Nanostructured titanium surfaces fabricated by hydrothermal method: Influence of alkali conditions on the osteogenic performance of implants

Hyperbranched Poly-l-Lysine Modified Titanium Surface With Enhanced Osseointegration, Bacteriostasis, and Anti-Inflammatory Properties for Implant Application: An Experimental In Vivo Study

OBJECTIVES

This study aimed to explore multiple effects of hyperbranched poly-l-lysine (HBPL) titanium (Ti) surfaces on osseointegration, bacteriostasis, and anti-inflammation across three different animal models.

METHODS

Ti surfaces were covalently modified with HBPL, with uncoated surfaces as controls. Characterization included scanning electron microscopy (SEM) and surface chemistry and elemental analysis (EDX). Ti and Ti-HBPL implants were placed in conventional canine edentulous sites, post-operative infection canine edentulous sites, and diabetic rat tibias. Implants from canine edentulous models were analyzed using micro-CT and histomorphometry to assess osseointegration at 8 weeks. Post-operative infection beagles were used to evaluate antibacterial efficacy through clinical parameters and bacterial cultures at 1 week. In diabetic rats, micro-CT and histomorphometry were performed at 8 weeks.

RESULTS

HBPL was uniformly grafted on Ti-HBPL surfaces. Ti-HBPL surfaces showed higher bone volume/total volume (BV/TV, p < 0.001), bone-implant contact (BIC%, p < 0.001), and trabecular number (Tb.N, p < 0.01) in beagles. Besides, it displayed higher BIC% (p < 0.001) and bone area fraction occupancy (BAFO%, p < 0.01) in hard tissue sections. In an infected model, Ti-HBPL surfaces exhibited lower bleeding on probing (BOP, p < 0.001), and plaque index (DI, p < 0.01), with reduced bacterial colony formation (p < 0.001) compared to the control group. In diabetic rats, Ti-HBPL surfaces showed an increase in BV/TV (p < 0.01) and Tb.N (p < 0.001), downregulated TNF-α and IL-1β (p < 0.01), and upregulated IL-10 (p < 0.01) and osteocalcin (OCN) expression (p < 0.01).

CONCLUSIONS

HBPL-Ti surfaces demonstrated enhanced osseointegration, bacteriostasis, and anti-inflammatory effects in vivo.

Optimizing alkaline hydrothermal treatment for biomimetic smart metallic orthopedic and dental implants

Orthopedic and dental implant failure continues to be a significant concern due to localized bacterial infections. Previous studies have attempted to improve implant surfaces by modifying their texture and roughness or coating them with antibiotics to enhance antibacterial properties for implant longevity. However, these approaches have demonstrated limited effectiveness. In this study, we attempted to engineer the titanium (Ti) alloy surface biomimetically at the nanometer scale, inspired by the cicada wing nanostructure using alkaline hydrothermal treatment (AHT) to simultaneously confer antibacterial properties and support the adhesion and proliferation of mammalian cells. The two modified Ti surfaces were developed using a 4 h and 8 h AHT process in 1 N NaOH at 230 °C, followed by a 2-hour post-calcination at 600 °C. We found that the control plates showed a relatively smooth surface, while the treatment groups (4 h & 8 h AHT) displayed nanoflower structures containing randomly distributed nano-spikes. The results demonstrated a statistically significant decrease in the contact angle of the treatment groups, which increased wettability characteristics. The 8 h AHT group exhibited the highest wettability and significant increase in roughness 0.72 ± 0.08 µm (P < 0.05), leading to more osteoblast cell attachment, reduced cytotoxicity effects, and enhanced relative survivability. The alkaline phosphatase activity measured in all different groups indicated that the 8 h AHT group exhibited the highest activity, suggesting that the surface roughness and wettability of the treatment groups may have facilitated cell adhesion and attachment and subsequently increased secretion of extracellular matrix. Overall, the findings indicate that biomimetic nanotextured surfaces created by the AHT process have the potential to be translated as implant coatings to enhance bone regeneration and implant integration.

