Experimental study of bone response to hydroxyapatite coating implants: bone-implant contact and removal torque test

The minipig intraoral dental implant model: A systematic review and meta-analysis

OBJECTIVES

The objective of this report was to provide a review of the minipig intraoral dental implant model including a meta-analysis to estimate osseointegration and crestal bone remodeling.

METHODS

A systematic review including PubMed and EMBASE databases through June 2021 was conducted. Two independent examiners screened titles/abstracts and selected full-text articles. Studies evaluating titanium dental implant osseointegration in native alveolar bone were included. A quality assessment of reporting was performed. Random-effects meta-analyses and meta-regressions were produced for bone-implant contact (BIC), first BIC, and crestal bone level.

RESULTS

125 out of 249 full-text articles were reviewed, 55 original studies were included. Quality of reporting was generally low, omissions included animal characteristics, examiner masking/calibration, and sample size calculation. The typical minipig model protocol included surgical extraction of the mandibular premolars and first molar, 12±4 wks post-extraction healing, placement of three narrow regular length dental implants per jaw quadrant, submerged implant healing and 8 wks of osseointegration. Approximately 90% of studies reported undecalcified incandescent light microscopy histometrics. Overall, mean BIC was 59.88% (95%CI: 57.43-62.33). BIC increased significantly over time (p<0.001): 40.93 (95%CI: 34.95-46.90) at 2 wks, 58.37% (95%CI: 54.38-62.36) at 4 wks, and 66.33% (95%CI: 63.45-69.21) beyond 4 wks. Variability among studies was mainly explained by differences in observation interval post-extraction and post-implant placement, and implant surface. Heterogeneity was high for all studies (I2 > 90%, p<0.001).

CONCLUSIONS

The minipig intraoral dental implant model appears to effectively demonstrate osseointegration and alveolar bone remodeling similar to that observed in humans and canine models.

Early Bone Healing on Hydroxyapatite-Coated and Chemically-Modified Hydrophilic Implant Surfaces in an Ovine Model

Implant topography affects early peri-implant bone healing by changing the osteoconduction rate in the surrounding biological environment. Implant surfaces have been designed to promote faster and stronger bone formation for rapid and stable prosthesis loading. Early peri-implant bone healing has been observed with a sandblasted, acid-etched implant that was chemically modified to be hydrophilic (cmSLA). The present study investigates whether early peri-implant bone healing extends to a rough surface implant with a high crystalline hydroxyapatite surface (TSV MP-1 HA). Three implants were randomly placed in porous trabecular bone within both medial femoral condyles of 10 sheep. Early peri-implant bone stability was measured at 3- and 6-weeks healing time following implant insertion. Results indicated a similar implant stability quotient between the implants at insertion and over time. The significant increase over time of reverse torque values with respect to insertion torque (p < 0.001) did not differ between the implants. However, the bone-to-implant contact of TSV MP-1 HA was significantly higher than that of cmSLA implants at 6 weeks (p < 0.01). These data validate previous findings of a hydrophilic implant surface and extend the observation of early osseointegration to a rough surface implant in porous trabecular bone.

Calcium Phosphate-Coated Titanium Implants in the Mandible: Limitations of the in vivo Minipig Model

INTRODUCTION

We aimed to compare implant osseointegration with calcium phosphate (CaP) surfaces and rough subtractive-treated sandblasted/acid etched surfaces (SA) in an in vivo minipig mandible model.

MATERIALS AND METHODS

A total of 36 cylindrical press-fit implants with two different surfaces (CaP, n = 18; SA, n = 18) were inserted bilaterally into the mandible of 9 adult female minipigs. After 2, 4, and 8 weeks, we analyzed the cortical bone-to-implant contact (cBIC; %) and area coverage of bone-to-implant contact within representative bone chambers (aBIC; %).

