Novel turbidimetric method to study polymer swelling

Synthesis and Characterization of N-Isopropylacrylamide Microspheres as pH Sensors

Swellable polymer microspheres that respond to pH were prepared by free radical dispersion polymerization using N-isopropylacrylamide (NIPA), N,N^'-methylenebisacrylamide (MBA), 2,2-dimethoxy-2-phenylacetylphenone, N-tert-butylacrylamide (NTBA), and a pH-sensitive functional comonomer (acrylic acid, methacrylic acid, ethacrylic acid, or propacrylic acid). The diameter of the microspheres was between 0.5 and 1.0 μm. These microspheres were cast into hydrogel membranes prepared by mixing the pH-sensitive swellable polymer particles with aqueous polyvinyl alcohol (PVA) solutions followed by crosslinking with glutaric dialdehyde for use as pH sensors. Large changes in the turbidity of the PVA membrane were observed as the pH of the buffer solution in contact with the membrane was varied. These changes were monitored by UV-visible absorbance spectroscopy. Polymer swelling of many NIPA copolymers was reversible and independent of the ionic strength of the buffer solution in contact with the membrane. Both the degree of swelling and the apparent pK_a of the polymer microspheres increased with temperature. Furthermore, the apparent pK_a of the polymer particles could be tuned to respond sharply to pH in a broad range (pH 4.0-7.0) by varying the amount of crosslinker (MBA) and transition temperature modifier (NTBA), and the amount, pK_a, and hydrophobicity of the pH-sensitive functional comonomer (alkyl acrylic acid) used in the formulation. Potential applications of these polymer particles include fiber optic pH sensing where the pH-sensitive material can be immobilized on the distol end of an optical fiber.

Swellable Copolymers of N-isopropylacrylamide and Alkyl Acrylic Acids for Optical pH Sensing

Swellable polymers that respond to pH (including a portion of the physiological pH range) have been prepared from N-isopropylacrylamide (NIPA) copolymerized with acrylic acid, methacrylic acid, ethacrylic acid or propacrylic acid by dispersion polymerization. When the swellable polymer particles are dispersed in a polyvinyl alcohol (PVA) hydrogel membrane, large changes occur in the turbidity of the membrane (which is measured using an absorbance spectrometer) as the pH of the buffer solution in contact with the hydrogel membrane is varied. The swelling of the NIPA copolymer is nonionic, as the ionic strength of the buffer solution in contact with the PVA membrane was increased from 0.1 to 1.0 M without a decrease in the swelling. For many of these NIPA copolymers, swelling was also reversible in both low- and high ionic strength pH-buffered media and at ambient and physiological temperatures. The composition of the formulation used to prepare these copolymers of NIPA can be correlated to the enthalpy and entropy of the pH-induced swelling.