Surface Topography Steer Soft Tissue Response and Antibacterial Function at the Transmucosal Region of Titanium Implant

Metallic dental implants have been extensively used in clinical practice due to their superior mechanical properties, biocompatibility, and aesthetic outcomes. However, their integration with the surrounding soft tissue at the mucosal region remains challenging and can cause implant failure due to the peri-implant immune microenvironment. The soft tissue integration of dental implants can be ameliorated through different surface modifications. This review discussed and summarized the current knowledge of topography-mediated immune response and topography-mediated antibacterial activity in Ti dental implants which enhance soft tissue integration and their clinical performance. For example, nanopillar-like topographies such as spinules, and spikes showed effective antibacterial activity in human salivary biofilm which was due to the lethal stretching of bacterial membrane between the nanopillars. The key findings of this review were (I) cross-talk between surface nanotopography and soft tissue integration in which the surface nanotopography can guide the perpendicular orientation of collagen fibers into connective tissue which leads to the stability of soft tissue, (II) nanotubular array could shift the macrophage phenotype from pro-inflammatory (M1) to anti-inflammatory (M2) and manipulate the balance of osteogenesis/osteoclasia, and (III) surface nanotopography can provide specific sites for the loading of antibacterial agents and metallic nanoparticles of clinical interest functionalizing the implant surface. Silver-containing nanotubular topography significantly decreased the formation of fibrous encapsulation in per-implant soft tissue and showed synergistic antifungal and antibacterial properties. Although the Ti implants with surface nanotopography have shown promising in targeting soft tissue healing in vitro and in vivo through their immunomodulatory and antibacterial properties, however, long-term in vivo studies need to be conducted particularly in osteoporotic, and diabetic patients to ensure their desired performance with immunomodulatory and antibacterial properties. The optimization of product development is another challenging issue for its clinical translation, as the dental implant with surface nanotopography must endure implantation and operation inside the dental microenvironment. Finally, the sustainable release of metallic nanoparticles could be challenging to reduce cytotoxicity while augmenting the therapeutic effects.

An ascorbic acid-decorated nanostructured surface on titanium inhibits breast cancer development and promotes osteogenesis

The chest wall is the most frequent metastatic site of breast cancer (BC) and the metastasis usually occurs in a solitary setting. Chest wall resection is a way to treat solitary BC metastasis, but intraoperative bone defects and local tumor recurrence still affect the life quality of patients. Titanium-based prostheses are widely used for chest wall repair and reconstruction, but their inherent bio-inertness makes their clinical performance unfavorable. Nanostructured surfaces can give titanium substrates the ability to excellently modulate a variety of cellular functions. Ascorbic acid is a potential stimulator of tumor suppression and osteogenic differentiation. An ascorbic acid-decorated nanostructured titanium surface was prepared through alkali treatment and spin-coating technique and its effects on the biological responses of BC cells and osteoblasts were assessed. The results exhibited that the nanorod structure and ascorbic acid synergistically inhibited the proliferation, spreading, and migration of BC cells. Additionally, the ascorbic acid-decorated nanostructured surface significantly promoted the proliferation and osteogenic differentiation of osteoblasts. This work may provide valuable references for the clinical application of titanium materials in chest wall reconstruction after the resection of metastatic BC.

Titanium surface interacting with blood clot enhanced migration and osteogenic differentiation of bone marrow mesenchymal stem cells

Introduction: Blood clot formation is the initial phase upon implantation, and the feature of blood clot orchestrates the following complement system activation, coagulation cascade, and bone marrow mesenchymal stromal cells (BMSCs) recruitment. This study aimed to investigate the effect of implant surface on blood-material interactions and subsequent BMSC cellular behaviors. Methods: This study was established to imitate the physiological process of implantation in vivo and in vitro. Whole blood was incubated with polished titanium (PT) surfaces and sandblasted and double acid-etching (SLA) surfaces for 10 min or 2 h, then seeded with BMSCs. The adhesion, proliferation, migration, and differentiation of cells were studied at specific time points. Titanium implants were implanted into the tibia in vivo and were screwed out after implantation. The activation of the coagulation cascade, platelets, complement system, and clot networks were assessed and further quantitatively analyzed. Results: Compared with the PT surface, the SLA surface induced the earlier and stronger blood coagulation cascade and formed a more stratified clots network with fibrinogen, platelets, and CD14 positive cell. The adhesion, proliferation, and migration of BMSCs were enhanced by pre-incubated surfaces. The higher levels of the osteogenic-related genes, ALP activity, and calcium nodule formation were showed on SLA surfaces with blood incubation. Conclusion: SLA titanium surfaces play a role in influencing the formation of blood clots and coordinating surface-blood interactions and cell biological processes. These findings provide the idea of modifying the blood clots formed on the implant surface by biomaterials modification and thus has implications for the development of better osteogenic biomaterials.

