In vitro study on how antioxidant solutions affect enamel surface characteristics and bonding interface of ceramic laminate veneers luting after dental bleaching

The effect of photoinitiator type and filler load on physicochemical and mechanical properties of experimental light-cured resin cements through lithium disilicate ceramics of different shades and thicknesses

OBJECTIVE

This study investigated the influence of photoinitiator types on degree of conversion (DC), rate of polymerization (RP), flexural strength (FS), flexural modulus (FM), and light transmittance (LT) of filled and unfilled light-curable resin cements through different thicknesses and shades of lithium disilicate ceramics.

METHODS

Lithium disilicate ceramic discs (IPS Emax Press, background [0.0], 0.5, 1.0, 2.0, 3.0, and 4.0 mm, shades A1 and BL3) were prepared. Experimental resin-based cements [TEGDMA/BisGMA (50/50 mass%)] were prepared using either camphorquinone (CQ)/amine (0.44/1.85 mol%) or TPO (0.44 mol%)], and a micro and nanofiller loads of nil (unfilled); 40/10 mass%; and 50/10 mass%). Resin cements (0.2 mm thick) were placed on the lower surface of the ceramic specimens and light-activated for 30 s from the upper surface using a Bluephase Style curing light (exitance at tip: 1236 mW/cm2 ± 1.20). LT and distribution of irradiance through the ceramics were measured using a UV-vis spectrometer and a beam profile camera, respectively (n = 3). The DC and RP were measured in real-time using mid infrared spectroscopy in attenuated total reflectance (ATR) mode (n = 3). FS and FM were measured using a universal testing machine (n = 5). Statistical analyses were performed on LT, DC, RP, FS, and FM data using a general linear model, and supplementary ANOVA and post hoc Tukey multiple comparison test were also performed (α = .05).

RESULTS

Thicknesses, shades, photoinitiator type, and fillers load significantly influenced the optical and mechanical characteristics of the resin-based materials (p < 0.05). The BL3 shade ceramic provided higher values of DC, RP, FS, FM, and LT compared with the A1 shade (p < 0.05). Increasing ceramic thickness decreased the properties of the resin-based materials (p < 0.05). Generally, TPO improved mechanical properties of the resin cement compared with CQ (p < 0.05).

SIGNIFICANCE

The luting process of indirect restorations may be improved by using high molar absorptivity, more reactive, and more efficient photoinitiators such as TPO, as opposed to conventional CQ. The use of such initiator may allow the placement of thicker and more opaque indirect restorations.

Biaxial flexural strength of hydrothermally aged resin-based materials

PURPOSE

The strength of temporary restorations plays a vital role in full-mouth reconstruction, and it can be impacted by the aging process. The aim of this in vitro study was to evaluate the biaxial flexural strength and fractographic features of different resin-based materials submitted to thermal aging.

MATERIAL AND METHODS

One hundred and ninety-two resin disc-shaped specimens (6.5 mm in diameter and 0.5 mm in thickness) were fabricated and divided into six experimental groups according to the resin-based materials (Filtek Bulk-Fill flowable resin; J-Temp temporary resin; and Fuji Lining glass ionomer cement) and aging process (before and after thermal cycling). Biaxial flexural strength test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min before and after thermal cycling (5 °C and 55 °C, 5760 cycles, 30 s). The mechanical properties were assessed using Weibull parameters (characteristic strength and Weibull modulus) (n = 30). Fractured specimens were examined under a polarized light stereomicroscope to identify crack origin and propagation direction. The surface microstructure of the resin-based materials was assessed by scanning electron microscopy (n = 2). The Weibull modulus (m), characteristic strength, and reliability properties were calculated, and a contour plot was used to detect differences among groups (95% confidence interval).

RESULTS

The Weibull modulus (m), characteristic strength, and reliability of the resin-based compounds were influenced by material type and thermal aging (p < 0.05). Weibull modulus (m) revealed no differences when comparing the materials and aging process (p > 0.05), except for the preceding aging period where Filtek Bulk-Fill exhibited higher values compared to J-Temp (p < 0.05). Filtek Bulk-Fill demonstrated superior characteristic strength and reliability compared to J-Temp and Fuji Lining before and after thermal cycling (p < 0.05). Fractography of the resin-based materials showed fractures originating from surface defects exposed to tensile side and their propagation toward the compressive side. Generally, no differences in surface microstructure were observed on micrographs before and after thermal aging for Filtek Bulk-Fill and Fuji Lining. However, the aging process developed flaws in J-Temp.

