Corrosion, surface, and tribological behavior of electrophoretically deposited polyether ether ketone coatings on 316L stainless steel for orthopedic applications

Preparation and characterizations of antibacterial iodine-containing coatings on pure Ti

Iodine-containing coatings were prepared on pure Ti surfaces via electrochemical deposition to enhance their antibacterial properties. The factors influencing iodine content were analyzed using an orthogonal experiment. The electrochemically deposited samples were characterized using scanning electron microscopy with energy dispersive spectroscopy and X-ray photoelectron spectroscopy, and their antibacterial properties and cytotoxicity were evaluated. The results showed that changing the deposition time is an effective way to control the iodine content. The iodine content, coating thickness, and adhesion of the samples increased with deposition time. Iodine in the coatings mainly exists in three forms, which are I2, I3-, and pentavalent iodine. For samples with iodine-containing coatings, the antibacterial ratios against E. coli and S. aureus were greater than 90% and increased with increasing iodine content. Although the samples with iodine-containing coatings showed some inhibition of the proliferation of MC3T3-E1 cells, the cell viabilities were all higher than 80%, suggesting that iodine-containing coatings are biosafe.

Enhancing the tribological performance of PLA-based biocomposites reinforced with graphene oxide

Poly(lactic acid) (PLA) reinforced with graphene has gained substantial interest as a biomaterial, where the tribological and mechanical behavior of PLA/graphene composites are major concerns. This study aims to develop PLA-based biocomposites reinforced with graphene oxide (GO) that have enhanced tribological capabilities. First, homogenous dispersions of GO and GO treated with the anionic surfactant dioctyl sulfosuccinate sodium salt (AOT) were retained. Then, poly(L-lactic acid) (PLLA) biopolymer and PLLA/GO, PLLA/GO(AOT), PLA/GO(AOT), and PLLA/polyethylene glycol (PEG)/GO biocomposite samples were produced via hot pressing, and their tribological behavior was examined in detail. The worn surface characteristics were examined using scanning electron microscopy (SEM), 3D confocal microscopy, and atomic force microscopy (AFM). Results showed that GO reinforcement considerably affected the sliding wear behavior of PLA. Contrary to anticipated, surface treatment of GO does not improve the PLLA/GO wear resistance; rather, it increases the wear rate. PEG positively affects the sliding wear performance of PLLA/GO. PLLA/GO and PLLA/PEG/GO biocomposites exhibited the lowest wear rate at normal loads of 5 and 8 N, respectively, which was decreased by about 50% compared to unreinforced PLLA samples. With the addition of GO, the wear mechanisms of the PLA-based biocomposites changed from adhesive wear to abrasive wear. These findings might increase the applicability of PLA-based biocomposites where tribological performance is the main concern, such as biodegradable implants for load-bearing bone fractures or scaffolds, opening up new opportunities for their use.