RESULTS

After 2 weeks, CaP implants showed no significant increase in cBIC and aBIC compared to SA (cBIC: mean 38 ± 5 vs. 16 ± 11%; aBIC: mean 21 ± 1 vs. 6 ± 9%). Two CaP implants failed to achieve osseointegration. After 4 weeks, no statistical difference between CaP and SA was seen for cBIC (mean 54 ± 15 vs. 43 ± 16%) and aBIC (mean 43 ± 28 vs. 32 ± 6). However, we excluded two implants in each group due to failure of osseointegration. After 8 weeks, we observed no significant intergroup differences (cBIC: 18 ± 9 vs. 18 ± 20%; aBIC: 13 ± 8 vs. 16 ± 9%). Again, three CaP implants and two SA implants had to be excluded due to failure of osseointegration.

CONCLUSION

Due to multiple implant losses, we cannot recommend the oral mandibular minipig in vivo model for future endosseous implant research. Considering the higher rate of osseointegration failure, CaP coatings may provide an alternative to common subtractive implant surface modifications in the early phase post-insertion.

Effects of Long Durations of RF-Magnetron Sputtering Deposition of Hydroxyapatite on Titanium Dental Implants

Objectives  Dental implant is a revolution in dentistry; some shortages are still a focus of research. This study use long duration of radiofrequency (RF)–magnetron sputtering to coat titanium (Ti) implant with hydroxyapatite (HA) to obtain a uniform, strongly adhered in a few micrometers in thickness.

Materials and Methods  Two types of substrates, discs and root form cylinders were prepared using a grade 1 commercially pure (CP) Ti rod. A RF–magnetron sputtering device was used to coat specimens with HA. Magnetron sputtering was set at 150 W for 22 hours at 100°C under continuous argon gas flow and substrate rotation at 10 rpm. Coat properties were evaluated via field emission scanning electron microscopy (FESEM), scanning electron microscopy–energy dispersive X-ray (EDX) analysis, atomic force microscopy, and Vickers hardness (VH). Student’s t -test was used.

Results  All FESEM images showed a homogeneous, continuous, and crack-free HA coat with a rough surface. EDX analysis revealed inclusion of HA particles within the substrate surface in a calcium (Ca)/phosphorus (P) ratio (16.58/11.31) close to that of HA. Elemental and EDX analyses showed Ca, Ti, P, and oxygen within Ti. The FESEM views at a cross-section of the substrate showed an average of 7 µm coat thickness. Moreover, these images revealed a dense, compact, and uniform continuous adhesion between the coat layer and the substrate. Roughness result indicated highly significant difference between uncoated Ti and HA coat (p-value < 0.05). A significant improvement in the VH value was observed when coat hardness was compared with the Ti substrate hardness (p-value < 0.05).

Conclusion  Prolonged magnetron sputtering successfully coat Ti dental implants with HA in micrometers thickness which is well adhered essentially in excellent osseointegration.

In Vivo Study for Clinical Application of Dental Stem Cell Therapy Incorporated with Dental Titanium Implants

The aim of this study was to investigate the behavior of dental-derived human mesenchymal stem cells (d-hMSCs) in response to differently surface-treated implants and to evaluate the effect of d-hMSCs on local osteogenesis around an implant in vivo. d-hMSCs derived from alveolar bone were established and cultured on machined, sandblasted and acid-etched (SLA)-treated titanium discs with and without osteogenic induction medium. Their morphological and osteogenic potential was assessed by scanning electron microscopy (SEM) and real-time polymerase chain reaction (RT-PCR) via mixing of 5 × 10⁶ of d-hMSCs with 1 mL of Metrigel and 20 μL of gel-cell mixture, which was dispensed into the defect followed by the placement of customized mini-implants (machined, SLA-treated implants) in New Zealand white rabbits. Following healing periods of 2 weeks and 12 weeks, the obtained samples in each group were analyzed radiographically, histomorphometrically and immunohistochemically. The quantitative change in osteogenic differentiation of d-hMSCs was identified according to the type of surface treatment. Radiographic analysis revealed that an increase in new bone formation was statistically significant in the d-hMSCs group. Histomorphometric analysis was in accordance with radiographic analysis, showing the significantly increased new bone formation in the d-hMSCs group regardless of time of sacrifice. Human nuclei A was identified near the area where d-hMSCs were implanted but the level of expression was found to be decreased as time passed. Within the limitations of the present study, in this animal model, the transplantation of d-hMSCs enhanced the new bone formation around an implant and the survival and function of the stem cells was experimentally proven up to 12 weeks post-sacrifice.