Manganese supplementation of orthopedic implants: a new strategy for enhancing integrin-mediated cellular responses

Integrin-mediated osteoblast adhesion to adsorbed extracellular ligands on orthopedic implants is crucial for the subsequent osteoblast behaviors and ultimate osseointegration. Considerable research efforts have focused on the development of implant surfaces that promote the adsorption of extracellular ligands, but ignored the fact that integrin binding to ligands requires divalent cations (such as Mn²⁺). Here, three kinds of Mn-doped nanowire-structured TiO₂ coatings with 1.9, 3.9, and 8.8 wt% dopant contents (Mn1-, Mn2-, and Mn3-TiO₂) were synthesized on Ti implants to enhance integrin-mediated osteoblastic responses. The Mg-doped and undoped TiO₂ nanocoatings served as the control. Mn element was not only successfully incorporated into the TiO₂ matrix, but also formed an oxygen-deficient Mn oxide on the nanowire surface. Although the adsorbed fibronectin (Fn) amount on Mn-doped nanocoatings and its unfolded status were slightly attenuated with increasing Mn amount, the interaction between the coating extract and Fn demonstrated a Mn²⁺-induced unfolding of Fn with the exposure of the RGD motif. Compared to the Mn1-, Mn2- and Mg-doped TiO₂ nanocoatings, the Mn3-TiO₂ nanocoating significantly upregulated the expression of integrin α5β1 probably through increasing the ligand-binding affinity of the integrin rather than integrin binding sites in Fn. Consistent with the activation trend of integrin α5β1, the Mn3-TiO₂ nanocoating enhanced cell adhesion with the long stretched structure of actin fibers and extensive formation of vinculin focal adhesion spots and upregulated the levels of alkaline phosphatase and osteocalcin activities. Therefore, Mn supplementation of orthopedic implants may be a promising way to improve osteogenesis at the implant surface.

Titanium Surface-Grafted Zwitterionic Polymers with an Anti-Polyelectrolyte Effect Enhances Osteogenesis

Zwitterionic polymers have attracted considerable attention because of their anti-adsorption and unique anti-polyelectrolyte effects and was widely used in surface modification. In this study, zwitterionic copolymers (poly (sulfobetaine methacrylate-co-butyl acrylate) (pSB) coating on the surface of a hydroxylated titanium sheet using surface-initiated atom transfer radical polymerization (SI-ATRP) was successfully constructed. X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR) and Water contact angle (WCA) analysis proved the successful preparation of the coating. The swelling effect caused by the anti-polyelectrolyte effect was reflected in the simulation experiment in vitro, and this coating can promote the proliferation and osteogenesis of MC3T3-E1. Therefore, this study provides a new strategy for designing multifunctional biomaterials for implant surface modifications.

Novel Strategy for Surface Modification of Titanium Implants towards the Improvement of Osseointegration Property and Antibiotic Local Delivery

The topography and chemical composition modification of titanium (Ti) implants play a decisive role in improving biocompatibility and bioactivity, accelerating osseointegration, and, thus, determining clinical success. In spite of the development of surface modification strategies, bacterial contamination is a common cause of failure. The use of systemic antibiotic therapy does not guarantee action at the contaminated site. In this work, we proposed a surface treatment for Ti implants that aim to improve their osseointegration and reduce bacterial colonization in surgery sites due to the local release of antibiotic. The Ti discs were hydrothermally treated with 3M NaOH solution to form a nanostructured layer of titanate on the Ti surface. Metronidazole was impregnated on these nanostructured surfaces to enable its local release. The samples were coated with poly(vinyl alcohol)-PVA films with different thickness to evaluate a possible control of drug release. Gamma irradiation was used to crosslink the polymer chains to achieve hydrogel layer formation and to sterilize the samples. The samples were characterized by XRD, SEM, FTIR, contact angle measurements, "in vitro" bioactivity, and drug release analysis. The alkaline hydrothermal treatment successfully produced intertwined, web-like nanostructures on the Ti surface, providing wettability and bioactivity to the Ti samples (Ti + TTNT samples). Metronidazole was successfully loaded and released from the Ti + TTNT samples coated or not with PVA. Although the polymeric film acted as a physical barrier to drug delivery, all groups reached the minimum inhibitory concentration for anaerobic bacteria. Thus, the surface modification method presented is a potential approach to improve the osseointegration of Ti implants and to associate local drug delivery with dental implants, preventing early infections and bone failure.

