Thermosensitive aggregation under conditions of repeated heating–cooling cycles

In situ investigation of aggregate sizes formed using thermo-responsive polymers: Effect of temperature and shear

Temperature-responsive flocculants, such as poly(N-isopropylacrylamide) (PNIPAM), induce reversible particle aggregation upon heating above a lower critical solution temperature (LCST). The aim of this work is to investigate the aggregation of ground iron ore using PNIPAM and conventional polyacrylamide (PAM) flocculants in a continuously-sheared suspension, through in situ chord length measurements using Focused Beam Reflectance Measurement techniques and real-time imaging of the particle aggregates. In the presence of uncharged PNIPAM, particle aggregation occurs only upon heating to the LCST, and the aggregates continue to grow with further heating. Subsequent cooling re-disperses the aggregates, and repeated heating causes reformation. Unlike uncharged PNIPAM, anionic PNIPAM produces aggregates at temperatures below the LCST due to the polymer chains binding to two different particles via attractive interactions between the acrylic acid groups and the hematite surfaces, and can be added at temperatures above the LCST due to the formation of charge-stabilised micelles. Under continuous shear, the flocculant most able to resist aggregate size reduction was anionic PAM, followed by PAM, anionic PNIPAM, PNIPAM (6MDa), and PNIPAM (122kDa). Reversible aggregate breakage was found with all samples, except with PNIPAM (6MDa) after being subjected to shear rates above 550s^-1. Furthermore, heating of the PNIPAM-dosed suspensions at shear rates below 200s^-1 produced larger and more breakage-resistant aggregates.

Thermoresponsive Gels

Thermoresponsive gelling materials constructed from natural and synthetic polymers can be used to provide triggered action and therefore customised products such as drug delivery and regenerative medicine types as well as for other industries. Some materials give Arrhenius-type viscosity changes based on coil to globule transitions. Others produce more counterintuitive responses to temperature change because of agglomeration induced by enthalpic or entropic drivers. Extensive covalent crosslinking superimposes complexity of response and the upper and lower critical solution temperatures can translate to critical volume temperatures for these swellable but insoluble gels. Their structure and volume response confer advantages for actuation though they lack robustness. Dynamic covalent bonding has created an intermediate category where shape moulding and self-healing variants are useful for several platforms. Developing synthesis methodology-for example, Reversible Addition Fragmentation chain Transfer (RAFT) and Atomic Transfer Radical Polymerisation (ATRP)-provides an almost infinite range of materials that can be used for many of these gelling systems. For those that self-assemble into micelle systems that can gel, the upper and lower critical solution temperatures (UCST and LCST) are analogous to those for simpler dispersible polymers. However, the tuned hydrophobic-hydrophilic balance plus the introduction of additional pH-sensitivity and, for instance, thermochromic response, open the potential for coupled mechanisms to create complex drug targeting effects at the cellular level.