Fabrication of ZnFe2O4 films and its application in photoelectrocatalytic degradation of salicylic acid

Norfloxacin mineralization under light exposure using Sb-SnO2 ceramic anodes coated with BiFeO3 photocatalyst

Advanced Oxidation Processes have been proven to be an efficient way to remove organic pollutants from wastewaters. In this work, a ceramic electrode of Sb-SnO₂ (BCE) with a layer of the photocatalytic material BiFeO₃ (BFO-BCE), has been characterized electrochemically and further tested for norfloxacin photo-electrooxidation in the presence and absence of light. The electrode photoactivity was highly enhanced thanks to the presence of BiFeO₃, as confirmed by Linear Sweep Voltammetry, chronoamperometry and potentiometry, and Electrochemical Impedance Spectroscopy. Additionally, working in galvanostatic mode, a high mineralization of norfloxacin was achieved after 240 min, reaching 62% at 25 mA cm^-2 under light conditions. This value is comparatively higher than the 40% achieved with the BCE. The oxidation byproducts were followed by ionic chromatography and HPLC analysis, which also allowed us to propose an oxidation pathway of the norfloxacin molecule. Finally, some indicators of the reactor performance such as the Mineralization Current Efficiency and the specific energy consumption were analyzed, revealing that lower current densities (8.3 mA cm^-2) led to higher current efficiencies, and that light improved both the current efficiency and energy consumption.

Mulberry-like heterostructure (Fe–O–Ti): a novel sensing material for ethanol gas sensors

The gas sensors have been widely used in various fields, to protect the safety of life and property. A novel heterostructure of Fe–O–Ti nanoparticles is fabricated by hydrothermal and wet chemical deposition methods. The Fe–O–Ti nanoparticles with a large number of pores possess high surface area, which is in favour of high-performance gas sensors. Compared with pure Fe₂O₃ and TiO₂, the Fe–O–Ti composite exhibits obviously enhanced sensing characteristics, such as faster response–recovery time (T_res = 6 s, T_rec = 48 s), higher sensing response (response = 35.6) and better selectivity. The results show that the special morphology and large specific surface area of mulberry-like Fe–O–Ti heterostructures provided a large contact area for gas reactions.

The gas sensors have been widely used in various fields, to protect the safety of life and property.

Photoelectrocatalytic degradation of oxalic acid using WO3 and stratified WO3/TiO2 photocatalysts under sunlight illumination

The WO₃ and stratified WO₃/TiO₂ thin films are successfully prepared by the spray pyrolysis method. The structural, morphological, compositional and photoelectrocatalytic properties of WO₃ and stratified WO₃/TiO₂ thin films are studied. XRD analysis confirms that films are polycrystalline with monoclinic and tetragonal crystal structures for WO₃ and TiO₂ respectively. The SEM images clearly show 3D sheeted porous structure of the as-prepared TiO₂ forms on WO₃ in stratified WO₃/TiO₂ samples. The synthesized photoelectrodes was used as catalyst for photoelectrocatalytic degradation of oxalic acid in aqueous medium. The rate constant (k) was evaluated as a function of the initial concentration of species. A significant decrease in concentrations of organic species was observed from COD analysis. The photoelectrocatalytic degradation effect is relatively higher in the case of the stratified WO₃/TiO₂ than WO₃ thin film photoelectrode in the degradation of oxalic acid and 83% removal efficiency of oxalic acid is obtained after 180min. Based on the obtained experimental data, the possible photoelectrocatalytic reaction mechanism was proposed. The photoelectrocatalytic experimental results indicate that stratified WO₃/TiO₂ photoelectrode is the promising material for removing of water pollutants.

Double-Shell Architectures of ZnFe2O4 Nanosheets on ZnO Hollow Spheres for High-Performance Gas Sensors

In this study, double-shell composites consisting of inner ZnO hollow microspheres (ZHS) surrounded by outer ZnFe2O4 nanosheets were successfully synthesized. The growth of the ultrathin ZnFe2O4 nanosheets (∼10 nm) on the ZHS outer surface was carried out at room temperature via solution reactions in order to generate a double-shell configuration that could provide a large surface area. As a proof-of-concept demonstration of the design, a comparative sensing investigation between the sensors based on the as-obtained ZnO/ZnFe2O4 composites and its two individual components (ZnO hollow spheres and ZnFe2O4 nanosheets) was performed. As expected, the response of the ZnFe2O4-decorated ZnO composites to 100 ppm acetone was about 3 times higher than that of initial ZnO microspheres. Moreover, a dramatic reduction of response/recover time has been achieved at different operating temperature. Such favorable sensing performances endow these ZnO/ZnFe2O4 heterostructures with a potential application in gas sensing.