Effect of Heated Sodium Hypochlorite on the Viscoelastic Properties of Dentin Evaluated Using Dynamic Mechanical Analysis

Effect of sodium hypochlorite temperature and concentration on the fracture resistance of root dentin

BACKGROUND

Sodium hypochlorite (NaOCl) is the most efficient root canal irrigant to date. The aim of this study was to compare the effect of NaOCl used at different temperatures and concentrations on the compressive strength of root dentin.

MATERIALS AND METHODS

Seventy-two extracted human single-canaled straight roots of comparable size and length were selected and randomly divided into six groups (n = 12): Group (A) served as a control with unprepared canals. The other groups were instrumented with rotary ProTaper Universal files up to size F3. Group (B) was irrigated with 1% NaOCl at room temperature, Group (C) with 1% NaOCl heated to 70 °C, Group (D) with 5.25% NaOCl at room temperature, and Group (E) with 5.25% NaOCl heated to 70 °C. Saline was used in Group (F). The roots were sectioned into 2-mm-thick disks that underwent compression testing using a universal testing machine. Data were analyzed using one-way ANOVA and post hoc Tukey tests. The significance level was set at p ≤ 0.05.

RESULTS

A total of 255 disks were tested. The control group showed the highest compressive strength (p = 0.0112). However, this did not differ significantly from that of heated (p = 0.259) or unheated (p = 0.548) 1% NaOCl. There were no statistically significant differences between the groups of instrumented teeth.

CONCLUSION

Within the conditions of this study, irrigation with NaOCl at different concentrations and temperatures during root canal preparation did not affect the compressive strength of root dentin.

CLINICAL RELEVANCE

This study demonstrates that the use of NaOCl as a root canal irrigant is not associated with a clinically relevant decrease in root compressive strength, especially when compared to saline.

Effect of root canal irrigant (sodium hypochlorite & saline) delivery at different temperatures and durations on pre-load and cyclic-loading surface-strain of anatomically different premolars

AIM

To evaluate the effect of NaOCl (5%) and saline (control) irrigant delivery at different temperatures and durations on pre-load and cyclic-loading tooth-surface-strain (TSS) on anatomically different premolars.

METHODOLOGY

Single-rooted premolars (n = 36), root-canal-prepared in standard manner, were randomly allocated to six irrigation groups: (A1) NaOCl-21 °C; (A2) NaOCl-60 °C; (A3) saline-21 °C then NaOCl-21 °C; (A4) saline-60 °C then NaOCl-21 °C; (A5) saline-21 °C then NaOCl-60 °C; (A6) saline-60 °C then NaOCl-60 °C. A1-2 received nine 10-min irrigation periods (IP) with NaOCl; A3-6 received nine 10-min IP with saline, followed by 9 IP with NaOCl at different temperature combinations. Premolars (n = 56) with single, fused or double roots prepared by standard protocol, were stratified and randomly allocated to: (B1) saline-21 °C; (B2) saline-80 °C; (B3) NaOCl-21 °C; (B4) NaOCl-80 °C. TSS (μє) was recorded pre-irrigation, post-irrigation and pre-load for each IP and during cyclic loading 2 min after each IP, over 30-274 min, using strain-gauges. Generalised linear mixed models were used for analysis.

RESULTS

Baseline TSS in double-rooted premolars was significantly (p=0.001) lower than in single/fused-rooted-premolars; and affected by mesial-wall-thickness (p=0.005). There was significant increase in loading-TSS (μє) after NaOCl-21 °C irrigation (p=0.01) but decrease after NaOCl-60 °C irrigation (p=0.001). TSS also increased significantly (p = 0.005) after Saline-80 °C irrigation. Pre-load "strain-shift" was noted only upon first saline delivery but every-time with NaOCl. Strain-shift negatively influenced loading-TSS after saline or NaOCl irrigation (A3-6) but was only significant for saline-21 °C.

CONCLUSIONS

Tooth anatomy significantly affected its strain characteristics, exhibiting limits within which strain changes occurred. Intra-canal introduction of saline or NaOCl caused non-random strain shifts without loading. Irrigation with NaOCl-21 °C increased loading tooth strain, as did saline-80 °C or NaOCl-80 °C but NaOCl-60 °C decreased it. A "chain-link" model was proposed to explain the findings and tooth biomechanics.