Extraction of organic compounds released from dental materials

Evaluation of the Impact of Irradiance Lamps and Storage Media on Elution of TEGDMA from Dental Composites

OBJECTIVES

 The aim of this study was to evaluate and compare the effect of irradiance light and storage media on the elution of triethylene glycol dimethacrylate (TEGDMA) from conventional Filtek Z350XT 3M ESPE and two bulk-fill composites Shofu Beautifil-Bulk and Filtek Bulk fill flowable 3M ESPE using high-performance liquid chromatography (HPLC).

MATERIALS AND METHODS

 Shofu Beautifil-Bulk, Filtek Bulk fill flowable 3M ESPE, and Filtek Z350XT 3M ESPE were the three types of composites used in this study. Disk shaped samples of 4-mm thickness and 10-mm diameter were fabricated using a stainless steel mold and were polymerized using light emitting diode (LED) and quartz tungsten halogen (QTH) lamps. After polymerization, the samples were immersed in ethanol, artificial saliva with betel quid extract, and distilled water for 1, 7, and 30 days, respectively. The elution of monomer TEGDMA was evaluated using HPLC.

STATISTICAL ANALYSIS

 To evaluate the mean concentration difference, mixed way analysis of variance (ANOVA) was applied. Between different light, materials, and within the time duration, Tukey's post hoc test was used. A p value of 0.05 was considered significant.

RESULTS

 During the first day of storage, a significant amount of monomer TEGDMA elution was seen in all the materials. The highest values observed to be in the disks cured with QTH lamp. However, the highest elution was seen when the disks were immersed in ethanol/water solution. While the most stable medium was distilled water, artificial saliva with betel nut extract also had a significant effect on the elution of TEGDMA. The highest value obtained was of Filtek Bulk fill flowable 3M ESPE after 30 days of immersion in both LED and QTH cured disks.

CONCLUSION

 Filtek Bulk fill flowable 3M ESPE shows better properties in relation to the release of monomer TEGDMA as it releases less amount of monomer in the storage media. The release of monomer was highest in ethanol as compared to artificial saliva and distilled water with the passage of time.

Monomer Release from Dental Resins: The Current Status on Study Setup, Detection and Quantification for In Vitro Testing

Improvements in mechanical properties and a shift of focus towards esthetic dentistry led to the application of dental resins in various areas of dentistry. However, dental resins are not inert in the oral environment and may release monomers and other substances such as Bisphenol-A (BPA) due to incomplete polymerization and intraoral degradation. Current research shows that various monomers present cytotoxic, genotoxic, proinflammatory, and even mutagenic effects. Of these eluting substances, the elution of BPA in the oral environment is of particular interest due to its role as an endocrine disruptor. For this reason, the release of residual monomers and especially BPA from dental resins has been a cause for public concern. The assessment of patient exposure and potential health risks of dental monomers require a reliable experimental and analytical setup. However, the heterogeneous study design applied in current research hinders biocompatibility testing by impeding comparative analysis of different studies and transfer to the clinical situation. Therefore, this review aims to provide information on each step of a robust experimental and analytical in vitro setup that allows the collection of clinically relevant data and future meta-analytical evaluations.