Implant stability and survival rates of a hydrophilic versus a conventional sandblasted, acid-etched implant surface: Systematic review and meta-analysis

BACKGROUND

Modifying the implant surface via enhancing the wettability (hydrophilicity) improves osseointegration, reducing the healing period. In this study, the authors aimed to evaluate the stability and survival rates of implants with a hydrophilic surface compared with those with a sandblasted, acid-etched surface.

TYPES OF STUDIES REVIEWED

The included studies (randomized controlled trials) were identified through searches of PubMed, ScienceDirect, and Cochrane Library databases without date of publication restrictions. Quality assessment was performed using the Cochrane Collaboration tool. For primary outcome, confidence intervals were set at 95%; weighted means across the studies were calculated using a fixed-effects model or risk ratios and their 95% confidence intervals for secondary outcome.

RESULTS

The authors included 5 randomized controlled trials (246 dental implants) in the systematic review, which compared a hydrophilic with conventional sandblasted, acid-etched implant surface. The implant stability (primary outcome) was measured at baseline and 3, 6, and 8 weeks, and implant survival rates were measured as a secondary outcome. Overall, compared with the control groups, no clinically significant differences in implant stability or survival rates were identified for the hydrophilic surface groups.

CONCLUSIONS AND PRACTICAL IMPLICATIONS

The results did not show any clinically significant effect of a hydrophilic surface on improving implant stability or survival rates. However, these findings must be analyzed carefully owing to the limitations of this review, such as the small samples size and some differences among the included studies.

An In Vivo Study in Rat Femurs of Bioactive Silicate Coatings on Titanium Dental Implants

Silica-based ceramics have been proposed for coating purposes to enhance dental and orthopedic titanium (Ti) implant bioactivity. The aim of this study was to investigate the influence of sphene-based bioceramic (CaO.TiO₂.SiO₂) coatings on implant osseointegration in vivo. Sphene coatings were obtained from preceramic polymers and nano-sized active precursors and deposited by an automatic airbrush. Twenty customized Ti implants, ten sphene-coated and ten uncoated rough implants were implanted into the proximal femurs of ten Sprague-Dawley rats. Overall, cortical and cancellous bone-to-implant contact (BIC) were determined using micro-computed tomography (micro-CT) at 14 and 28 days. Moreover, peri-implant bone healing was histologically and histomorphometrically evaluated. The white blood cell count in the synovial fluid of the knee joints, if present, was also assessed. No difference in the BIC values was observed between the sphene-coated and uncoated implants, overall and in the two bone compartments (p > 0.05). Delamination of the coating occurred in three cases. Consistently with micro-CT data, the histological evaluation revealed no differences between the two groups. In addition, no synovial fluid could be collected on the test side, thus confirming sphene biocompatibility. In conclusion, sphene coating was found to be a suitable material for biomedical applications. Further studies are needed to improve coating adhesion to the implants.

