Two acidic coordination polymers containing uncoordinated carboxyl groups: Syntheses, crystal structures and proton conductivities in Nafion composite membranes

A simple MOF constructed using Pb(II) with strong polarizing force: a filler of Nafion membrane to increase proton conductivity

Metal-organic frameworks (MOFs) are promising competitive candidates as fillers for Nafion proton exchange membrane (PEM). Increasing efforts have been made to explore methods for synthesizing MOF fillers and the mechanism by which MOF doping improves the proton conductivity (σH+) values of composite membranes. In this study, a Pb(II) cation with strong polarizing force was selected for the hydrothermal reaction with a simple sulfoterephthalate ligand (H3L). Pb-MOF [Pb2L(OH)]n was obtained, which was constructed using Pb-O layers and deprotonated sulfoterephthalate L3- and exhibited good thermal and water stability. Different amounts of Pb-MOF particles were doped into Nafion to fabricate Pb-MOF/Nafion-x composite membranes, which were characterized using SEM, PXRD, IR spectroscopy, TGA, and other methods. It was found that doping Pb-MOF can apparently improve the water absorbability and thermal stability of the composite membrane. The σH+ of the Pb-MOF/Nafion-7 composite membrane was the highest and 2.14 times that of the pure Nafion membrane at 353 K. The higher proton conduction properties may be explained by the strong polarization force, and Pb(II) cations on the surface of Pb-MOF can decrease the bond energy of the O-H bond of absorbed water molecules and increase the acidity of the composite membrane. The phenomena in this study and our previous study confirm that acidity is the most important factor in favor of proton conductivity.

Enhancing Proton Conductivity of Nafion Membrane by Incorporating Porous Tb-Metal-Organic Framework Modified with Nitro Groups

A rigid carboxylate ligand with a nitro functional group was selected to coordinate with Tb(III) cation, and Tb-MOF ({[Tb₄(L)₄(OH)₄(H₂O)₃]·8H₂O}_n, H₂L = 2-nitroterephthalic acid) with large porous and excellent hydrophilicity was obtained successfully. The obtained Tb-MOF was filled into the Nafion matrix to improve its proton conduction performance. The Tb-MOF/Nafion composite membrane was characterized by PXRD, IR, and thermogravimetry (TG) and for water uptake, area swelling, and proton conductivity. The activity energy, E_a, value of the composite membrane, which is a very important factor affecting the proton conduction performance of the membrane, was fitted and calculated. It was revealed that Tb-MOF can improve the proton conductivities of composite membranes, and the improvement degree and E_a value were both affected by Tb-MOF content. When Tb-MOF content was 5%, the proton conductivity of the composite membrane was 1.53 × 10^-2 S·cm^-1 at 100% RH and 80 °C, which is 1.81 times that of the pure Nafion membrane. A MOF containing a nitro functional group was first doped into Nafion in this study and exhibited excellent performance for improving composite membrane proton conductivity. This study will provide a valuable reference for designing different functionalized MOFs to promote the proton conductivities of proton exchange membranes.

Proton conductivities of four low dimensional MOFs: affected by the amount of chelated ligands

The smaller the proportion of the chelated ligand, the more water molecules in the compound, which increases the chance of forming continuous hydrogen bonds, enhances the water absorption ability, and improves the proton conductivity of the compound.