Presence of neodymium and gadolinium in cobalt ferrite lattice: Structural, magnetic and microwave features for electromagnetic wave absorbing

Promoting Electromagnetic Wave Absorption Performance by Integrating MoS2@Gd2O3/MXene Multiple Hetero-Interfaces in Wood-Derived Carbon Aerogels

Multi-component composite materials with a magnetic-dielectric synergistic effect exhibit satisfactory electromagnetic wave absorption performance. However, the effective construction of the structure for these multi-component materials to fully exploit the advantages of each component remains a challenge. Inspired by natural biomass, this study utilizes wood as the raw material and successfully prepares high-performance MoS2@Gd2O3/Mxene loaded porous carbon aerogel (MGMCA) composite material through a one-pot hydrothermal method and carbonization treatment process. With a delicate structural design, the MGMCA is endowed with abundant heterogeneous interface structures, favorable impedance matching characteristics, and a magnetic-dielectric synergistic system, thus demonstrating multiple electromagnetic wave loss mechanisms. Benefiting from these advantages, the obtained MGMCA exhibits outstanding electromagnetic wave absorption performance, with a minimum reflection loss of -57.5 dB at an ultra-thin thickness of only 1.9 mm. This research proposes a reliable strategy for the design of multi-component composite materials, providing valuable insight for the design of biomass-based materials as electromagnetic wave absorbers.

Synthesis of Cobalt Particles and Investigation of Their Electromagnetic Wave Absorption Characteristics

As the integration technology for integrated circuit (IC) packaging continues to advance, the issue of electromagnetic interference in IC packaging becomes increasingly prominent. Magnetic materials, acknowledged for their superior electromagnetic absorption capabilities, play a pivotal role in mitigating electromagnetic interference problems. In this study, we employed a liquid-phase reduction method. We prepared three types of cobalt (Co) particles with distinct morphologies. Through variations in the synthesis process conditions, we were able to control the aspect ratio of protrusions on the surface of the Co particles. It was found that the sword-like Co particles exhibit superior electromagnetic wave absorption capabilities, showing a reflection loss value of up to -50.96 dB. Notably, when the coating thickness is only 1.6 mm, the effective absorption bandwidth is extended up to 7.6 GHz. The spatially expansive sword-like Co particles, with their unique structure featuring dipole polarization and interfacial polarization, demonstrated enhanced dielectric and magnetic loss capabilities, concurrently showcasing superior impedance-matching performance.

Effect of praseodymium in cation distribution, and temperature-dependent magnetic response of cobalt spinel ferrite nanoparticles

This work reports cation distribution, magnetic, structural, and morphological studies of rare-earth Pr doped cobalt ferrite nanoparticles CoFe_2-xPr_xO₄(x= 0, 0.02, 0.04, 0.06 at%) fabricated by sol-gel auto-combustion method. X-ray diffraction analysis, field emission scanning electron microscopy (FESEM), high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), and Fourier-transform infrared (FTIR) microscopy were utilized to study the structural and morphological characteristics of the prepared samples. Rietveld refinement by the Material Analyses Using Diffraction (MAUD) software showed the formation of mono-phase cubic spinel structure with Fd-3m space group; however, there was a trace of impure PrFeO₃phase for the sample CoFe_1.96Pr_0.04O₄(x= 0.06). Cation distribution was inferred from the XRD patterns using MAUD program. FESEM analysis revealed the spherical-shaped particles with dimensions close to the data extracted from XRD analysis and HRTEM images confirmed it. FTIR measurements revealed the presence of two prominent stretching vibrational modes confirming the successful formation of ferrite spinel structure. Magnetic properties of the nanoparticles were measured at two different temperatures 300 K and 10 K. For the low temperature of 10 K a high sensitive measurement method as Superconducting Quantum Interference Device (SQUID) magnetometry was used and Vibrating Sample Magnetometer (VSM) recorded the magnetic data at 300 K. Comparison of the magnetic results exhibited a significant enhancement with temperature drop due to the reduction in thermal fluctuations. Paramagnetic nature of rare-earth ions may be the main reason forM_Sdecrement from 76 emu g^-1(x= 0.0) to 60 emu g^-1(x= 0.02) at 300 K. At 10 K, the estimated cation distribution played a vital role in justification of obtained magnetic results. All the obtained data showed that the synthesized magnetic nanoparticles can be implemented in permanent magnet industry and information storage fields, especially when it comes to lower temperatures.