Comprehensive In Vitro Testing of Calcium Phosphate-Based Bioceramics with Orthopedic and Dentistry Applications

Recently, a large spectrum of biomaterials emerged, with emphasis on various pure, blended, or doped calcium phosphates (CaPs). Although basic cytocompatibility testing protocols are referred by International Organization for Standardization (ISO) 10993 (parts 1-22), rigorous in vitro testing using cutting-edge technologies should be carried out in order to fully understand the behavior of various biomaterials (whether in bulk or low-dimensional object form) and to better gauge their outcome when implanted. In this review, current molecular techniques are assessed for the in-depth characterization of angiogenic potential, osteogenic capability, and the modulation of oxidative stress and inflammation properties of CaPs and their cation- and/or anion-substituted derivatives. Using such techniques, mechanisms of action of these compounds can be deciphered, highlighting the signaling pathway activation, cross-talk, and modulation by microRNA expression, which in turn can safely pave the road toward a better filtering of the truly functional, application-ready innovative therapeutic bioceramic-based solutions.

Implementation and characterization of coating pure titanium dental implant with sintered β-TCP by using Nd:YAG laser

Objectives

This work presents laser coating of grade 1 pure titanium (Ti) dental implant surface with sintered biological apatite beta-tricalcium phosphate (β-TCP), which has a chemical composition close to bone.

Materials and methods

Pulsed Nd:YAG laser of single pulse capability up to 70 J/10 ms and pulse peak power of 8 kW was used to implement the task. Laser pulse peak power, pulse duration, repetition rate and scanning speed were modulated to achieve the most homogenous, cohesive and highly adherent coat layer. Scanning electron microscopy (SEM), energy dispersive X-ray microscopy (EDX), optical microscopy and nanoindentation analyses were conducted to characterise and evaluate the microstructure, phases, modulus of elasticity of the coating layer and calcium-to-phosphate ratio and composition.

Results showed that the laser power and scanning speed influenced coating adherence. The cross-sectional field-emission scanning electron microscopy images at low power and high speed showed poor adherence and improved as the laser power increased to 2 kW. Decreasing the scanning speed to 0.2 mm/s at the same power of 2 kW increased adherence. EDX results of the substrate demonstrated that the chemical composition of the coat layer did not change after processing. Moreover, the maps revealed proper distribution of Ca and P with some agglomeration on the surface. The sharp peaks on the X-ray diffraction patterns indicated that β-TCPs in the coat layer were mostly crystalline. The elastic modulus was low at the surface and increased gradually with depth to reach 19 GPa at 200 nm; this value was close to that of bone. The microhardness of the coated substrate increased by about 88%. The laser pulse energy of 8.3 J, pulse peak power of 2 kW, pulse duration of 4.3 min, repetition rate of 10 Hz and scanning speed of 0.2 ms⁻¹ yielded the best results.

Conclusion

Both processing and coating have potential use for dental implant applications.

Kaempferol-immobilized titanium dioxide promotes formation of new bone: effects of loading methods on bone marrow stromal cell differentiation in vivo and in vitro

Background

Surface modification of titanium dioxide (TiO₂) implants promotes bone formation and shortens the osseointegration period. Kaempferol is a flavonoid that has the capacity to promote osteogenic differentiation in bone marrow stromal cells. The aim of this study was to promote bone formation around kaempferol immobilized on TiO₂ implants.

Methods

There were four experimental groups. Alkali-treated TiO₂ samples (implants and discs) were used as a control and immersed in Dulbecco's phosphate-buffered saline (DPBS) (Al-Ti). For the coprecipitation sample (Al-cK), the control samples were immersed in DPBS containing 50 µg kaempferol/100% ethanol. For the adsorption sample (Al-aK), 50 µg kaempferol/100% ethanol was dropped onto control samples. The surface topography of the TiO₂ implants was observed by scanning electron microscopy with energy-dispersive X-ray spectroscopy, and a release assay was performed. For in vitro experiments, rat bone marrow stromal cells (rBMSCs) were cultured on each of the TiO₂ samples to analyze cell proliferation, alkaline phosphatase activity, calcium deposition, and osteogenic differentiation. For in vivo experiments, TiO₂ implants placed on rat femur bones were analyzed for bone-implant contact by histological methods.