Preventing Peri-implantitis: The Quest for a Next Generation of Titanium Dental Implants

Titanium and its alloys are frequently the biomaterial of choice for dental implant applications. Although titanium dental implants have been utilized for decades, there are yet unresolved issues pertaining to implant failure. Dental implant failure can arise either through wear and fatigue of the implant itself or peri-implant disease and subsequent host inflammation. In the present report, we provide a comprehensive review of titanium and its alloys in the context of dental implant material, and how surface properties influence the rate of bacterial colonization and peri-implant disease. Details are provided on the various periodontal pathogens implicated in peri-implantitis, their adhesive behavior, and how this relationship is governed by the implant surface properties. Issues of osteointegration and immunomodulation are also discussed in relation to titanium dental implants. Some impediments in the commercial translation for a novel titanium-based dental implant from "bench to bedside" are discussed. Numerous in vitro studies on novel materials, processing techniques, and methodologies performed on dental implants have been highlighted. The present report review that comprehensively compares the in vitro, in vivo, and clinical studies of titanium and its alloys for dental implants.

Biocompatible silane adhesion layer on titanium implants improves angiogenesis and osteogenesis

Silane adhesion layer strategy has been widely used to covalently graft biomolecules to the titanium implant surface, thereby conferring the implant bioactivity to ameliorate osseointegration. However, few researchers pay attention to the effects of silanization parameters on biocompatibility and biofunctionality of the silane adhesion layers. Accordingly, the present study successfully fabricated the silane adhesion layers with different thickness, intactness, and surface morphologies by introducing 3-aminopropyltriethoxysilane on the alkali-treated titanium surface in time-varied processing of silanization. The regulatory effects of the silane adhesion layers on angiogenesis and osteogenesis were assessed in vitro. Results showed that the prolonged silanization processing time increased the thickness and intactness of the silane adhesion layer and significantly improved its biocompatibility. Notably, the silane adhesion layer prepared after 12 h of silanization exhibited a brain-like surface morphology and benefited the adhesion and proliferation of endothelial cells (ECs) and osteoblasts (OBs). Moreover, the layer promoted angiogenesis via stimulating vascular endothelial growth factor (VEGF) secretion and nitric oxide (NO) production of ECs. Simultaneously, it improved osteogenesis by enhancing alkaline phosphatase (ALP) activity, collagen secretion, and extracellular matrix mineralization of OBs. This work systematically investigated the biocompatibility and biofunctionality of the modified silane adhesion layers, thus providing valuable references for their application in covalently grafting biomolecules on the titanium implant surface.

Construction of a Hierarchical Micro-/Submicro-/Nanostructured 3D-Printed Ti6Al4V Surface Feature to Promote Osteogenesis: Involvement of Sema7A through the ITGB1/FAK/ERK Signaling Pathway

Constructing hierarchical hybrid structures is considered a facile method to improve the osseointegration of implants. Herein, a hierarchical micro-/submicro-/nanostructured surface feature of Ti6Al4V implants (3DAT group) was successfully constructed by combining the inherently formed three-dimensional (3D)-printed microscale topography, acid-etched sub-micropits, and anodized nanotubes. Compared with the classical SLA surface, the microscale topography and sub-micropits increased the three-dimensional space for the cell growth and mechanical stability of implants, while the modification of nanotubes dramatically improved the surface hydrophilicity, protein adsorption, and biomineralization. Most importantly, the 3DAT surface feature possessed excellent osteogenic performance in vitro and in vivo, with the involvement of semaphorin 7A (Sema7A) as revealed by RNA-seq through the ITGB1/FAK/ERK signaling pathway. The present study suggested that the hierarchically structured surface design strategy could accelerate the osseointegration rate of 3D-printed Ti6Al4V implants, promising personalized reconstruction of bone defects.

