Porous nanofibrous composite membrane for unparalleled proton conduction

Zwitterion-functionalized nanofiber-based composite proton exchange membranes with superior ionic conductivity and chemical stability for direct methanol fuel cells

Proton exchange membranes with high ionic conductivity and good chemical stability are critical for achieving high power density and long lifespan of direct methanol cells (DMFCs). Herein, a zwitterionic molecule was grafted onto the surface of polyvinylidene fluoride (PVDF) nanofibers to obtain functionalized PVDF porous substrate (SBMA-PDA@PVDF). Then, sulfonated poly(ether ether ketone) (SPEEK) was filled into the pores of SBMA-PDA@PVDF, and further ionic cross-linked via H2SO4 to prepare the composite membrane (SBMA-PDA@PVDF/SPEEK). The basic groups on the zwitterionic interface could not only establish ionic cross-linking with SPEEK to increase chemical stability and reduce swelling, but also serve as the adsorption sites for subsequent H2SO4 cross-linking to significantly enhance proton conductivity. Super-high proton conductivity (165.34 mS cm-1, 80 °C) was achieved for the membrane, which was 2.12 times higher than that of the pure SPEEK. Moreover, the SBMA-PDA@PVDF/SPEEK membrane exhibited remarkably improved oxidative stability of 91.6 % mass retention after soaking in Fenton's agent for 12 h, while pure SPEEK completely decomposed. Satisfactorily, the DMFC assembled with SBMA-PDA@PVDF/SPEEK exhibited a peak power density of 99.01 mW cm-2, which was twice as much as that of commercial Nafion 212 (48.88 mW cm-2). After 235 h durability test, only 11 % voltage loss was observed.

‘Proton escalator’ PEI and phosphotungstic acid containing nanofiber membrane with remarkable proton conductivity

Polyethyleneimine (PEI) and phosphotungstic acid (HPW) build an efficient proton transmission path. The segmental movement of flexible PEI speeds up the migration of protons, which acts as a ‘proton-escalator’.

One Dimensional Enhanced Anhydrous Proton Conduction in Well Defined Molecular Columns Induced by Non-Covalent Interactions

1D anhydrous proton conduction is enhanced significantly in ionic channels created by self-assembly of functionalized organic phosphonic acid and aromatic heterocyclic 1,2,4-triazole molecules. This study reveals high proton conduction in one dimension through a well-defined supramolecular architecture in which two different molecules undergo host-guest synergy and self-assemble to provide two-fold advantages: 1) formation of the ionic channels and 2) higher proton conduction in the absence of water. A clear correlation is found between the phenomena of ionic channels and anhydrous conductivity in the absolute dry state and we demonstrate that the one-dimensional conductivity can be as high as that recorded for 3D channels in, for instance, Nafion.

Solution Blown Nylon 6 Nanofibrous Membrane as Scaffold for Nanofiltration

In this work, a nylon 6 nanofibrous membrane was prepared via solution blowing technology and followed hot-press as scaffold for nanofiltration. The structure and properties of the hot-pressed nylon 6 nanofibrous membrane (HNM) were studied the effect of hot-pressing parameters and areal densities. Then an ultra-thin polyamide (PA) active layer was prepared by interfacial polymerization on HNM. The effects of nanofibrous scaffolds on the surface properties of ultra-thin nanofiltration membranes and their filtration performance were studied. Results showed that the nylon 6 nanofibers prepared at a concentration of 15 wt % had a good morphology and diameter distribution and the nanofibers were stacked more tightly and significantly reduced in diameter after hot pressing at 180 °C under the pressure of 15 MPa for 10 s. When the porous scaffold was prepared, HNM with an areal density of 9.4 and 14.1 g/m² has a better apparent structure, a smaller pore size, a higher porosity and a greater strength. At the same time, different areal densities of HNM have an important influence on the preparation and properties of nanofiltration membranes. With the increase of areal density, the uniformity of HNM increased while their surface roughness and pore size decreased, which is beneficial to the establishment of PA barrier layer. With areal density of 9.4 and 14.1 g/m², the as-prepared nanofiltration membrane has a smoother surface and more outstanding filtration performance. The pure water flux is 13.1 L m⁻² h⁻¹ and the filtration efficiencies for NaCl and Na₂SO₄ are 81.3% and 85.1%, respectively.