Results

Kaempferol was detected on the surface of Al-cK and Al-aK. The results of the in vitro study showed that rBMSCs cultured on Al-cK and Al-aK promoted alkaline phosphatase activity, calcium deposition, and osteogenic differentiation. The in vivo histological analysis revealed that Al-cK and Al-aK stimulated new bone formation around implants.

Conclusion

TiO₂ implant-immobilized kaempferol may be an effective tool for bone regeneration around dental implants.

Effects of recycling on the biomechanical characteristics of retrieved orthodontic miniscrews

Objective

The aim of this study was to compare recycled and unused orthodontic miniscrews to determine the feasibility of reuse. The comparisons included both miniscrews with machined surfaces (MS), and those with etched surfaces (ES).

Methods

Retrieved MS and ES were further divided into three subgroups according to the assigned recycling procedure: group A, air-water spray; group B, mechanical cleaning; and group C, mechanical and chemical cleaning. Unused screws were used as controls. Scanning electron microscopy, energy-dispersive X-ray spectrometry, insertion time and maximum insertion torque measurements in artificial bone, and biological responses in the form of periotest values (PTV), bone–implant contact ratio (BIC), and bone volume ratio (BV) were assessed.

Results

Morphological changes after recycling mainly occurred at the screw tip, and the cortical bone penetration success rate of recycled screws was lower than that of unused screws. Retrieved ES needed more thorough cleaning than retrieved MS to produce a surface composition similar to that of unused screws. There were no significant differences in PTV or BIC between recycled and unused screws, while the BV of the former was significantly lower than that of the latter (p < 0.05).

Conclusions

These results indicate that reuse of recycled orthodontic miniscrews may not be feasible from the biomechanical aspect.

Graphite Oxide to Graphene. Biomaterials to Bionics

The advent of implantable biomaterials has revolutionized medical treatment, allowing the development of the fields of tissue engineering and medical bionic devices (e.g., cochlea implants to restore hearing, vagus nerve stimulators to control Parkinson's disease, and cardiac pace makers). Similarly, future materials developments are likely to continue to drive development in treatment of disease and disability, or even enhancing human potential. The material requirements for implantable devices are stringent. In all cases they must be nontoxic and provide appropriate mechanical integrity for the application at hand. In the case of scaffolds for tissue regeneration, biodegradability in an appropriate time frame may be required, and for medical bionics electronic conductivity is essential. The emergence of graphene and graphene-family composites has resulted in materials and structures highly relevant to the expansion of the biomaterials inventory available for implantable medical devices. The rich chemistries available are able to ensure properties uncovered in the nanodomain are conveyed into the world of macroscopic devices. Here, the inherent properties of graphene, along with how graphene or structures containing it interface with living cells and the effect of electrical stimulation on nerves and cells, are reviewed.

Surface Modifications and Their Effects on Titanium Dental Implants

This review covers several basic methodologies of surface treatment and their effects on titanium (Ti) implants. The importance of each treatment and its effects will be discussed in detail in order to compare their effectiveness in promoting osseointegration. Published literature for the last 18 years was selected with the use of keywords like titanium dental implant, surface roughness, coating, and osseointegration. Significant surface roughness played an important role in providing effective surface for bone implant contact, cell proliferation, and removal torque, despite having good mechanical properties. Overall, published studies indicated that an acid etched surface-modified and a coating application on commercial pure titanium implant was most preferable in producing the good surface roughness. Thus, a combination of a good surface roughness and mechanical properties of titanium could lead to successful dental implants.