Electrical stimulation: Effective cue to direct osteogenic differentiation of mesenchymal stem cells?

Mesenchymal stem cells (MSCs) play a major role in bone tissue engineering (BTE) thanks to their capacity for osteogenic differentiation and being easily available. In vivo, MSCs are exposed to an electroactive microenvironment in the bone niche, which has piezoelectric properties. The correlation between the electrically active milieu and bone's ability to adapt to mechanical stress and self-regenerate has led to using electrical stimulation (ES) as physical cue to direct MSCs differentiation towards the osteogenic lineage in BTE. This review summarizes the different techniques to electrically stimulate MSCs to induce their osteoblastogenesis in vitro, including general electrical stimulation and substrate mediated stimulation by means of conductive or piezoelectric cell culture supports. Several aspects are covered, including stimulation parameters, treatment times and cell culture media to summarize the best conditions for inducing MSCs osteogenic commitment by electrical stimulation, from a critical point of view. Electrical stimulation activates different signaling pathways, including bone morphogenetic protein (BMP) Smad-dependent or independent, regulated by mitogen activated protein kinases (MAPK), extracellular signal-regulated kinases (ERK) and p38. The roles of voltage gate calcium channels (VGCC) and integrins are also highlighted according to their application technique and parameters, mainly converging in the expression of RUNX2, the master regulator of the osteogenic differentiation pathway. Despite the evident lack of homogeneity in the approaches used, the ever-increasing scientific evidence confirms ES potential as an osteoinductive cue, mimicking aspects of the in vivo microenvironment and moving one step forward to the translation of this approach into clinic.

Surface Modification Techniques to Produce Micro/Nano-scale Topographies on Ti-Based Implant Surfaces for Improved Osseointegration

Titanium and titanium alloys are used as artificial bone substitutes due to the good mechanical properties and biocompatibility, and are widely applied in the treatment of bone defects in clinic. However, Pure titanium has stress shielding effect on bone, and the effect of titanium-based materials on promoting bone healing is not significant. To solve this problem, several studies have proposed that the surface of titanium-based implants can be modified to generate micro or nano structures and improve mechanical properties, which will have positive effects on bone healing. This article reviews the application and characteristics of several titanium processing methods, and explores the effects of different technologies on the surface characteristics, mechanical properties, cell behavior and osseointegration. The future research prospects in this field and the characteristics of ideal titanium-based implants are proposed.

Multifunctional Coatings of Titanium Implants Toward Promoting Osseointegration and Preventing Infection: Recent Developments

Titanium and its alloys are dominant material for orthopedic/dental implants due to their stable chemical properties and good biocompatibility. However, aseptic loosening and peri-implant infection remain problems that may lead to implant removal eventually. The ideal orthopedic implant should possess both osteogenic and antibacterial properties and do proper assistance to in situ inflammatory cells for anti-microbe and tissue repair. Recent advances in surface modification have provided various strategies to procure the harmonious relationship between implant and its microenvironment. In this review, we provide an overview of the latest strategies to endow titanium implants with bio-function and anti-infection properties. We state the methods they use to preparing these efficient surfaces and offer further insight into the interaction between these devices and the local biological environment. Finally, we discuss the unmet needs and current challenges in the development of ideal materials for bone implantation.

Superhydrophilic multifunctional nanotextured titanium dental implants: in vivo short and long-term response in a porcine model

Current clinical demand in dental implantology is for a multifunctional device with optimum mechanical properties, improved biocompatibility and bioactivity, and having differential interactions with cells and pathogenic agents. This would minimise bacterial infection, biofilm formation and modulate inflammation, leading to a fast and durable osseointegration. The present study intends to establish the multifunctional behaviour of surface modified titanium dental implants that are superhydrophilic, with unique micro-nano or nanoscale topographies, developed by a facile hydrothermal technique. Here, the short and long-term performances of these textured implants are tested in a split mouth design using a porcine model, in pre- and post-loaded states. Quantitative and qualitative analyses of the bone implant interphase are performed through μ-CT and histology. Parameters that evaluate bone mineral density, bone contact volume and bone implant contact reveal enhanced bone apposition with better long-term response for the nano and micro-nano textured surfaces, compared to the commercial microtextured implant. Concurrently, the nanoscale surface features on implants reduced bacterial attachment by nearly 90% in vivo, outperforming the commercial variant. This preclinical evaluation data thus reveal the superiority of nano/micro-nano textured designs for clinical application and substantiate their improved osseointegration and reduced bacterial adhesion, thus proposing a novel dental implant with multifunctional characteristics.