CONCLUSION

Resin-based material composition resulted in different flexural strength performance, impacting the Weibull modulus (m), characteristic strength, and reliability of the resin-based restorations.

Orthodontic adhesive loaded with different proportions of ZrO2 silver-doped nanoparticles: An in vitro μTBS, SEM, EDX, FTIR, and antimicrobial analysis

Zirconium dioxide silver-doped nanoparticles (ZrO2AgDNPs) impacts the adhesive material in terms of its physical characteristics, antimicrobial properties, degree of conversion (DC), and micro-tensile bond strength (μTBS) of orthodontic brackets to the enamel surface. A comprehensive methodological analysis utilizing a range of analytical techniques, including scanning electron microscopy coupled with energy-dispersive x-ray spectroscopy (EDX), Fourier-transform infrared (FTIR) spectroscopy, DC analysis, and μTBS testing. A light-curable orthodontic adhesive, specifically Transbond XT, was combined with ZrO2AgDNPs at 2.5% and 5%. As a control, an adhesive with no incorporation of ZrO2AgDNPs was also prepared. The tooth samples were divided into three groups based on the weightage of NPs: group 1: 0% ZrO2AgDNPs (control), group 2: 2.5 wt% ZrO2AgDNPs, and group 3: 5 wt% ZrO2AgDNPs. EDX graph demonstrated silver (Ag), Zirconium (Zr), and Oxygen (O2), The antibacterial efficacy of adhesives with different concentrations of NPs (0%, 2.5%, and 5%) was assessed using the pour plate method. The FTIR spectra were analyzed to identify peaks at 1607 cm-1 corresponding to aromatic CC bonds and the peaks at 1638 cm-1 indicating the presence of aliphatic CC bonds. The μTBS was assessed using universal testing machine (UTM) and bond failure of orthodontic brackets was seen using adhesive remanent index (ARI) analysis. Kruskal-Wallis test assessed the disparities in survival rates of Streptococcus mutans. Analysis of variance (ANOVA) and post hoc Tukey multiple comparisons test calculated μTBS values. The lowest μTBS was observed in group 1 adhesive loaded with 0% ZrO2AgDNPs (21.25 ± 1.22 MPa). Whereas, the highest μTBS was found in group 3 (26.19 ± 1.07 MPa) adhesive loaded with 5% ZrO2AgDNPs. ZrO2AgDNPs in orthodontic adhesive improved μTBS and has acceptable antibacterial activity against S mutans. ZrO2AgDNPs at 5% by weight can be used in orthodontic adhesive alternative to the conventional method of orthodontic adhesive for bracket bonding. RESEARCH HIGHLIGHTS: The highest μTBS was found in orthodontic adhesive loaded with 5% ZrO2AgDNPs. ARI analysis indicates that the majority of the failures fell between 0 and 1 among all investigated groups. The colony-forming unit count of S. mutans was significantly less in orthodontic adhesive loaded with nanoparticles compared with control. The 0% ZrO2AgDNPs adhesive showed the highest DC.

PEEK and glass fiber post pushout bond strength and vickers hardness of canal disinfected with curcumin photosensitizer activated by microbubble emulsion and sodium-hypochlorite with EDTA

AIMS

Impact of different post-space disinfectants (Saline, Sodium hypochlorite (NaOCl) followed by ethylene-diamine-tetra-acetic acid (EDTA) and curcumin activated by microbubble emulsion (MBE) on the Vickers hardness (VH) of root canal dentin and extrusion bond strength (EBS) of Glass fiber post (GFP) and PEEK post.