Nanosized Hydroxyapatite Coating on PEEK Implants Enhances Early Bone Formation: A Histological and Three-Dimensional Investigation in Rabbit Bone

Polyether ether ketone (PEEK) has been frequently used in spinal surgery with good clinical results. The material has a low elastic modulus and is radiolucent. However, in oral implantology PEEK has displayed inferior ability to osseointegrate compared to titanium materials. One idea to reinforce PEEK would be to coat it with hydroxyapatite (HA), a ceramic material of good biocompatibility. In the present study we analyzed HA-coated PEEK tibial implants via histology and radiography when following up at 3 and 12 weeks. Of the 48 implants, 24 were HA-coated PEEK screws (test) and another 24 implants served as uncoated PEEK controls. HA-coated PEEK implants were always osseointegrated. The total bone area (BA) was higher for test compared to control implants at 3 (p < 0.05) and 12 weeks (p < 0.05). Mean bone implant contact (BIC) percentage was significantly higher (p = 0.024) for the test compared to control implants at 3 weeks and higher without statistical significance at 12 weeks. The effect of HA-coating was concluded to be significant with respect to early bone formation, and HA-coated PEEK implants may represent a good material to serve as bone anchored clinical devices.

A new application of cell-free bone regeneration: immobilizing stem cells from human exfoliated deciduous teeth-conditioned medium onto titanium implants using atmospheric pressure plasma treatment

Introduction

Surface modification of titanium (Ti) implants promotes bone formation and shortens the osseointegration period. The aim of this study was to promote bone regeneration and stability around implants using atmospheric pressure plasma (APP) pretreatment. This was followed by immobilization of stem cells from human exfoliated deciduous teeth-conditioned medium (SHED-CM) on the Ti implant surface.

Methods

Ti samples (implants, discs, powder) were treated with APP for 30 seconds. Subsequently, these were immobilized on the treated Ti surface, soaked and agitated in phosphate-buffered saline or SHED-CM for 24 hours at 37 °C. The surface topography of the Ti implants was observed using scanning electron microscopy with energy dispersive X-ray spectroscopy. In vivo experiments using Ti implants placed on canine femur bone were then conducted to permit histological analysis at the bone-implant boundary. For the in vitro experiments, protein assays (SDS-PAGE, Bradford assay, liquid chromatography-ion trap mass spectrometry) and canine bone marrow stromal cell (cBMSC) attachment assays were performed using Ti discs or powder.

Results

In the in vitro study, treatment of Ti implant surfaces with SHED-CM led to calcium phosphate and extracellular matrix protein immobilization. APP pretreatment increased the amount of SHED-CM immobilized on Ti powder, and contributed to increased cBMSC attachment on Ti discs. In the in vivo study, histological analysis revealed that the Ti implants treated with APP and SHED-CM stimulated new bone formation around implants.

Conclusions

Implant device APP pretreatment followed by SHED-CM immobilization may be an effective application to facilitate bone regeneration around dental implants.

VEGF promotes osteogenic differentiation of ASCs on ordered fluorapatite surfaces

Vascular endothelial growth factor (VEGF) has been reported to mediate both osteogenesis and angiogenesis in bone regeneration. We previously found an upregulation of VEGF in adipose-derived stem cells (ASCs) when obvious mineralization occurred on a novel fluorapatite (FA)-coated surfaces. This study investigated the effect of FA and VEGF on the growth, differentiation and mineralization of (ASC) grown on ordered FA surfaces. Cells grown on FA and treated with VEGF demonstrated osteogenic differentiation as measured with ALP staining, and obvious mineralization as measured by Alizarin red staining. A combined stimulating effect of FA and VEGF was seen using both indicators. VEGF signaling pathway perturbation using a specific VEGF receptor inhibitor showed the lowest levels of ALP and Alizarin red staining, which was partially rescued when the cells were grown on FA and/or treated with the addition of VEGF. The osteogenic differentiation of ASCs stimulated by these FA surfaces as well as VEGF has been shown to be mediated through, but probably not only, the VEGF signaling pathway. The enhancement of osteogenic differentiation and mineralization supports the potential use of therapeutic VEGF and FA coatings in bone regeneration.

