Properties and thermal neutron areal transmittance of a B4C filled thermoplastic elastomer based rubber composite

High-density polyethylene (HDPE)-incorporated boron carbide and boric acid nanoparticles as a nanoshield of photoneutrons from medical linear accelerators

PURPOSE

The current study aimed to investigate boron carbide and boric acid nanoparticles (NPs) as absorbents for thermal neutrons and high-density polyethylene (HDPE) as a substrate and neutron moderator for fast neutrons. The goal was to assess the performance of boron carbide and boric acid NPs based on HDPE as a nanoshield of photoneutrons from medical linear accelerators.

MATERIALS AND METHODS

This study was conducted in two parts of simulation and practice. The Monte Carlo (MC) simulation involved modeling and verification of the single-layer, double-layer, and combined nanoshields by selecting nanomaterials and substrates and, finally, calculating the macroscopic cross-sections. The practical part involved manufacturing nanoshields based on the simulation results and evaluating the manufactured nanocomposites via experimental measurements.

RESULTS

MC simulation results with an uncertainty of less than 1% showed that for the monolayer samples, the best result belonged to boron carbide at a concentration of 10% and a macroscopic cross-section of 0.933 cm-1. At a concentration of 20%, the highest value among the double-layer samples was 0.936 cm-1 and for the combined samples, this value was 0.928 cm-1. Boron carbide single-layer nanocomposites at a 10% concentration, as well as the bilayer nanoshield of 10% boron carbide and 20% boric acid performed well; however, the best performance belonged to the nanoshield with a macroscopic cross-section of 0.960 and the combination containing 5% boron carbide and 10% boric acid.

CONCLUSIONS

The research suggests that utilizing boron carbide and boric acid nanoshields in combination with HDPE holds promise as a viable approach to protecting from the photoneutrons. Further exploration of these nanocomposite shields and their practical applications is warranted, with the potential to yield significant advancements in radiation therapy safety and efficacy.

The Dynamic Properties at Elevated Temperature of the Thermoplastic Polystyrene Matrix Modified with Nano-Alumina Powder and Thermoplastic Elastomer

The performance improvement of advanced electronic packaging material is an important topic to meet the stringent demands of modern semiconductor devices. This paper studies the incorporation of nano-alumina powder and thermoplastic elastomer (TPE) into thermoplastic polystyrene matrix to tune the thermal and mechanical properties after injection molding process. In the sample preparation, acetone was employed as a solvent to avoid the powder escape into surrounding during the mechanical mixing in a twin-screw mixer. The pressure and shear force were able to mix the composite with good uniformity in compositions. The samples with different compositions were fabricated using injection molding. The measured results showed that adding 5 wt.% of TPE into the simple polystyrene was able to raise the melt flow index from 12.3 to 13.4 g/10 min while the thermal decomposition temperature remained nearly unchanged. Moreover, the addition of small amount of nano-alumina powder could quickly improve the mechanical property by raising its storage modulus. For example, the addition of 3 wt.% of nano-alumina powder had an increase of 7.3% in storage modulus. Over doping of nano-alumina powder in the composite, such as 10 wt.%, on the other hand, lowered the storage modulus from 2404 MPa to 2069 MPa. The experimental study demonstrated that the tuning in the polystyrene’s thermal and mechanical properties is feasible by composition modification with nano-alumina powder and TPE. The better concentration of the additives should be determined according to the specific applications.