Effect of synthesis conditions on the properties of an ionic liquid in the 1-butyl-3-methylimidazolium acetate - Na-bentonite ionogel. Steric stabilization and confinement

Pure Chitosan-Based Fibers Manufactured by a Wet Spinning Lab-Scale Process Using Ionic Liquids

Ionic liquids offer alternative methods for the sustainable processing of natural biopolymers like chitosan. The ionic liquid 1-butyl-3-methylimidazolium acetate (BmimOAc) was successfully used for manufacturing of pure chitosan-based monofilaments by a wet spinning process at lab-scale. Commercial chitosan with 90% deacetylation degree was used for the preparation of spinning dopes with solids content of 4–8 wt.%. Rheology tests were carried out for the characterization of the viscometric properties. BmimOAc was used as a solvent and deionized water as coagulation and washing medium. Optical (scanning electron microscope (SEM), light microscope) and textile physical tests were used for the evaluation of the morphological and mechanical characteristics. The manufactured chitosan monofilaments a homogeneous structure with a diameter of ~150 μm and ~30 tex yarn count. The mechanical tests show tensile strengths of 8 cN/tex at Young’s modulus up to 4.5 GPa. This work represents a principal study for the manufacturing of pure chitosan fibers from ionic liquids and provides basic knowledge for the development of a wet spinning process.

Enhancing the Thermal Stability of Ionogels: Synthesis and Properties of Triple Ionic Liquid/Halloysite/MCC Ionogels

In this study, an ionic liquid (IL), 1-butyl-3-methylimidazolium acetate, was used to prepare ionogels with microcrystalline cellulose (MCC) and halloysite (Hal). SEM, XRD, TG, DSC, FTIR spectroscopy, conductometry and mechanical tests were used to study the morphology, structure, thermal behaviour and electrophysical and mechanical characteristics of synthesised ionogels. XRD analysis showed a slight decrease in the interlayer space of halloysite in ionogels containing MCC, which may have been associated with the removal of residual water molecules resulting from hydrophilic IL anions and polymer macromolecules. A change in conductivity and glass-transition temperature of the ionic liquid was revealed due to intercalation into halloysite (a confinement effect) and modification with cellulose. For triple IL/Hal/MCC ionogels, the characteristic thermal degradation temperatures were higher than the corresponding values for IL/Hal composites. This indicates that the synthesised IL/Hal/MCC ionogels are characterised by a greater thermal stability than those of IL/Hal systems.