Quantitative analysis of defects and domain boundaries in mesoporous SBA-16 films

Bismuth incorporation and the role of ordering in GaAsBi/GaAs structures

The structure and composition of single GaAsBi/GaAs epilayers grown by molecular beam epitaxy were investigated by optical and transmission electron microscopy techniques. Firstly, the GaAsBi layers exhibit two distinct regions and a varying Bi composition profile in the growth direction. In the lower (25 nm) region, the Bi content decays exponentially from an initial maximum value, while the upper region comprises an almost constant Bi content until the end of the layer. Secondly, despite the relatively low Bi content, CuPtB-type ordering was observed both in electron diffraction patterns and in fast Fourier transform reconstructions from high-resolution transmission electron microscopy images. The estimation of the long-range ordering parameter and the development of ordering maps by using geometrical phase algorithms indicate a direct connection between the solubility of Bi and the amount of ordering. The occurrence of both phase separation and atomic ordering has a significant effect on the optical properties of these layers. PACS: 78.55.Cr III-V semiconductors; 68.55.Nq composition and phase identification; 68.55.Ln defects and impurities: doping, implantation, distribution, concentration, etc; 64.75.St phase separation and segregation in.

Phase mapping of aging process in InN nanostructures: oxygen incorporation and the role of the zinc blende phase

Uncapped InN nanostructures undergo a deleterious natural aging process at ambient conditions by oxygen incorporation. The phases involved in this process and their localization is mapped by transmission electron microscopy (TEM)-related techniques. The parent wurtzite InN (InN-w) phase disappears from the surface and gradually forms a highly textured cubic layer that completely wraps up a InN-w nucleus which still remains from the original single-crystalline quantum dots. The good reticular relationships between the different crystals generate low misfit strains and explain the apparent easiness for phase transformations at room temperature and pressure conditions, but also disable the classical methods to identify phases and grains from TEM images. The application of the geometrical phase algorithm in order to form numerical moiré mappings and RGB multilayered image reconstructions allows us to discern among the different phases and grains formed inside these nanostructures. Samples aged for shorter times reveal the presence of metastable InN:O zinc blende (zb) volumes, which act as the intermediate phase between the initial InN-w and the most stable cubic In(2)O(3) end phase. These cubic phases are highly twinned with a proportion of 50:50 between both orientations. We suggest that the existence of the intermediate InN:O-zb phase should be seriously considered to understand the reason for the widely scattered reported fundamental properties of thought to be InN-w, as its bandgap or superconductivity.