Rauber BF, De Carli JP, Dallepiane FG, Dogenski LC, Goedel F, Cecchin D, Palhano HS, Corazza PH, Collares KF, Souza MA, Farina AP. Aspects of glass and hybridization protocols for bonding of fiber posts to root dentine. Eur J Oral Sci 2024; 132:e13002. [PMID: 38938069 DOI: 10.1111/eos.13002] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/12/2024] [Revised: 06/03/2024] [Accepted: 06/06/2024] [Indexed: 06/29/2024]
Abstract
This study evaluated bond strength of glass fiber posts to root dentin using push-out (PO) and diametral compression (DC), testing glycolic acid as a conditioner and varying dentin moisture. An additional aim was to test whether DC can be an alternative test to PO for bond strength assessment. Eighty bovine teeth were divided into eight groups (n = 10) defined by the use of either 37% glycolic acid or 37% phosphoric acid (PA) on moist or wet dentin before bonding with either Adapter SingleBond/RelyX ARC or One Step Plus/Duo-Link Bisco. Each tooth provided discs with an internal diameter of 2 mm, external diameter of 5 mm, and height of 2 mm, which underwent PO and DC. Finite element analysis (FEA) was carried out on 3D models. When analyzing PO results through linear regression, the highest values of bond strength were observed using glycolic acid on wet dentin in the cervical and middle thirds of the teeth. Analyzing DC results, the only statistical influence on values was the dental thirds. The scatterplot of the DC results and the PO bond strength values indicated no relationship between the results of the two tests (r = 0.03; p = 0.64). PO test detected more sensitive changes in bond strength values than DC.
Collapse
Affiliation(s)
| | | | | | | | - Fábio Goedel
- School of Engineering, University of Passo Fundo, Passo Fundo, RS, Brazil
| | - Doglas Cecchin
- School of Dentistry, University of Passo Fundo, Passo Fundo, RS, Brazil
| | | | | | | | | | - Ana Paula Farina
- School of Dentistry, University of Passo Fundo, Passo Fundo, RS, Brazil
| |
Collapse
|
2
|
Carreon AH, Funkenbusch PD. Nanoscale properties and deformation of human enamel and dentin. J Mech Behav Biomed Mater 2019; 97:74-84. [DOI: 10.1016/j.jmbbm.2019.05.009] [Citation(s) in RCA: 4] [Impact Index Per Article: 0.8] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/01/2019] [Revised: 03/29/2019] [Accepted: 05/03/2019] [Indexed: 10/26/2022]
|
3
|
Zaytsev D. Mechanical properties of human enamel under compression: On the feature of calculations. MATERIALS SCIENCE & ENGINEERING. C, MATERIALS FOR BIOLOGICAL APPLICATIONS 2016; 62:518-23. [PMID: 26952454 DOI: 10.1016/j.msec.2016.02.016] [Citation(s) in RCA: 4] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 04/20/2015] [Revised: 01/20/2016] [Accepted: 02/03/2016] [Indexed: 11/24/2022]
Abstract
The paper is aimed at determination of the causes of shape effect in human tooth enamel under compression and correction of the relevant mechanical characteristics. For this purpose, six groups of samples with different ratios of the compression surface diagonal to the sample height, which consisted of 10 cuboid samples in each, were prepared from the backside of human enamel. The lateral deformation of a sample was calculated at the maximum compressive stress for correction of the mechanical characteristics. It is shown that the ratio between the lateral and axial deformations decreases with an increase in the ratio of the compression surface diagonal to the sample height. This is caused by the friction between the compression plates and the working surfaces of the enamel sample when the lateral deformation is suppressed. In addition, the slope of enamel sample by about 15° occurred during compression due to the inclination of rigid and low deformable enamel rods. The corrections of the elastic modulus and the compression strength taking into account the lateral deformation and the sample slope are carried out. The mechanical properties of enamel samples with the 2.1 aspect ratio are closer to the intrinsic properties of human enamel samples. The elastic modulus and the compression strength of human enamel under compression are 5.64 GPa and 363 MPa, respectively. The lateral deformation (~10%) may be considered as the critical parameter that indicates the strength of human enamel.
Collapse
|
4
|
Correction of some mechanical characteristics of human dentin under compression considering the shape effect. MATERIALS SCIENCE & ENGINEERING. C, MATERIALS FOR BIOLOGICAL APPLICATIONS 2015; 49:101-105. [PMID: 25686932 DOI: 10.1016/j.msec.2014.12.080] [Citation(s) in RCA: 8] [Impact Index Per Article: 0.9] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 10/22/2014] [Revised: 11/29/2014] [Accepted: 12/07/2014] [Indexed: 11/22/2022]
Abstract
The paper is aimed to determine the true compression strength and Poisson's ratio of human dentin. The origin of the shape effect in dentin under compression is discussed, too. It was shown that the shape effect is mainly caused by the friction between the surface of the sample and the compression plates. Ratio d/h=4 is the optimal proportion between the diagonal of compression surface and the height of dentin sample for compression testing. Inhomogeneous deformation takes place in the sample with a low aspect ratio whereas lateral deformation is suppressed in the sample with a high aspect ratio. There is significant difference between the conventional compression strength and the true compression strength. True compression strength of human dentin is 432±16MPa, the Young's modulus is 4.04±0.12GPa and Poisson's ratio of human dentin is 0.14±0.04.