Structural characterization, magnetic behavior and high-resolution EELS study of new perovskites Sr2Ru2−xCoxO6−δ (0.5⩽x⩽1.5)

Epitaxial synthesis and physical properties of double-perovskite oxide Sr2CoRuO6 thin films

We report epitaxial structures and physical properties of double-perovskite Sr2CoRuO6 films grown using pulsed-laser deposition. Samples with a degree of Co/Ru order of 2-73% were obtained by changing growth temperature. X-ray absorption spectroscopy (XAS) on the highest ordered sample revealed that Co ions were trivalent with a high-spin configuration and Ru ions were pentavalent. We found large differences in magnetization and resistivity between the highest and lowest ordered samples as well as the absence of strong magnetism and metallicity, which are common characteristics of SrCoO3 and SrRuO3. Using resonant photoemission spectroscopy and XAS, dominant d-orbital components at the top of the occupied state (the bottom of the unoccupied state) were identified to be Ru 4d t 2g (Co 3d and Ru 4d t 2g ). These results suggest that the ground state of double-perovskite Sr2CoRuO6 is a ferrimagnetic insulator.

A complete high-to-low spin state transition of trivalent cobalt ion in octahedral symmetry in SrCo0.5Ru0.5O(3-δ)

The complex metal oxide SrCo0.5Ru0.5O(3-δ) possesses a slightly distorted perovskite crystal structure. Its insulating nature infers a well-defined charge distribution, and the six-fold coordinated transition metals have the oxidation states +5 for ruthenium and +3 for cobalt as observed by X-ray spectroscopy. We have discovered that Co(3+) ion is purely high-spin at room temperature, which is unique for a Co(3+) in an octahedral oxygen surrounding. We attribute this to the crystal field interaction being weaker than the Hund's-rule exchange due to a relatively large mean Co-O distances of 1.98(2) Å, as obtained by EXAFS and X-ray diffraction experiments. A gradual high-to-low spin state transition is completed by applying high hydrostatic pressure of up to 40 GPa. Across this spin state transition, the Co Kβ emission spectra can be fully explained by a weighted sum of the high-spin and low-spin spectra. Thereby is the much debated intermediate spin state of Co(3+) absent in this material. These results allow us to draw an energy diagram depicting relative stabilities of the high-, intermediate-, and low-spin states as functions of the metal-oxygen bond length for a Co(3+) ion in an octahedral coordination.