Hydrogen permeability of sulfur tolerant Pd–Cu alloy membranes

Recent Developments in Compact Membrane Reactors with Hydrogen Separation

Hydrogen production and storage in small and medium scale, and chemical heat storage from renewable energy, are of great interest nowadays. Micro-membrane reactors for reforming of methane, as well as for the dehydrogenation of liquid organic hydrogen carriers (LOHCs), have been developed. The systems consist of stacked plates with integrated palladium (Pd) membranes. As an alternative to rolled and electroless plated (Pd) membranes, the development of a cost-effective method for the fabrication of Pd membranes by suspension plasma spraying is presented.

Supported Pd-Au Membrane Reactor for Hydrogen Production: Membrane Preparation, Characterization and Testing

A supported Pd-Au (Au 7wt%) membrane was produced by electroless plating deposition. Permeation tests were performed with pure gas (H₂, H₂, N₂, CO₂, CH₄) for long time operation. After around 400 h under testing, the composite Pd-Au membrane achieved steady state condition, with an H₂/N₂ ideal selectivity of around 500 at 420 °C and 50 kPa as transmembrane pressure, remaining stable up to 1100 h under operation. Afterwards, the membrane was allocated in a membrane reactor module for methane steam reforming reaction tests. As a preliminary application, at 420 °C, 300 kPa of reaction pressure, space velocity of 4100 h⁻¹, 40% methane conversion and 35% hydrogen recovery were reached using a commercial Ni/Al₂O₃ catalyst. Unfortunately, a severe coke deposition affected irreversibly the composite membrane, determining the loss of the hydrogen permeation characteristics of the supported Pd-Au membrane.

Volatile Heterobimetallic Complexes from PdII and CuII β-Diketonates: Structure, Magnetic Anisotropy, and Thermal Properties Related to the Chemical Vapor Deposition of CuPd Thin Films

A novel approach for preparing volatile heterometallic complexes for use as precursors for the chemical vapor deposition of various materials is reported. New CuPd complexes based on β-diketonate units were prepared, and their structures and compositions were determined. [PdL₂ *CuL₂ ] (1) and [PdL₂ *Cu(tmhd)₂ ] (2) (L=2-methoxy-2,6,6-trimethylheptane-3,5-dionate; tmhd=2,2,6,6- tetramethylheptane-3,5-dionate) are 1D coordination polymers with alternating metal complexes, which are connected through weak interactions between the Cu atoms and the OCH₃ groups from the ligand of the Pd complexes. The volatility and thermal stability were studied using thermogravimetric and differential thermal analyses and mass spectrometry. Compound 1 vaporizes without decomposition into monometallic complexes. It exhibits magnetic anisotropy, which was revealed from the angular variations in the EPR spectrum of a single crystal. The vapor thermolysis process for 1 was investigated using mass spectrometry, allowing the process to be framed within the temperature range of 200-350 °C. The experimental data, supported by QTAIM calculations of the allowed intermolecular interactions, suggest that 1 likely exists in the gas phase as bimetallic molecules. Compound 1 proved to be suitable as a single-source precursor for the efficient preparation of CuPd alloy films with tunable Cu/Pd ratio. A possible mechanism for the film growth is proposed based on the reported data.