Boron-incorporated micro/nano-topographical calcium silicate coating dictates osteo/angio-genesis and inflammatory response toward enhanced osseointegration

Orthopedic implant coatings with optimal surface features to achieve favorable osteo/angio-genesis and inflammatory response would be of great importance. However, to date, few coatings are capable of fully satisfying these requirements. In this work, to take advantage of the structural complexity of micro/nano-topography and benefits of biological trace elements, two types of boron-containing nanostructures (nanoflakes and nanolamellars) were introduced onto plasma-sprayed calcium silicate (F-BCS and L-BCS) coatings via hydrothermal treatment. The C-CS coating using deionized water as hydrothermal medium served as control. Boron-incorporated CS coating stimulated osteoblastic differentiation of bone marrow-derived mesenchymal stem cells (BMSCs). Specifically, the combination of β1 integrin-vinculin-mediated cell spreading and activation of bone morphogenetic protein signaling pathway acted synergistically to cause significant upregulation of runt-related transcription factor 2 (RUNX2) protein and Runx2 gene expression in BMSCs on the F-BCS coating surface, which induced the transcription of downstream osteogenic differentiation marker genes. F-BCS coating allowed specific boron ion release, which favored angiogenesis as evidenced by the enhanced migration and tube formation of human umbilical vein endothelial cells in the coating extract. Boron-incorporated coatings significantly suppressed the expression of toll-like receptor adaptor genes in RAW264.7 macrophages and subsequently the degradation of nuclear factor-κB inhibitor α, accompanied by the inactivation of the downstream pro-inflammatory genes. In vivo experiments confirmed that F-BCS-coated Ti implant possessed enhanced osseointegration compared with L-BCS- and C-CS-coated implants. These data highlighted the synergistic effect of specific nanotopography and boron release from orthopedic implant coating on improvement of osseointegration.

Innovative surfaces and alloys for dental implants: What about biointerface-safety concerns?

OBJECTIVES

The present review article aimed to discuss the recent technologies employed for the development of dental implants, mainly regarding innovative surface treatments and alternative alloys, emphasizing the bio-tribocorrosion processes.

METHODS

An electronic search applying specific MeSH terms was carried out in PubMed and Google Scholar databases to collect data until August 2021, considering basic, pre-clinical, clinical and review studies. The relevant articles (n=111), focused on innovative surface treatments for dental implants and their potential undesirable biological effects, were selected and explored.

RESULTS

Novel texturization methodologies for dental implants clearly provided superficial and structural atomic alterations in micro- and nanoscale, promoting different mechanical-chemical interactions when applied in the clinical set. Some particulate metals released from implant surfaces, their degradation products and/or contaminants exhibited local and systemic reactions after implant installation and osseointegration, contributing to unexpected treatment drawbacks and adverse effects. Therefore, there is an urgent need for development of pre-clinical and clinical platforms for screening dental implant devices, to predict the biointerface reactions as early as possible during the development phases.

SIGNIFICANCE

Modern surface treatments and innovative alloys developed for dental implants are not completely understood regarding their integrity during long-term clinical function, especially when considering the bio-tribocorrosion process. From this review, it is possible to assume that degradation and contamination of dental surfaces might be associated within peri-implant inflammation and cumulative long-lasting systemic toxicity. The in-depth comprehension of the biointerface modifications on these novel surface treatments might preclude unnecessary expenses and postoperative complications involving osseointegration failures.

Strontium-incorporated titanium implant surfaces treated by hydrothermal treatment enhance rapid osseointegration in diabetes: A preclinical vivo experimental study

OBJECTIVES

The aim of the current study was to explore effects of strontium-incorporated titanium implant surfaces by hydrothermal treatment on osseointegration in diabetic rats.

