Insight into the Meerwein-Ponndorf-Verley reduction of cinnamaldehyde over MgAl oxides catalysts

Isomorphic Insertion of Ce(III)/Ce(IV) Centers into Layered Double Hydroxide as a Heterogeneous Multifunctional Catalyst for Efficient Meerwein-Ponndorf-Verley Reduction

The development of highly active acid-base catalysts for transfer hydrogenations of biomass derived carbonyl compounds is a pressing challenge. Solid frustrated Lewis pairs (FLP) catalysis is possibly a solution, but the development of this concept is still at a very early stage. Herein, stable, phase-pure, crystalline hydrotalcite-like compounds were synthesized by incorporating cerium cations into layered double hydroxide (MgAlCe-LDH). Besides the insertion of well-isolated cerium centers surrounded by hydroxyl groups, the formation of hydroxyl vacancies near the aluminum centers, which were formed by the insertion of cerium centers into the layered double hydroxides (LDH) lattice, was also identified. Depending on the initial cerium concentration, LDHs with different Ce(III)/Ce(IV) ratios were produced, which had Lewis acidic and basic characters, respectively. However, the acid-base character of these LDHs was related to the actual Ce(III)/Ce(IV) molar ratios, resulting in significant differences in their catalytic performance. The as-prepared structures enabled varying degrees of transfer hydrogenation (Meerwein-Ponndorf-Verley MPV reduction) of biomass-derived carbonyl compounds to the corresponding alcohols without the collapse of the original lamellar structure of the LDH. The catalytic markers through the test reactions were changed as a function of the amount of Ce(III) centers, indicating the active role of Ce(III)-OH units. However, the cooperative interplay between the active sites of Ce(III)-containing specimens and the hydroxyl vacancies was necessary to maximize catalytic efficiency, pointing out that Ce-containing LDH is a potentially commercial solid FLP catalysts. Furthermore, the crucial role of the surface hydroxyl groups in the MPV reactions and the negative impact of the interlamellar water molecules on the catalytic activity of MgAlCe-LDH were demonstrated. These solid FLP-like catalysts exhibited excellent catalytic performance (cyclohexanol yield of 45%; furfuryl alcohol yield of 51%), which is competitive to the benchmark Sn- and Zr-containing zeolite catalysts, under mild reaction conditions, especially at low temperature (T = 65 °C).

Mixed Oxides Derived from Hydrotalcites Mg/Al Active in the Catalytic Transfer Hydrogenation of Furfural to Furfuryl Alcohol

Herein, a family of Mg/Al hydrotalcites was synthesized as catalytic precursors of MgAlOx mixed oxides. Both hydrotalcites and mixed oxides were characterized and the mixed oxides were tested in the reduction of furfural to yield furfuryl alcohol by MPV reaction using isopropanol as hydrogen donor. Different catalytic parameters were tested, such as the type of alcohol, calcination temperature of the hydrotalcite, and reaction temperature. Furfural and isopropanol were adsorbed on the MgAl-3 catalyst to follow the species adsorbed on the catalyst by FTIR analysis. The results showed that the isopropanol was activated as isopropoxide and furfural changed the adsorption site with increasing temperature but maintaining the h1-conformation. The catalytic performances were associated with the basicity of the catalysts and the deactivation processes have been attributed to the existence of adsorbed species on the surface, mainly due to furfural-derived compounds. The catalysts were reused in three consecutive cycles showing a sharp drop of catalytic activity. To recover the activity, the catalysts were calcined at 500 °C but the activity was only partially recovered. The XPS analysis after reactivation showed that the catalyst surface was modified due to the segregation of hydroxides of Mg and Al.

Metal-doped mesoporous ZrO2 catalyzed chemoselective synthesis of allylic alcohols from Meerwein–Ponndorf–Verley reduction of α,β-unsaturated aldehydes

The activity of the Cr_ZrO₂ catalyst is attributed to the Cr–Zr electronic interaction, which resulted in the enhanced surface acidity on ZrO₂.

Influence of Structure-modifying Agents in the Synthesis of Zr-doped SBA-15 Silica and Their Use as Catalysts in the Furfural Hydrogenation to Obtain High Value-added Products through the Meerwein-Ponndorf-Verley Reduction

Zr-doped mesoporous silicas with different textural parameters have been synthesized in the presence of structure-modifying agents, and then characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N₂ adsorption-desorption at −196 °C, NH₃ thermoprogrammed desorption (NH₃–TPD), CO₂ thermoprogrammed desorption (CO₂–TPD), and X-ray photoelectron spectroscopy (XPS). These porous materials were evaluated in the furfural hydrogenation through the Meerwein-Ponndorf-Verley (MPV) reaction. The catalytic results indicate that the catalyst synthesized under hydrothermal conditions and adding a pore expander agent is more active and selective to furfuryl alcohol. However, the Zr-doped porous silica catalysts that were synthesized at room temperature, which possess narrow pore sizes, tend to form i-propyl furfuryl and difurfuryl ethers, coming from etherification between furfuryl alcohol (FOL) and isopropanol molecules (used as H-donor) by a S_N2 mechanism.