METHODS

Ninety maxillary central incisors having fully formed roots were included. After the specimen's disinfection, root canal treatment was completed. Post space was prepared by removing gutta-percha using gates glidden drills. Teeth were then arbitrarily allocated into three groups based on the methods of disinfection regime used. Group 1: Saline, Group 2: NaOCl+ EDTA and Group 3: Curcumin activated by MBE (n = 30). Analysis of VH of radicular dentin was performed using a micro-Vickers tester on ten samples from each group. After post-space disinfection, twenty specimens from each group were further divided into two subgroups (n = 10) In group-1A 2A, and 3A, GFP was used. Whereas, prefabricated PEEK posts were used in 1B, 2B, and 3B subgroups. The PBS and failure modes were performed using a universal testing machine and stereomicroscope respectively. Data was analyzed using ANOVA and Tukey post hoc test to identify significant variations among groups concerning the MH and EBS of the different posts used (p = 0.05).

RESULTS

Group 2 (5.25 % NaOCl + 17 % EDTA) (0.15 ± 0.02 GPa) treated specimens presented lowest scores of VH. However, Group 1 (Saline) irrigated canals displayed the highest scores of surface hardness (0.25 ± 0.07 GPa). Additionally, a cervical third of 3A (CP activated by MBE + GFP) (11.22 ± 0.79 MPa) presented the highest scores of bond integrity. Whereas Group 1B (Saline + PEEK post) treated specimens presented the lowest scores of PBS (4.15 ± 0.15 MPa).

CONCLUSION

Curcumin activated by microbubble emulsion for disinfection of canal dentin demonstrated favorable VH. Similarly, glass fiber post-cemented in radicular walls disinfected with curcumin activated with MBE showed promising post-bond integrity to the canal dentin.

The impact of methylene blue photosensitizer, aPDT and a calcium hydroxide-based paste on the physicochemical and mechanical characteristics of root canal dentin and the bonding interface of fiberglass posts

PURPOSE

To investigate the influence of methylene blue (MB)-mediated antimicrobial photodynamic therapy (aPDT) and calcium hydroxide (CH) medication on the mechanical characteristics, degree of conversion (DC), quantification, and volume of gaps at the adhesive interface of glass fiber posts (GFPs) luted to distinct thirds of root canal dentin. Additionally, the microhardness (MH), elastic modulus (Eit), morphology, and chemical structure of the intraradicular dentin were assessed.

MATERIALS AND METHODS

6 experimental groups were formed by sorting 102 bovine incisors. Canals receiving deionized water irrigation as a negative control; canals receiving deionized water irrigation and filled with CH as a positive control; groups treated with CH + MB at 50 and 100 mg/L without irradiation; and groups treated with CH + MB at 50 and 100 mg/L irradiated by red laser for 60 s (660 nm; 100 mW; 6.5 J; 72 J/cm2). MH, Eit, and DC properties were evaluated for both the resin cement layer and root dentin substrate (n = 8). Volume and quantification of gaps at the bonding interface (n = 6), and dentin morphology and chemical content were investigated (n = 3). Data were analyzed using a repeated-measures 2-way ANOVA followed by Tukey post hoc analysis (α = 0.05).

RESULTS

The distinct intraradicular thirds and treatment with MB-mediated aPDT, whether activated or not, in combination with CH, had a significant impact on the mechanical characteristics of the root dentin. This effect was also observed in the MH, Eit, DC, quantification, and volume of gaps at the luting interface (P < .05). In general, a higher concentration of MB, whether activated by a red laser or not, led to lower values in the mechanical properties of the root dentin, as well as in MH, Eit, and DC at the adhesive interface (P < .05). Additionally, these groups exhibited higher values for quantification and volume of gaps at the luting substrate (P < .05). Scanning electron micrographs and energy dispersive X-ray spectra showed qualitative similarity among all groups, except for the negative experimental control group.

CONCLUSIONS

MB-mediated aPDT at 50 mg/L, in combination with CH, demonstrated favorable physico-chemical and mechanical characteristics in intraradicular dentin, along with satisfactory mechanical features and the adhesive interface integrity for GFPs at all intraradicular depths.

CLINICAL SIGNIFICANCE

MB-mediated aPDT at a concentration of 50 mg/L combined to CH medication represents a suitable choice for photosensitization in the context of intracanal disinfection following the biomechanical procedure and prior to luting of intraradicular restorations.

