Thermal and mechanical characterization of thermoplastic orthodontic aligners discs after molding process

Comparative evaluation of physical and mechanical properties of clear aligners - a systematic review

INTRODUCTION

The clinical effectiveness of clear aligners depends on the material properties both physical and mechanical. The purpose of this systematic review is to evaluate the physical and mechanical properties of different clear aligner materials and changes in the same during and after intra-oral use.

METHODS

Search was done in five electronic databases: Pubmed, Embase, Scopus, Web of Science and Ovid individually by two reviewers. In vivo, Ex vivo and In vitro studies that evaluated the physical and mechanical properties of clear aligner materials were selected. The risk of bias assessment was performed using a modified Cochrane risk of bias tool.

RESULTS

From the 24 articles selected, 19 evaluated a single physical property and 23 articles evaluated a single mechanical property of clear aligner materials. All domains in the risk of bias assessment showed low risk of bias except for 'blinding of outcome' which was unclear in almost all the selected studies. Properties such as hardness, optical properties, stiffness, and yield strength were found to be different for different clear aligner materials and were found to change with thermoforming, with intra-oral aging, and in simulated intraoral conditions. Due to heterogenicity in the parameters used to assess physical or mechanical properties a meta-analysis could not be done.

CONCLUSIONS

Properties like hardness, color, stiffness, stress relaxation and creep behavior were different for various clear aligner materials and were found to deteriorate with thermoforming and intra-oral aging. Polyurethane-based materials have a higher level of hardness and stiffness but exhibit increased creep and stress relaxation properties.

PROSPERO REGISTRATION NUMBER

CRD42021269597.

Efficacy of an experimental gaseous ozone-based sterilization method for clear aligners

OBJECTIVES

To assess effectiveness of an experimental sterilization method based on the exposure of an O3/O2 gas mixture directly inside the packaging for clear aligners.

MATERIALS AND METHODS

Fifty samples consisting of pieces of polyethylene terephthalate glycol (PET-G) aligners were contaminated by manual handling and subsequently divided into different groups (n = 30 for exposure to O3/O2 gas at different times, n = 10 for positive control with 2% chlorhexidine digluconate, n = 10 for negative control). The measurement of optical densities (OD) of the initial and final microbial cultures was recorded for all groups. Kruskal-Wallis test was used for differences between groups while Wilcoxon test was used to compare initial and final OD values within groups. Statistical significance was set at P < .05.

RESULTS

Comparison within the groups showed statistically significant differences for exposure to the gaseous mixture (72 hours), for positive and negative controls. Other significant differences were found in the multiple comparisons between the application of gaseous ozone (48 hours and 72 hours) and the negative control.

CONCLUSIONS

The direct exposure of gaseous ozone on the aligners inside their packaging showed microbicidal capacity at 72 hours, which was equivalent to the positive control with immersion in chlorhexidine digluconate. This innovative sterilization procedure could be considered in the final manufacturing processes of clear aligners to eliminate the potentially pathogenic microorganisms that are deposited on surfaces of these orthodontic devices.

Physiochemical and mechanical characterisation of orthodontic 3D printed aligner material made of shape memory polymers (4D aligner material)

OBJECTIVES

To conduct a physiochemical and mechanical material analysis on 3D printed shape-memory aligners in comparison to thermoformed aligners.

MATERIALS AND METHODS

Four materials were examined, including three thermoformed materials: CA Pro (CP), Zendura A (ZA), Zendura FLX (ZF), and one 3D printed material: Tera Harz (TC-85). Rectangular strips measuring 50 × 10 × 0.5 mm were produced from each material. Five tests were conducted, including differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), shape recovery tests, three-points bending (3 PB), and Vickers surface microhardness (VH).