MATERIALS AND METHODS

The surface characteristics of SLA and SLA-Sr surfaces were detected by related instruments. Thirty-six male Sprague-Dawley rats were induced into diabetes, and thirty-six rats were normal. SLA and SLA-Sr implants were, respectively, inserted into bilateral tibial metaphysis of each rat. Percentage of bone-to-implant contact (BIC%) and percentage of bone area (BA%) were analyzed at 4 and 8 weeks after implantation. Immunohistochemistry of osteoprotegerin (OPG) and Wnt5a were conducted at 1 and 4 weeks. Gene expression levels of inflammatory cytokines and related signaling molecules in peri-implant bone tissue were detected at 3 and 7 days.

RESULTS

Strontium was uniformly distributed on SLA-Sr surfaces, and it was released in an effective concentration range. SLA-Sr surfaces showed significantly higher BIC% in diabetic rats at 4 (p < .05) and 8 weeks (p < .05). Besides, it displayed higher BIC% at 4 weeks (p < .05) in normal rats. Also, SLA-Sr surfaces upregulated expression of OPG at 4 weeks (p < .05) in diabetic rats. What's more, SLA-Sr surfaces downregulated inflammation (TNF-α, IL-1β, and IL-6; p < .01) in diabetic rats at 3 days. In addition, expression of Wnt5a and ROR2 was upregulated (p < .05) at 7 days after implantation under diabetes.

CONCLUSION

It is suggested that strontium-incorporated titanium implant surfaces by hydrothermal treatment could enhance implant osseointegration as compared with SLA implant surfaces in diabetic rats.

Covalent grafting of hyperbranched poly-L-lysine on Ti-based implants achieves dual functions of antibacteria and promoted osteointegration in vivo

The dual functional implants of antibacteria and osteointegration are highly demanded in orthopedic and dentistry, especially for patients who suffer from diabetes or osteoporosis simultaneously. However, there is lack of the facile and robust method to produce clinically applicable implants with this dual function although coatings possessing single function have been extensively developed. Herein, hyperbranched poly-L-lysine (HBPL) polymers were covalently immobilized onto the alkali-heat treated titanium (Ti) substrates and implants by using 3-glycidyloxypropyltrimethoxysilane (GPTMS) as the coupling agent, which displayed excellent antibacterial activity against S. aureus and E. coli with an efficiency as high as 89.4% and 92.2% in vitro, respectively. The HBPL coating also significantly promoted the adhesion, spreading, proliferation and osteogenic differentiation of MC3T3-E1 cells in vitro. Furthermore, the results of a S. aureus infection rat model in vivo ulteriorly verified that the HBPL-modified screws had good antibacterial and anti-inflammatory abilities at an early stage of implantation and better osteointegration compared with the control Ti screws.

Nanointeraction: The profound influence of nanostructured and nano-drug delivery biomedical implant surfaces on cell behavior

Nanostructured surfaces feature promising biological properties on biomaterials attracting large interest at basic research, implant industry development, and bioengineering applications. Thou, nanoscale interactions at a molecular and cellular level are not yet completely understood and its biological and clinical implications need to be further elucidated. As follows, the aim of this comprehensive review was to evaluate nanostructured surfaces at biomedical implants focusing on surface development, nanostructuration, and nanoengineered drug delivery systems that can induce specific cell interactions in all relevant aspects of biological, reparative, anti-bacterial, anti-inflammatory and clinical processes. The methods and the physio-chemical properties involved in nanotopography performance, the main cellular characteristics involved at surface/cell interaction, and a summary of results and outlooks reported in studies applying nanostructured surfaces and nano-drug delivery systems is presented. The future prospects and commercial translation of this developing field, particularly concerning multifunctional nanostructured surfaces and its clinical implications are further discussed. At a cellular level, nanostructured biomedical implant surfaces can enhance osteogenesis by targeting osteoblasts, osteocytes, and mesenchymal cells, stimulate fibroblast/epithelial cells proliferation and adherence, inhibit bacterial cell proliferation and biofilm accumulation, and act as immune-modulating surfaces targeting macrophages and reducing pro-inflammatory cytokine expression. Moreover, several methodological options to create drug-delivery systems on metallic implant surfaces are available, however, the clinical translation is yet incomplete. The efficiency of which nanostructured/nano-delivery surfaces may target specific cell interactions and favor clinical outcomes needs to be further elucidated in pre-clinical and clinical studies, along with engineering solutions for commercial translation and approval of controlling agencies.

