Thermal decomposition and reconstruction of CaFe-layered double hydroxide studied by X-ray diffractometry and 57Fe Mössbauer spectroscopy

On the Reconstruction Peculiarities of Sol–Gel Derived Mg2−xMx/Al1 (M = Ca, Sr, Ba) Layered Double Hydroxides

In this study, the reconstruction peculiarities of sol–gel derived Mg2−xMx/Al1 (M = Ca, Sr, Ba) layered double hydroxides were investigated. The mixed metal oxides (MMO) were synthesized by two different routes. Firstly, the MMO were obtained directly by heating Mg(M)–Al–O precursor gels at 650 °C, 800 °C, and 950 °C. These MMO were reconstructed to the Mg2−xMx/Al1 (M = Ca, Sr, Ba) layered double hydroxides (LDHs) in water at 50 °C for 6 h (pH 10). Secondly, in this study, the MMO were also obtained by heating reconstructed LDHs at the same temperatures. The synthesized materials were characterized using X-ray powder diffraction (XRD) analysis and scanning electron microscopy (SEM). Nitrogen adsorption by the Brunauer, Emmett, and Teller (BET) and Barrett, Joyner, and Halenda (BJH) methods were used to determine the surface area and pore diameter of differently synthesized alkaline earth metal substituted MMO compounds. It was demonstrated for the first time that the microstructure of reconstructed MMO from sol–gel derived LDHs showed a “memory effect”.

Effects of ultrasonic irradiation on the synthesis, crystallization, thermal and dissolution behaviour of chloride-intercalated, co-precipitated CaFe-layered double hydroxide

The output power (30-150 W) and the periodicity (20-100%) of ultrasound emission were varied in a wide range to regulate and improve the crystallization process in the commonly used co-precipitation technique of chloride-intercalated CaFe-layered double hydroxides. The influence of ultrasound irradiation on the as-prepared materials was studied by X-ray diffractometry, dynamic light scattering, UV-Vis-NIR diffuse reflectance spectroscopy, specific surface area measurement, pore size analysis, ion-selective electrode potentiometric investigations and thermogravimetry. Additionally, structural alterations due to heat treatment at various temperatures were followed in detail by Fourier-transform infrared and X-ray absorption spectroscopies as well as scanning electron microscopy. The ultrasonic treatment was capable of controlling the sizes of primarily formed (from 19 nm to 30 nm) as well as the aggregated (secondary) particles (between 450 nm and 700 nm), and thus modifying their textural parameters and enhancing the incorporation of chloride anions into the interlamellar space. For the first time, the optical energy gap of CaFe-LDH was reported here depending on the nature of applied stirring (4.18-4.34 eV). The heat-treatment investigations revealed that the layered structure was stabile until 200 °C, even at the atomic level.

Ultrasonically-enhanced preparation, characterization of CaFe-layered double hydroxides with various interlayer halide, azide and oxo anions (CO32-, NO3-, ClO4-)

An ultrasonically-enhanced mechanochemical method was developed to synthesize CaFe-layered double hydroxides (LDHs) with various interlayer anions (CO₃^2-, NO₃^-, ClO₄^-, N₃^-, F^-, Cl^-, Br^- and I^-). The duration of pre-milling and ultrasonic irradiation and the variation of synthesis temperature in the wet chemical step were investigated to obtain the optimal parameters of preparation. The main method to characterize the products was X-ray diffractometry, but infrared and synchrotron-based X-ray absorption spectroscopies as well as thermogravimetric measurements were also used to learn about fine structural details. The synthesis method afforded successful intercalation of the anions, among others the azide anion, a rarely used counter ion providing a system, which enables safe handling the otherwise highly reactive anion. The X-ray absorption spectroscopic measurements revealed that the quality of the interlayered anions could modulate the spatial arrangement of the calcium ions around the iron(III) ions, but only in the second coordination sphere.