Magnetic and photophysical properties of new TbIII –based two-dimensional hydrogen-bonded polymer

Intensity and lifetime ratiometric luminescent thermometer based on a Tb(III) coordination polymer

A three-dimensional terbium(III) coordination polymer of formula [Tb(bttb)0.5(2,5-pzdc)0.5]n (1) [H4bttb = 1,2,4,5-tetrakis(4'-carboxyphenyl)benzene and H2-2,5-pzdc = 2,5-pyrazinedicarboxylic acid] was obtained under hydrothermal conditions. The bttb4- tetraanion in 1 adopts the bridging and chelating-bridging pseudo-oxo coordination modes while the 2,5-pzdc2- dianion exhibits a rather unusual bis-bidentate bridging pseudo-oxo coordination mode, both ligands being responsible for the stiffness of the resulting 3D structure. Solid-state photoluminescent measurements illustrate that 1 exhibits remarkable green luminescence emission, the most intense band occurring in the region of 550 nm (5D4 → 7F5) with lifetimes at the millisecond scale. Thermometric performances of 1 reveal a maximum relative sensitivity (Sm) of 0.76% K-1 at 295 K (δT = 0.05 K), constituting a TbIII ratiometric solid luminescent thermometer over the physiological temperature range. Variable-temperature static (dc) magnetic susceptibility measurements for 1 in the temperature range 2.0-300 K show the expected behavior for the depopulation of the splitted mJ levels of the 7F7 ground state of the magnetically anisotropic terbium(III) ion plus a weak antiferromagnetic interaction through the carboxylate bridges. No significant out-of-phase magnetic susceptibility signals were observed for 1 in the temperature range 2.0-10.0 K, either in the absence or presence of a static dc magnetic field.

Eu@PMMA and Sm@PMMA nanofibers prepared by electrospinning: structure, morphology, luminescence and magnetic properties

Eu³⁺ and Sm³⁺ coordination polymers and a series of Eu@PMMA and Sm@PMMA nanofibers were prepared. Color tunability was achieved with the luminescence changing from reddish orange in the bulk state to near-white light in the nanofiber stage.

Cu(ii)/Ni(ii)–organic frameworks constructed from the homometallic clusters by 5-(2-carboxyphenoxy)isophthalic acid and N-ligand: synthesis, structures and visible light-driven photocatalytic properties

Four new complexes, namely, Cu₂(O-cpia)(btb)_0.5·(OH) (1), Cu₃(O-cpia)₂(bpy)₂ (2), [Ni₂(O-cpia)(phen)·(OH)·H₂O]·2H₂O (3) and [Ni₃(O-cpia)₂(bpy)₃·2H₂O]·2H₂O (4) (O-cpia = 5-(2-carboxyphenoxy)isophthalic acid, btb = 1,4-bis(1,2,4-triazol-1-yl)butane, bpy = 4,4′-bipyridine) were successfully isolated under hydrothermal conditions. The four complexes exhibit different architectures constructed from different homometallic clusters varying from mononuclear, binuclear to tetranuclear metal(ii) polyhedra as Second Building Blocks (SBUs). 1 features a 3D framework constructed from the tetranuclear clusters [Cu₄(μ₃-OH)₂] as SBUs, linked with Cu(1)O₄N and Cu(2)O₅ polyhedra by O-cpia/btb mixed linkers. 2 also exhibits a 3D structure based on trinuclear clusters [Cu₃(COO)₄] SBUs, bridged with Cu(1)O₃N₂ and Cu(2)O₄ polyhedra via O-cpia/bpy mixed ligands. 3 shows a 2D network consisting of tetranuclear clusters [Ni₄(μ₃-OH)₂] SBUs, which are bridged with Ni(1)O₄N₂ and Ni(2)O₆ through O-cpia ligands. It is worth noting that 4, with a 3D structure, is generated from the binuclear clusters [Ni₂(COO)₄] (Ni(1)O₄N) and mononuclear metal Ni(2) cores (Ni(2)O₄N₂) as SBUs, and bridged by O-cpia/bpy mixed ligands. Meanwhile, the degradation of dyes (RhB) by the complexes under visible light irradiation was studied. 1–4 are semiconducting in nature, with E_g of 1.30 eV (1), 1.78 eV (2), 2.85 eV (3) and 2.14 eV (4). Cu(ii) complexes 1 and 2 are highly efficient photocatalysts for the degradation of RhB under visible light irradiation.

Four Cu(ii)/Ni(ii)-metal–organic frameworks were constructed from different homometallic clusters by O-cpia/N-ligands. Cu(ii)-complexes show highly efficient photocatalysts for the degradation of RhB under visible light irradiation.