Does the use of antioxidant agents after dental bleaching compromise the aesthetic results of ceramic laminate veneers?

PURPOSE

This in vitro study aimed to evaluate the aesthetic compromise generated in adhesive interface of ceramic laminate veneer luted after tooth bleaching and the use of antioxidant agents. Thus, the chromatic coordinates and whitening index (WID) were evaluated, comparing whiteness changes (ΔWID) results to perceptibility and acceptability thresholds.

MATERIAL AND METHODS

In total, 88 bovine enamel samples (7 × 8 × 4 mm; n = 8) were submitted to the ceramic laminate veneer luting protocol according to surface treatment (unbleached and bleached enamel), antioxidant agents (control; 10% ascorbic acid and 10% α-tocopherol), and luting periods (after 24 h and after 14 days). To lute IPS e.max ceramic restorations (7 × 8 × 0.6 mm), Tetric N-Bond Universal adhesive system and Variolink Aesthetic LC resin cement were used. An ultraviolet-visible spectrophotometer (UV-VIS) was utilized to measure CIE L*a*b* coordinates prior to and after UV-B artificial accelerated aging for 252, 504, and 756 h. L*, a*, and b* axes were evaluated separately, and the whitening stability (ΔWID) effect was assessed by varying the whiteness index for dentistry (WID). The 50:50% visual threshold was used to evaluate ΔWID values (whiteness perceptibility [WPT] and whiteness acceptability [WAT]). Color parameters changes (ΔL*Δa*Δb*), WID, and ΔWID data were subjected to 2-way repeated measures ANOVA followed by Tukey's test (α = 0.05).

RESULTS

Different UV-aging periods influenced the chromatic coordinates, WID, and ΔWID of the ceramic restorations regardless of the bleaching treatment, antioxidant solutions and luting periods (P < .05). In general, ΔWID values after UV-aging periods were above perceptibility and acceptability thresholds (WPT = 0.72 and WAT = 2.62, respectively) for all experimental groups (P < .05). Unbleached and 10% ascorbic acid-treated enamels luted after 14 days of the antioxidant action exhibited lower ΔL* and Δb* values, while control group showed lower Δa* values. All experimental groups showed similar performance on ΔWID compared to the control group, regardless of the UV-aging period analyzed (P > .05).

CONCLUSION

α-tocopherol is a suitable antioxidant solution to be used 24 h post enamel bleaching not compromising clinical acceptability of ceramic laminate veneers.

CLINICAL RELEVANCE

The adhesive interface of ceramic laminate veneers may appear darker after the use of antioxidant agents affecting the clinical acceptability of the restorations.

Fracture strength and bonding interface morphology of CAD/CAM-fabricated ceramic laminate veneers on bleached enamel treated with two different antioxidants

This study aimed to investigate the effects of two antioxidants and their application time on the fracture strength of computer-aided design and computer-aided manufacturing (CAD/CAM)-fabricated ceramic laminate veneers to bleached enamel, as well as their effects on the bonding interface micromorphology. Eight groups were set: Group NC (without bleaching and antioxidant treatment); Group NA (bleaching without antioxidant treatment); Group SA30, SA60, SA120 and Group PAC30, PAC60, PAC120 (bleaching and treating with sodium ascorbate or proanthocyanidins for 30, 60, and 120 min, respectively). After cementation of veneers, fracture strength values and failure modes were analyzed. The bonding interface morphology was observed by confocal laser scanning microscopy. The fracture strength was impaired when cementation procedure was performed immediately after bleaching. This reduction in fracture strength was reestablished with antioxidant treatment, and an extended treatment time contributed to better improvement. The resin tags at the bonding interfaces of the bleached enamel were impaired. Antioxidant treatments were able to reverse this unfavorable trend.

In vitro study on how photodynamic therapy and calcium hydroxide medication influence adhesive interface properties of glass-fiber posts to intraradicular dentin

PURPOSE

This in vitro study evaluated the influence of antimicrobial photodynamic therapy (aPDT), using methylene blue (MB) as photosensitizer (PS) and calcium hydroxide (CH) as intracanal medication on adhesive bond strength, sealing, and integrity of the luting interface of glass-fiber posts to different thirds of endodontically treated root canal dentin.