RESULTS

DSC recorded glass transition temperatures (Tg) at 79.9 °C for CP, 92.2 °C for ZA, 107.1 °C for ZF, and 42.3 °C for TC-85. In DMA analysis at 20-45 °C, a prominent decrease in storage modulus was observed, exclusively for TC-85, as the temperature increased. Notably, within the temperature range of 30-45 °C, TC-85 exhibited substantial shape recovery after 10 min, reaching up to 86.1 %, while thermoformed materials showed minimal recovery (1.5-2.9 %). In 3 PB test (at 30, 37, 45 °C), ZA demonstrated the highest force at 2 mm bending, while TC-85 exhibited the lowest. Regarding VH at room temperature, there was a significant decrease for both ZA and ZF after thermoforming. ZA had the highest hardness, followed by ZF and TC-85, with CP showing the lowest values.

CONCLUSIONS

TC-85 demonstrates exceptional shape memory at oral temperature, improving adaptation, reducing force decay, and enabling, together with its higher flexibility, extensive tooth movement per step. Additionally, it maintains microhardness similar to thermoformed sheets, ensuring the durability and effectiveness of dental aligners.

CLINICAL RELEVANCE

The 3D printed aligner material with shape memory characteristics (4D aligner) has revolutionized the orthodontic aligner field. It showed mechanical properties more suitable for orthodontic treatment than thermoforming materials. Additionally, it offers enhanced control over aligner design and thickness, while optimizing the overall workflow. It also minimizes material wastage, and reduces production expenses.

Topographical and Optical Characteristics of Thermoplastic Dental Appliances Materials Related to Water Sorption

Clear thermoplastic materials have increased in popularity in the dental field due to their various applications, combination of excellent aesthetics, and good biomechanical behavior, but they may be influenced by different environmental conditions. The purpose of the present study was to assess the topographical and optical characteristics of thermoplastic dental appliances materials relative to water sorption. PET-G polyester thermoplastic materials were evaluated in this study. Related to water uptake and desiccation stages, surface roughness was analyzed, and three-dimensional AFM profiles were generated for nano-roughness measurements. Optical CIE L*a*b* coordinates were recorded and parameters like translucency (TP), contrast ratio for the opacity (CR), and opalescence (OP) were derived. Levels of color changes were achieved. Statistical analyses were performed. Water uptake significantly increases the specific weight of the materials, and after desiccation, the mass decreases. Roughness increased after water immersion as well. Regression coefficients indicated a positive correlation between TP and a* and between OP and b*. Studied PET-G materials have a different behavior to water exposure, but for all their specific weight, they increased significantly within the first 12 h. It is accompanied by an increase in the roughness values, even if they continue to be kept below the critical mean surface roughness. On nano-level, 3D images show an increase in inhomogeneity in the network structure of particles. Slight color changes were registered.

A full-field DIC analysis of the mechanical-deformation behavior of polyethylene terephthalate glycol (PET-G) aligners

OBJECTIVES

The aim was to investigate the full-field mechanical-deformation behavior of clear aligners made by polyethylene terephthalate glycol (PET-G) subjected to cyclic compression tests.

METHODS

Digital Image Correlation (DIC) (Chu et al., 1985; Schreier et al., 2009), a contactless full-field measurement technique, and Optical Microscope (OM) analysis were applied to study two PET-G aligners thermoformed from discs of a thickness of 0.75 mm and 0.88 mm. The clear aligners were placed on dental shape resin casts and were subjected to cyclic compression up to 13000 load cycles from 0 to 50 N at room temperature. The chosen number of load cycles simulates the average load history to which an aligner is subjected for one week. Local displacements and strains were measured for each test at 2, 6, 10, 20, 1000, 5000 and 13000 loading cycles.

RESULTS

Both aligners showed greater displacements in the early stages of loading, more pronounced for the 0.88 mm one. Local displacement and strain maps are derived both along the load direction and to the transverse one (never done from other researchers). Load-displacement cyclic curves allowed to evaluate the evolution of the stored energy and the stiffness during the test. The OM analyses showed significant morphological variations on the aligners' surface, such as wear and tear, high depressions and cracks, especially for the 0.75 mm specimen.

SIGNIFICANCE

Full-field analysis allowed to understand the mechanical behavior of device with complex geometry and complex load distribution, like invisible aligners. The knowledge of the stiffness and the direction of the total displacement helps the orthodontist to implement the best strategy to improve the patient's comfort and the treatment time.