The optimized preparation of HA/L-TiO2/D-TiO2 composite coating on porous titanium and its effect on the behavior osteoblasts

Various surface bioactivation technology has been confirmed to improve the osteogenic ability of porous titanium (pTi) implants effectively. In this study, a three-layered composite coating, i.e. outer layer of hydroxyapatite (HA), middle layer of loose titanium dioxide (L-TiO₂) and inner layer of dense TiO₂ (D-TiO₂), was fabricated on pTi by a combined processing procedure of pickling, alkali heat (AH), anodic oxidation (AO), electrochemical deposition (ED) and hydrothermal treatment (HT). After soaking in simulated body fluid for 48 h, the surface of the AHAOEDHT-treated pTi was completely covered by a homogeneous apatite layer. Using MC3T3-E1 pro-osteoblasts as cell model, the cell culture revealed that both the pTi without surface treatment and the AHAOEDHT sample could support the attachment, growth and proliferation of the cells. Compared to the pTi sample, the AHAOEDHT one induced higher expressions of osteogenesis-related genes in the cells, including alkaline phosphatase, Type I collagen, osteopontin, osteoclast inhibitor, osteocalcin and zinc finger structure transcription factor. As thus, besides the good corrosion resistance, the HA/L-TiO₂/D-TiO₂-coated pTi had good osteogenic activity, showing good potential in practical application for bone defect repair.

In-vivo performance of plasma-sprayed CaO-MgO-SiO2-based bioactive glass-ceramic coating on Ti-6Al-4V alloy for bone regeneration

The CaO-MgO-SiO₂-based bioactive glass-ceramic coating (named M2) on Ti-6Al-4V alloy has been proven to behave well in vitro. But how to make full sense of its performances in terms of osteogenesis and osseointegration in vivo matters very much. For this, the M2-coated Ti-6Al-4V cylinders were prepared by atmospheric plasma spraying (APS) and implanted into New Zealand rabbit for 1, 2 and 3 months, respectively, by setting commercial HA-coated Ti-6Al-4V as the control. It is encouraging that, the two groups bonded with the surrounding tissues stably and newly formed bone grew towards or around the implants after 3-month implantation according to radiographic images. From the histological sections, it is obvious that, compared to the control, the M2-coated implant was more favorable for the osteogenesis and neo-vascularisation in the whole experimental process and demonstrated a better osseointegration with the host bone, indicating the former possessed better osteoconductivity, osteoinductivity and osteogenic ability. The study indicated that the M2-coated Ti-6Al-4V implant exerted a great potential to substitute the commercial HA-coated Ti-6Al-4V implant in repairing load-bearing bone defects.

Enhanced corrosion resistance of zinc-containing nanowires-modified titanium surface under exposure to oxidizing microenvironment

Titanium (Ti) and its alloys as bio-implants have excellent biocompatibilities and osteogenic properties after modification of chemical composition and topography via various methods. The corrosion resistance of these modified materials is of great importance for changing oral system, while few researches have reported this point. Recently, oxidative corrosion induced by cellular metabolites has been well concerned. In this study, we explored the corrosion behaviors of four common materials (commercially pure Ti, cp-Ti; Sandblasting and acid etching-modified Ti, Ti-SLA; nanowires-modified Ti, Ti-NW; and zinc-containing nanowires-modified Ti, Ti-NW-Zn) with excellent biocompatibilities and osteogenic capacities under the macrophages induced-oxidizing microenvironment. The results showed that the materials immersed into a high oxidizing environment were more vulnerable to corrode. Meanwhile, different surfaces also showed various corrosion susceptibilities under oxidizing condition. Samples embed with zinc element exhibited more excellent corrosion resistance compared with other three surfaces exposure to excessive H₂O₂. Besides, we found that zinc-decorated Ti surfaces inhibited the adhesion and proliferation of macrophages on its surface and induced the M2 states of macrophages to better healing and tissue reconstruction. Most importantly, zinc-decorated Ti surfaces markedly increased the expressions of antioxidant enzyme relative genes in macrophages. It improved the oxidation microenvironment around the materials and further protected their properties. In summary, our results demonstrated that Ti-NW-Zn surfaces not only provided excellent corrosion resistance properties, but also inhibited the adhesion of macrophages. These aspects were necessary for maintaining osseointegration capacity and enhancing the corrosion resistance of Ti in numerous medical applications, particularly in dentistry.