Surgical procedure of extracting teeth for obtaining dental pulp for regenerative medicine in swine

Dental pulp is a potential source of cells that can be used in cell replacement therapy for various nerve disorders, including stroke, spinal cord injury, and peripheral nerve defect. However, the validation of an animal model closely related to humans is needed in translational research. The miniature pig is a suitable experimental model in maxillofacial surgery, because its anatomical structure and size are similar to those of humans. However, the swine tooth is extremely long. The routine closed extraction procedure for harvesting dental pulp tissue causes root fracture. This report describes the details of a surgical procedure for tooth extraction. Four healthy 7-8-month-old male NIBS miniature pigs were used. Two mandibular deciduous right incisors (Di1 and Di2) were extracted in order to obtain dental pulp tissue. Gingival envelope incision with vertical-releasing incision was performed, and a full-thickness mucoperiosteal flap was made. The buccal alveolar bone was exposed and removed by osteotomy. Di1 and Di2 were extracted. Dental pulp tissue was obtained from these extracted teeth by splitting hard tissue. In this procedure, 9.8 ± 2.5 × 10(5) cells were obtained from the mandibular Di1 and Di2 (n = 4).

Biomechanical evaluation and surface characterization of a nano-modified surface on PEEK implants: a study in the rabbit tibia

Polyether ether ketone (PEEK) is today frequently used as a biomaterial in different medical operations due to its excellent mechanical and chemical properties. However, the untreated surface of PEEK is bioinert and hydrophobic, and it does not osseointegrate in its pure form. The aim of this study was to evaluate a unique nano-modified surface of PEEK with respect to osseointegration. Forty-eight threaded, non-cutting PEEK implants were inserted bilaterally in the tibia of 24 rabbits. Half of the implants (n=24) were coated with nanocrystalline hydroxyapatite (test) and the remaining implants (n=24) were left uncoated (control). Half of the animals (n=12) were euthanized after 3 weeks of healing and the remaining (n=12) after 12 weeks. The implant retention was measured with a removal torque apparatus. Surface analysis was performed with interferometry, scanning electron microscopy, and X-ray photon spectroscopy to relate the removal torque to the applied surface. The test implants revealed a significantly higher retention after 3 weeks (P=0.05) and 12 weeks (P=0.028) compared to controls. The result of the present study proves that the addition of nanocrystalline hydroxyapatite coating to PEEK surfaces significantly increases its removal torque and biocompatibility.

Significance of calcium phosphate coatings for the enhancement of new bone osteogenesis--a review

A systematic analysis of results available from in vitro, in vivo and clinical trials on the effects of biocompatible calcium phosphate (CaP) coatings is presented. An overview of the most frequently used methods to prepare CaP-based coatings was conducted. Dense, homogeneous, highly adherent and biocompatible CaP or hybrid organic/inorganic CaP coatings with tailored properties can be deposited. It has been demonstrated that CaP coatings have a significant effect on the bone regeneration process. In vitro experiments using different cells (e.g. SaOS-2, human mesenchymal stem cells and osteoblast-like cells) have revealed that CaP coatings enhance cellular adhesion, proliferation and differentiation to promote bone regeneration. However, in vivo, the exact mechanism of osteogenesis in response to CaP coatings is unclear; indeed, there are conflicting reports of the effectiveness of CaP coatings, with results ranging from highly effective to no significant or even negative effects. This review therefore highlights progress in CaP coatings for orthopaedic implants and discusses the future research and use of these devices. Currently, an exciting area of research is in bioactive hybrid composite CaP-based coatings containing both inorganic (CaP coating) and organic (collagen, bone morphogenetic proteins, arginylglycylaspartic acid etc.) components with the aim of promoting tissue ingrowth and vascularization. Further investigations are necessary to reveal the relative influences of implant design, surgical procedure, and coating characteristics (thickness, structure, topography, porosity, wettability etc.) on the long-term clinical effects of hybrid CaP coatings. In addition to commercially available plasma spraying, other effective routes for the fabrication of hybrid CaP coatings for clinical use still need to be determined and current progress is discussed.