MATERIAL AND METHODS

102 incisors were sorted into 6 groups: a negative control irrigated with deionized water; a positive control irrigated with deionized water and filled with CH; CH + MB 50 mg/L without laser radiation; CH + MB 100 mg/L without laser radiation; CH + MB 50 mg/L radiated by red laser; and CH + MB 100 mg/L radiated by red laser. Push-out bond strength (n = 8), adhesive interface sealing (n = 3), and volume and quantification of voids (n = 6) were assessed using a universal testing machine, confocal laser scanning microscope, and computerized microtomography, respectively. Scanning electron micrographs were obtained from representative samples to qualify the fracture patterns. Push-out bond strength and adhesive interface integrity data were subjected to 2-way ANOVA for repeated measures followed by Tukey's test (α = 0.05). Adhesive interface sealing was evaluated by the inter-examiner Kappa test and submitted to Kruskal-Wallis and Dunns tests (α = 0.05).

RESULTS

Assessing the apical region, the positive control and MB_100WA + Ca(OH)₂ groups showed lower adhesive bond strength compared to the MB_100A + Ca(OH)₂ group (P < 0.05). The cervical third showed higher bond strength than the apical third for the positive control, MB_50WA + Ca(OH)_2, MB_100WA + Ca(OH)_2, and MB_50A + Ca(OH)₂ groups (P < 0.05). A prevalence of mixed failure was observed in all experimental groups. There were no statistically significant differences in adhesive interface sealing for any of the parameters assessed (P > 0.05). MB_100WA + Ca(OH)₂ and MB_100A + Ca(OH)₂ groups promoted a higher volume and quantification of voids compared to the negative control group evaluating the cervical third (P < 0.05). In general, there were no differences in the quantification of voids comparing the intraradicular thirds (P > 0.05), differently to the volume of voids in which, in general, the cervical third promoted higher values compared to the middle and apical thirds (P < 0.05).

CONCLUSION

aPDT with methylene blue PS at 50 mg/L associated with calcium hydroxide as intracanal medication demonstrated satisfactory bond strength, sealing, and integrity of the adhesive interface at any intraradicular depth.

Surface characterization of indirect restorative materials submitted to different etching protocols

OBJECTIVES

This in vitro study aimed to evaluate the effect of different times and concentrations of hydrofluoric acid etching on the surface of indirect restorative materials obtained from blocks used in CAD-CAM technology.

METHODS

Specimens (4 mm × 4 mm × 0.8 mm) were obtained for each indirect restorative material: zirconia-reinforced lithium monosilicate ceramic (Celtra Duo), nanoceramic resin (Lava Ultimate), and polymer-infiltrated ceramic network material (Vita Enamic). The materials were submitted to etching with 5% or 10% hydrofluoric acid for 20, 40, 60, or 90 s. A control group for each material was evaluated without any surface treatment, totaling nine experimental groups for each material (n = 10). The specimens were evaluated for surface roughness (R_a and R_z), confocal optical microscopy, the contact angle (θ), surface free energy (γs), total free interaction energy (∆G) using a goniometer, and microshear bond strength to resin cement. Specimen images were obtained using scanning electron microscopy, confocal optical microscopy, and atomic force microscopy. Data on the surface roughness, the contact angle, surface free energy, total free interaction energy, and bond strength were subjected to two-way ANOVA and Tukey´s test (α=0.05).

RESULTS

In general, Celtra Duo showed better results after etching with 10% hydrofluoric acid for 40 or 60 s. Lava Ultimate showed better performance after etching with 10% hydrofluoric acid for 20 or 40 s, whereas Vita Enamic showed better results after etching with 5% hydrofluoric acid for 90 s.

CONCLUSION

Each material showed different characteristics after etching with hydrofluoric acid. Knowledge of the proper protocol for each material is essential to ensure improvements in the adhesion process and durability of indirect restorations. In general, Celtra Duo presented mechanical properties superior to those of Lava Ultimate and Vita Enamic.

CLINICAL SIGNIFICANCE

Specific etching protocols must be recommended for each indirect material because longer exposure to hydrofluoric acid can jeopardize the surface, thus affecting the mechanical and bond strength properties.