Relationship between the WO3 states and reaction pathway over CeO2-ZrO2-WO3 catalysts for selective catalytic reduction of NO with NH3

Ce1−xFexVO4 with Improved Activity for Catalytic Reduction of NO with NH3

A series of Ce1−xFexVO4 (x = 0, 0.25, 0.50, 0.75, 1) catalysts prepared by modified hydrothermal synthesis were used for selective catalytic reduction (SCR) of NOx with NH3. Among them, Ce0.5Fe0.5VO4 showed the highest catalytic activity. The catalysts were characterized by X-ray diffraction (XRD), N2 adsorption–desorption, scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX), X-ray fluorescence (XRF), X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction using H2 (H2-TPR), and temperature-programmed desorption of NH3 (NH3-TPD). The results indicated the formation of Ce-Fe-V-O solid solutions. The average oxidation states (AOS) of Ce, Fe, V, and O atoms changed obviously with the incorporation of Fe3+ into CeVO4, and the acidity of Ce0.5Fe0.5VO4 differs from that of CeVO4 and FeVO4. The presence of more acid sites and a sharp increase in active oxygen species in Ce0.5Fe0.5VO4 effectively improved the selective catalytic reduction (SCR) activity.

Tungsten-Based Catalysts for Environmental Applications

This review aims to give a general overview of the recent use of tungsten-based catalysts for wide environmental applications, with first some useful background information about tungsten oxides. Tungsten oxide materials exhibit suitable behaviors for surface reactions and catalysis such as acidic properties (mainly Brønsted sites), redox and adsorption properties (due to the presence of oxygen vacancies) and a photostimulation response under visible light (2.6–2.8 eV bandgap). Depending on the operating condition of the catalytic process, each of these behaviors is tunable by controlling structure and morphology (e.g., nanoplates, nanosheets, nanorods, nanowires, nanomesh, microflowers, hollow nanospheres) and/or interactions with other compounds such as conductors (carbon), semiconductors or other oxides (e.g., TiO2) and precious metals. WOx particles can be also dispersed on high specific surface area supports. Based on these behaviors, WO3-based catalysts were developed for numerous environmental applications. This review is divided into five main parts: structure of tungsten-based catalysts, acidity of supported tungsten oxide catalysts, WO3 catalysts for DeNOx applications, total oxidation of volatile organic compounds in gas phase and gas sensors and pollutant remediation in liquid phase (photocatalysis).

Design of co-symbiotic FexMnyO catalysts for NO reduction by CO

Fe_xMn_yO catalyst with different Fe content was prepared by ethylene glycol solvent-thermal method, and the CO-SCR activity of Fe_xMn_yO catalyst was tested to investigate the influence of Fe doping amount on the activity of manganese based catalyst.

Comparison of support synthesis methods for TiO2and the effects of surface sulfates on its activity toward NH3-SCR

Addition of SO₄²⁻inhibits the transformation of TiO₂from anatase to rutile and generates sulfate salts to increase the surface acidity.