Effect of pH on Ferromagnetic Iron Oxide Nanoparticles

Sustainable Nanomagnetism: Investigating the Influence of Green Synthesis and pH on Iron Oxide Nanoparticles for Enhanced Biomedical Applications

This study comprehensively analyzed green nanomagnetic iron oxide particles (GNMIOPs) synthesized using a green method, investigating their size, shape, crystallinity, aggregation, phase portions, stability, and magnetism. The influence of pH and washing solvents on the magnetic properties of the nanoparticles and their incorporation into PCL membranes was examined for biomedical applications. Polyphenols were utilized at different pH values (1.2, 7.5, and 12.5), with washing being performed using either ethanol or water. Characterization techniques, including XRD, SEM, TEM, FTIR, and VSM, were employed, along with evaluations of stability, magnetic properties, and antioxidant activity. The findings indicate that both pH levels and the washing process exert a substantial influence on several properties of NMIOPs. The particle sizes ranged from 6.6 to 23.5 nm, with the smallest size being observed for GNMIOPs prepared at pH 12.5. Higher pH values led to increased crystallinity, cubic Fe3O4 fractions, and reduced crystalline anisotropy. SEM and TEM analyses showed pH-dependent morphological variations, with increased aggregation being observed at lower pH values. GNMIOPs displayed exceptional magnetic behavior, with the highest saturation magnetization being observed in GNMIOPs prepared at pH 7.5 and 12.5 and subsequently washed with ethanol. The zeta potential measurements indicated a stability range for GNMIOPs spanning from -31.8 to -41.6 mV, while GNMIOPs synthesized under high-pH conditions demonstrated noteworthy antioxidant activity. Furthermore, it was explored how pH and washing solvent affected the morphology, roughness, and magnetic properties of GNMIOP-infused nanofiber membranes. SEM showed irregularities and roughness due to GNMIOPs, varying with pH and washing solvent. TEM confirmed better dispersion with ethanol washing. The magnetic response was stronger with ethanol-washed GNMIOPs, highlighting the influence of pH and washing solvent on membrane characteristics.

Quantifying the Structure and Properties of Nanomagnetic Iron Oxide Particles for Enhanced Functionality through Chemical Synthesis

This comprehensive study investigates the properties of chemical nanomagnetic iron oxide particles (CNMIOPs) synthesized through a chemical method. The primary objective is to examine how pH levels and washing solvents affect the magnetism properties of these nanoparticles. Three different pH levels (1.2, 7.5, and 12.5) using NaOH and two washing solvents (ethanol and water) are employed. The characterization techniques include FTIR, SEM, TEM, XRD, ZSP, and VSM. Furthermore, the study incorporates two specific pH- and solvent-dependent CNMIOPs into PCL electrospun materials to analyze their performance in a targeted application. The results show that pH and the washing process significantly affect the CNMIOPs' properties. Higher pH levels result in smaller particles with higher crystallinity and reduce crystalline anisotropy. SEM and TEM analysis confirm different morphologies, including cubic, spherical, and elongated shapes. Ethanol-washed CNMIOPs exhibit superior magnetic behavior, with the highest magnetization saturation at pH 12.5 (Ms = 58.3 emu/g). The stability of the CNMIOPs ranges from -14.7 to -23.8 mV, and higher pH levels exhibit promising antioxidant activity. Furthermore, the study explores the effects of pH and washing solvents on CNMIOP-infused nanofiber membranes, with better dispersion observed with ethanol washing. Overall, this research provides valuable insights into the properties and behavior of CNMIOPs under varying pH and washing conditions.