KOH-doped polybenzimidazole for alkaline direct glycerol fuel cells

Preparation of Alkaline Polyelectrolyte Membrane Based on Quaternary Ammonium Salt-Modified Cellulose and Its Application in Zn-Air Flexible Battery

In this study, a type of alkaline solid polyelectrolyte (ASPE) membrane was developed via the introduction of microcrystalline cellulose (MCC) and its modified product (QMCC) into the polyvinyl alcohol (PVA) matrix. In this process, green NaOH/urea-based solvent was used to achieve a good dispersion of MCC in the PVA matrix; meanwhile, the OH^- groups in the NaOH/urea-based solvent provided an alkaline environment for good ion conductivity. Compared to the MCC-incorporated ASPE, further improved conductivity was achieved when the MCC was modified with quantitative quaternary ammonium salt. TGA showed that the addition of QMCC improved the water retention of the matrix, which was beneficial to the OH^- conduction in the system. Compared to the control (50 mS cm^-1), a maximum conductivity of 238 mS cm^-1 was obtained after the incorporation of QMCC in the PVA matrix. Moreover, the tensile strength of the polymer electrolyte were also significantly increased with the addition of QMCC. Finally, this developed ASPE membrane was used in assembling a flexible Zn-air battery and showed a promising potential in the development of flexible electronic devices.

KOH-doped Porous Polybenzimidazole Membranes for Solid Alkaline Fuel Cells

In this study the preparation and properties of potassium hydroxide-doped meta-polybenzimidazole membranes with 20–30 μm thickness are reported as anion conducting polymer electrolyte for application in fuel cells. Dibutyl phthalate as porogen forms an asymmetrically porous structure of membranes along thickness direction. One side of the membranes has a dense skin layer surface with 1.5–15 μm and the other side of the membranes has a porous one. It demonstrated that ion conductivity of the potassium hydroxide-doped porous membrane with the porogen content of 47 wt.% (0.090 S cm−1), is 1.4 times higher than the potassium hydroxide-doped dense membrane (0.065 S cm−1). This is because the porous membrane allows 1.4 times higher potassium hydroxide uptake than dense membranes. Tensile strength and elongation studies confirm that doping by simply immersing membranes in potassium hydroxide solutions was sufficient to fill in the inner pores. The membrane-electrode assembly using the asymmetrically porous membrane with 1.4 times higher ionic conductivity than the dense non-doped polybenzimidazole (mPBI) membrane showed 1.25 times higher peak power density.

Cationic ether-free poly(bis-alkylimidazolium) ionene blend polybenzimidazole as anion exchange membranes

A new simple route towards ether-free AEM design and fabrication with a wide potential structural scope.

Glycerol Electro-Oxidation in Alkaline Media and Alkaline Direct Glycerol Fuel Cells

The low price, highly active triol structure, high volumetric energy density, simple storage and environment-friendly properties make glycerol a promising fuel for an alkaline direct alcohol fuel cell (ADAFC). Unlike other ADAFCs, alkaline direct glycerol fuel cells (ADGFCs) can be used either to generate only energy (the common use of fuel cells) or to produce both energy and valuable chemicals. This work presents an overview of catalysts for glycerol oxidation in alkaline media, and their use in ADGFCs. A particular attention was paid to binary and ternary catalysts able both to increase the selectivity to valuable C3 glycerol oxidation products, reducing the C–C bond cleavage, and simultaneously to enhance glycerol conversion.