An FTIR and ESR study of iron doped calcium borophosphate glass-ceramics

Development of Iron-Silicate Composites by Waste Glass and Iron or Steel Powders

There is growing interest in the opportunities regarding construction and demolition wastes, such as glass and metal powders, for developing a circular economy and their transformation into new materials. This management and recycling of construction and demolition waste offers environmental benefits and conservation of natural resources. In this paper, new magnetic composite materials were prepared by wet chemical synthesis methods using crushed glasses and iron and steel waste powders as raw materials. The prepared iron-silicate composites were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis, infrared (IR), ultraviolet-visible, and electron paramagnetic resonance (EPR) spectroscopy, and magnetic measurements. The XRD data confirm the formation of varied crystalline phases of the iron ions. The presence of the Fe3O4 crystalline phase was detected in the composites containing the iron waste powders. The inspection of the SEM micrographs revealed slightly better homogeneity for the composite material containing larger amounts of iron waste and heterogeneous morphology with cracks and random crystallinity for the composite doped with steel waste. By doping with different contents of iron or steel waste powder, structural modifications in the silicate network and the formation of new bands in the IR spectra were evidenced. The UV-Vis spectra were characterized by the absorption peaks for both the tetrahedral and octahedral geometries of the Fe3+ ions and the octahedral coordination of the Fe2+ ions with oxygen anions. The EPR data show resonance lines with g ~2, 4.3, and 6.4, corresponding to the Fe3+ ions. Using hysteresis curves, the superparamagnetic properties of the iron-silicate composites were evidenced.

Preparation, characterization, and in vitro release kinetics of doxorubicin-loaded magnetosomes

The doxorubicin (DOX) was successfully coupled to the magnetosomes from Acidithiobacillus ferrooxidans (At. ferrooxidans) by genipin bridging. The parameters (magnetosome concentration, DOX concentration, genipin concentration-, and cross-link time) expected for temperature significantly influenced the coupling rate. Bacterial magnetosome-doxorubicin complexes (BMDCs) were characterized by transmission electron microscope (TEM), particle size analyzer and Fourier transform infrared spectroscopy. Results indicated that BMDCs exhibited a mean particle size of 83.98 mm and displayed a negative charge. The chemical reaction occurring between CO and NH group and the physical adsorption predominated by electrostatic interaction were found to involve in coupling. BMDCs can release 40% of DOX in simulated gastrointestinal conditions within 38 h. Kinetic models including Higuchi, Korsmeyer-Peppas, Zero order, First order, Hixon-Crowell, Baker-Lonsdale, and Weibull and Gompertz were utilized to explore the release mechanism of DOX from BMDCs. All models were found to fit well (r² ≥ 0.8144) with the release data and the Gompertz was the best fit model (r² = 0.9742), implying that the complex mechanisms involving Fickian and Gompertz diffusion contributed to the release. These findings suggested that magnetosomes from At. ferrooxidans have great potential applications in biomedical and clinical fields as the carrier of target drug delivery systems in the future.

Degradation of phenol by a heterogeneous photo-Fenton process using Fe/Cu/Al catalysts

Cu²⁺ and Fe³⁺ can react with H₂O₂, producing Cu⁺, Fe²⁺, and ˙OH. Then ˙OH can react with phenol directly. The degradation of phenol leads to the formation of the mixed byproducts, such as catechol, benzoquinone, resorcinol and hydroquinone.