materials (CRMs) were investigated in three-point bending tests to calculate flexural strength (FS), modulus of elasticity (ME), modulus of resilience (MR), modulus of toughness (MT), and elastic recovery (ER). All specimens (n = 180) were stored under the same conditions and tested in four subsets (n = 15 per material) that were respectively withdrawn after repeated thermocycling (5000 cycles; 5-55 °C, H2O) and repetitive drying (7 d; 37 °C, air). For every specimen, weight differences were determined per storage condition. Likewise, loss tangent data were separately recorded via dynamic mechanical analysis to reliably assess damping characteristics.

RESULTS

Repeated thermocycling always induced weight increase and a concurrent significant loss in all mechanical properties except for MT and ER of a polymethylmethacrylate-based CRM. Drying consistently provoked weight loss and raised mechanical properties to initial values. Weight increase, however, enhanced loss tangent values and accordingly distinct damping characteristics, whereas weight decrease markedly lowered damping properties.

SIGNIFICANCE

Water uptake repeatedly induced a decrease in common mechanical properties but concurrently increased damping behavior. Invertible equilibrium processes were found with no evidence for permanent material degradation.

The multi-scale meso-mechanics model of viscoelastic dentin

Human dentin is a hierarchical material with multi-level micro-/nano-structures, consisting of tubule, perti-tubular dentin (PTD) and intertubular dentin (ITD) as the major constituents at microscale; and the PTD and ITD are further composed of collagen and hydroxyapatite (HAp) crystals with different volume fractions at nanoscale. In most cases, the HAp is considered as elastic while the collagen as viscoelastic material. It is of great significance to study the hierarchical structure and viscoelasticity of human dentin to understand the mechanical properties of dentin for further development of restorative materials. Based on this, this paper focuses on multiscale modeling of the elastic properties and dynamic viscoelastic response of dentin and establishes a bottom-up micromechanics model from nano-to macro-scale. In order to study the nanostructural effect on the viscoelastic behavior of hierarchical structures, the homogenization theories of random platelets composites (HTRPC) and the locally-exact homogenization theory (LEHT) are introduced for the homogenization of heterogeneous materials of microstructures at different levels. The HTRPC, based on Eshelby Inclusion theory, is used to predict the effective modulus of PTD and ITD. The LEHT is a method for homogenizing multiphase dentin characterized by repeated unit cells (RUCs). The resulting predictions are in very good agreement with several experimental data from the literature. In addition, the results of nanostructrual effect on dentin show that the viscoelasticity of dentin is majorly contributed by collagen and the HAp greatly provide the strength and hardness of dentin. Furthermore, the ageing effect on dentin's viscoelasticity is considered from the proposed multiscale micromechanics model. It is demonstrated that the ageing effect is much more influential in affecting the loss moduli of dentin than the storage.

Damping Behaviour and Mechanical Properties of Restorative Materials for Primary Teeth

The energy dissipation capacity and damping ability of restorative materials used to restore deciduous teeth were assessed compared to common mechanical properties. Mechanical properties (flexural strength, modulus of elasticity, modulus of toughness) for Compoglass F, Dyract eXtra, SDR flow, Tetric Evo Ceram, Tetric Evo Ceram Bulk Fill, and Venus Diamond were determined using a 4-point bending test. Vickers hardness and Martens hardness, together with its plastic index (η_ITdis), were recorded using instrumented indentation testing. Leeb hardness (HLD) and its deduced energy dissipation data (HLD_dis) were likewise determined. The reliability of materials was assessed using Weibull analysis. For common mechanical properties, Venus Diamond always exhibited the significantly highest results and SDR flow the lowest, except for flexural strength. Independently determined damping parameters (modulus of toughness, HLD_dis, η_ITdis) invariably disclosed the highest values for SDR flow. Composite materials, including SDR flow, showed markedly higher reliabilities (Weibull modulus) than Compoglass F and Dyract eXtra. SDR flow showed pronounced energy dissipation and damping characteristics, making it the most promising material for a biomimetic restoration of viscoelastic dentin structures in deciduous teeth. Future developments in composite technology should implement improved resin structures that facilitate damping effects in artificial restorative materials.