Bimetallic Ni/Cu mesoporous silica nanoparticles as an efficient and reusable catalyst for the Sonogashira cross-coupling reactions

Synergistic performance of a new bimetallic complex supported on magnetic nanoparticles for Sonogashira and C-N coupling reactions

This paper describes the synthesis of a novel Cu-Ni bimetallic system comprising of magnetic nanoparticles, as the core, and 4-amino-3,5-bis(pyridin-2-yl)-1,2,4-triazole (4-ABPT), as a conjugated bridge, between nickel and copper species. With low Cu and Ni loading (0.06 mol% Ni, 0.08 mol% Cu), the resulting Fe3O4@SiO2@4-ABPT/Cu-Ni showed to be a highly efficient catalyst for the Sonogashira and C-N cross-coupling reactions. The developed catalyst was well characterized by FT-IR, XRD, EDX-mapping, FE-SEM, TEM, ICP, VSM, TGA/DTG/DTA, LSV, and XPS techniques. Fe3O4@SiO2@4-ABPT/Cu-Ni nanocatalyst was compatible with a wide range of amines and aryl halides in the Sonogashira and C-N cross-coupling reactions and offered desired coupling products in high to excellent yields under palladium- and solvent-free conditions. Based on the XPS results, the 4-ABPT ligand can adjust electron transfer between Ni and Cu in Fe3O4@SiO2@4-ABPT/Cu-Ni, promoting the formation and stabilization of Cu+ and Ni3+ species. Electronic interactions and the synergistic effect between these metals increased the selectivity and activity of Fe3O4@SiO2@4-ABPT/Cu-Ni catalyst in the Sonogashira and C-N cross-coupling reactions compared with its monometallic counterparts. Additionally, the magnetic properties of Fe3O4@SiO2@4-ABPT/Cu-Ni facilitated its separation from the reaction mixture, promoting its reuse for several times with no significant loss in its catalytic activity or performance.

A novel, efficient and magnetically recyclable Cu-Ni bimetallic alloy nanoparticle as a highly active bifunctional catalyst for Pd-free Sonogashira and C-N cross-coupling reactions: a combined theoretical and experimental study

In this study, a Fe3O4@SiO2@Cyt-Ni/Cu nanocomposite as a novel heterogeneous bimetallic catalyst was synthesized which exhibits efficient performance for the Sonogashira and C-N cross-coupling reactions. The characterization of the catalyst was studied by FT-IR, PXRD, VSM, EDX, TEM, FE-SEM and TGA analyses. The geometry optimization and relative energies of the designed bimetallic complexes were theoretically determined using density functional theory (DFT) calculation at the B3LYP/6-31G**/LANL2DZ level. The catalyst showed good activity in the coupling of various aryl halides with alkynes (Sonogashira reaction) as well as aryl halide with N-heterocycles and achieved coupling products with good to high yields for all of them in a short time. The high catalytic performance could be due to the synergistic effect between Ni and Cu, which causes the reaction to proceed more efficiently. This heterogeneous nanocatalyst could be easily recovered from the reaction mixture with an external magnet and reused for 7 consecutive runs with minimal loss of catalytic activity.

A novel core@double-shell three-layer structure with dendritic fibrous morphology based on Fe3O4@TEA@Ni-organic framework: a highly efficient magnetic catalyst in the microwave-assisted Sonogashira coupling reaction

In synthetic organic chemistry, the formation of carbon-carbon bonds is a significant and substantial reaction. As a result, developing a highly active magnetic heterogeneous catalyst with excellent performance is a very appealing technique for constructing C-C bonds in organic chemistry. The present study describes the fabrication of a novel and readily recoverable nickel-based metal-organic framework (MOF) for C-C bond formation through the Sonogashira coupling reaction. The efficient magnetic core-shell structure (Fe₃O₄@TEA@MOF) with a 3D dendritic fibrous morphology was successfully synthesized using a hydrothermal approach by immobilizing Ni-based MOF onto the Fe₃O₄@TEA core-shell structure. The fabrication of Fe₃O₄@TEA@MOF was confirmed by various analyses; Fourier-transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray analysis (EDS), and elemental mapping confirmed the stepwise fabrication of catalyst. X-ray diffraction analysis (XRD) showed the crystalline nature of the catalyst. Field-emission scanning electron microscopy (FE-SEM) displayed the 3D dendritic fibrous morphology. Thermogravimetric analysis (TGA) and vibrating sample magnetometer analysis (VSM) showed the excellent thermal stability and magnetic properties of Fe₃O₄@TEA@MOF. The Brunauer-Emmett-Teller analysis (BET) found that the fabricated catalyst with a surface area of 36.2 m² g^-1, pore volume of 0.18 cm³ g^-1, and mean pore diameter of 20.38 nm belongs to mesoporous structures. In addition, the information from the inductively coupled plasma-optical emission spectroscopy (ICP-OES) about fresh and reused catalysts showed that the metal leaching amount is slight and about 1.98%. Other advantages of the Fe₃O₄@TEA@MOF catalyst can be mentioned as easily reusable for four runs and high performance (above 98%) in synthesizing diphenylacetylene from phenylacetylene, aryl halide, and cesium carbonate (as the base) under solvent-free and microwave conditions.