UV/solar light induced photocatalytic degradation of phenols and dyes by Fe(PS-BBP)Cl3

Application of 3D printing technology for green synthesis of Fe2O3 using ABS/TPU/chlorella skeletons for methyl orange removal

Photocatalysis is widely acknowledged as an efficient and environmentally friendly method for treating dye-contaminated wastewater. However, the utilization of powdered photocatalysts presents significant challenges, including issues related to recyclability and the potential for secondary pollution. Herein, a novel technique based on 3D printing for the synthesizing of iron oxide (Fe2O3) involving chlorella was presented. Initially, chlorella powders were immobilized within acrylonitrile butadiene styrene (ABS) and thermoplastic polyurethane (TPU) substrate plastics using melt extrusion technology. Subsequently, these composite materials were transformed into ABS/TPU/chlorella skeletons (ATCh40), through fused deposition molding (FDM) technology. The integration of Fe2O3 onto the ATCh40 (ATCh40-Fe2O3) skeletons was accomplished by subjecting them to controlled heating in an oil bath. A comprehensive characterization of the synthesized materials confirms the successful growth of Fe2O3 on the surface of 3D skeletons. This strategy effectively addresses the immobilization challenges associated with powdered photocatalysts. In photocatalytic degradation experiments targeting methyl orange (MO), the ATCh40-Fe2O3 skeletons exhibited a remarkable MO removal rate of 91% within 240 min. Under conditions where the pH of MO solution was maintained at 3, and the ATCh40-Fe2O3 skeletons were subjected to a heat treatment in a 150 °C blast drying oven for 2 hours, the degradation rate of MO remained substantial, achieving 90% removal after 6 cycles. In contrast, when the same synthetic procedure was applied to ABS/TPU (AT) skeletons, the resulting product was identified as α-FeOOH. The MO removal rate by the AT-α-FeOOH skeletons was considerably lower, reaching only 49% after 240 min. This research provided a practical approach for the construction of photocatalytic devices through the use of 3D printing technology.

Adsorption Characteristics of Phenolic Compounds on Graphene Oxide and Reduced Graphene Oxide: A Batch Experiment Combined Theory Calculation

A series of phenolic compounds containing 2-phenylphenol (PPE), bisphenol A (BPA), 4-isopropylphenol (IPE), 4-methylphenol (ME) and phenol (PE) were selected to investigate their major influence factors for their adsorption on graphene oxide (GO) and reduced graphene oxide (RGO) by studying their adsorption isotherms and kinetics. It was found that the adsorption of all tested phenols fitted well with the Freundlich model. In comparison, the adsorption ability of RGO with a stronger π-π interaction was superior to GO, which was confirmed by using naphthalene probe measurements. The thermodynamic characteristics, by studying the effect of the adsorption temperatures (298, 313 and 333 K), demonstrated that the adsorption process was spontaneous, exothermic and entropy-decreasing. The chemical structures of the phenols also affected their adsorption on GO and RGO. It was found that the adsorption capacities of phenols were, in order, PE (0.271 mmol g−1 on GO and 0.483 mmol g−1 on RGO) < ME (0.356 and 0.841 mmol g−1) < IPE (0.454 and 1.117 mmol g−1) < BPA (0.4 and 1.56 mmol g−1) < PPE (0.7 and 2.054 mmol g−1), which depended on the π-electron density of the benzene ring by means of a density functional theory (DFT) calculation. Undoubtedly, the reduction of GO and an increase in π-electron density on the chemical structures of phenols facilitated the adsorption.