Gad MM, Abualsaud R, Alqarawi FK, Emam ANM, Khan SQ, Akhtar S, Mahrous AA, Al-Harbi FA. Translucency of nanoparticle-reinforced PMMA denture base material: An in-vitro comparative study.
Dent Mater J 2021;
40:972-978. [PMID:
33883327 DOI:
10.4012/dmj.2020-296]
[Citation(s) in RCA: 15] [Impact Index Per Article: 5.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/23/2022]
Abstract
The aim of this study was to assess the translucency of denture base acrylic resin reinforced with zirconium dioxide (ZrO2NPs), silicon dioxide (SiO2NPs), and diamond (DNPs) nanoparticles. A total of 130 heat-polymerized acrylic discs (15×2.5 mm) were fabricated conventionally and divided into control and experimental groups according to nanoparticle type and concentration (0.5, 1, 1.5, and 2.5 wt%). Unmodified acrylic resin specimens served as control. All specimens were thermocycled (5,000 cycles). Translucency was measured using a spectrophotometer. ANOVA and post-hoc Turkeys' test were used for data analysis at α=0.05. The translucency of modified PMMA was significantly lower than control (p<0.05) except 0.5% ZrO2NPs and SiO2NPs (p>0.05) which exhibited the highest translucency values among modified groups. As the NPs concentration increased, the translucency decreased and the lowest value was seen with 2.5% DNPs (1.18±0.10). The addition of ZrO2NPs, SiO2NPs, and DNPs into denture base resin decreased the translucency.
Collapse