Effect of phototherapy on dentin bond strength and microleakage when bonded to resin with different conditioning regimes

Comparative evaluation of effect of chlorhexidine application on dentin bond strength with two different adhesives after ER, CR: YSGG phototherapy: an in vitro study

This study aimed to assess the efficacy of phototherapy with an Er, Cr:YSGG laser on the bond strength of dentin using two different adhesive systems after chlorhexidine (CHX) application. Twenty-four non-carious human molar teeth were separated into three main groups: negative control Group A (Group A), CHX and phototherapy with an Er, Cr:YSGG laser (Group PC), and CHX with conventional diamond bur (no phototherapy) (Group C). These groups were divided into two subgroups based on adhesives: Clearfil Universal Quick Bond and Clearfil SE Bond. To evaluate the microtensile bond strength, the occlusal enamel surfaces of the teeth were removed with a low-speed, water-cooled diamond bur to expose hard dentin tissue. The teeth within Group PC were treated with Er, Cr:YSGG phototherapy. The surfaces were then disinfected with 0.2% chlorhexidine gluconate. Subgroups were applied according to the manufacturer's instructions using the adhesive systems mentioned above. Following adhesive application, the teeth were restored with composite resin. A microtensile bond strength test was performed on the test sticks obtained from the teeth using a universal test device. Data were analyzed using variance analysis (ANOVA) at a significance level of p < 0.05. Among all groups, the highest bond strength was achieved with Clearfil SE Bond with CHX + phototherapy (45.6 ± 4.2), while the lowest was achieved with Clearfil Universal Quick Bond without phototherapy (control group) (27.0 ± 6.7) (p < 0.05). Phototherapy with Er, Cr: YSGG following chlorhexidine application enhanced the bond strength of both the bond systems (p < 0.05).

Influence of methylene blue, Riboflavin, and indocyanine green on the bond strength of caries affected dentin when bonded to resin-modified glass ionomer cement

AIM

The present study aimed to assess the influence of methylene blue (MBP), Riboflavin, and indocyanine green (ICG) on the bond strength of caries affected dentin (CAD) when bonded to resin-modified glass ionomer cement (RMGIC).

MATERIALS AND METHODS

Human third molars with caries lesions were isolated and collected scrutinized based on ICDAS criteria. The teeth were cleaned using a periodontal scaler and disinfected. All samples were positioned in polyvinyl up to the cementoenamel junction. The samples were randomly distributed into five groups based on the pretreatment regime. Samples in group 1, were pretreated with MBP; group 2, polyacrylic acid (PAA) group 3, ICG, group 4, Riboflavin photosensitizer, and group 5, 37% phosphoric acid (PA). All samples were bonded with RMGIC. 10 samples were subjected to the universal testing machine for shear bond strength (SBS) testing. Five samples from each group were placed in fuchsine dye for the microleakage assessment. Comparison of means and standard deviations (SD) of SBS and microleakage in investigated groups was performed using analysis of variance (ANOVA) and Tukey's post hoc test at a significance level (p=0.05) RESULTS: : The highest micro shear bond values were observed in group 2 (CAD conditioned with PAA) (14.26±1.67 MPa). Whereas, the lowest bond values were found in group 1 (treated with MBP) (8.82±1.08 MPa). CAD conditioned with different photosensitizers i.e., MBP, ICG, and Riboflavin before bonding to RMGIC displayed comparable bond values (8.82±1.08 MPa), (9.47±0.21 MPa), and (11.23±0.47 MPa) respectively (p>0.05). Samples conditioned with 37% PA showed significantly higher microleakage scores compared to other surface-treated groups (p<0.05).

CONCLUSION

Caries-affected dentin conditioned with polyacrylic acid demonstrated low microleakage and high bond strength.

Effect of Photodynamic therapy and Er,Cr: YSGG laser on bond strength of bleached enamel to composite resin

OBJECTIVE

The purpose of the present study was bleached enamel reversal using conventional ascorbic acid (AA) and contemporary methods including Photodynamic therapy (PDT), Er, Cr: YSGG (ECL) on bond integrity to composite resin.

MATERIAL AND METHOD

Forty sound permanent mandibular premolars were collected from a dental clinical setting and disinfected. All forty samples were mounted vertically in a rubber mold exposing only the clinical crown. All samples were bleached using Opalescence Boost Professional Teeth Whitening. After the bleaching procedure, each sample was randomly allocated into four groups according to surface treatment. Samples in group 1 were treated with methylene blue photosensitizer (MBP). Samples in group 2 were exposed to 10% sodium ascorbate. Samples in group 3 were treated with Er, Cr: YSGG laser (ECL). Samples in group 4 were not treated (control). All Samples were treated with 37% phosphoric acid and a bonding agent was applied. A bulk-fill composite was cured to all specimens and all samples were treated in a thermocycler. Specimens were placed in a universal testing machine for shear bond strength (SBS) testing. Descriptive statistics were associated by analysis of variance (ANOVA) and Tukey's post hoc test maintaining level of significance (p<0.05) RESULTS: The lowest SBS scores were achieved in the bleached enamel (BE) group (15.25±1.745 MPa). Whereas, the highest bond integrity was attained by AA group (32.23±1.854 MPa). Samples treated with ECL (31.87±1.659 MPa) and AA (32.23±1.854) were comparable (p>0.05). Samples treated with PDT exhibited significantly different SBS (22.41±1.258) compared to other experimental groups CONCLUSION: ECL showed a reversal effect of BE compared to AA and has the potential to be used in clinical settings. BE reversal using MBP needs further investigation.

Adhesive strength of bioactive resin for endodontic tooth build up to dentin treated with conventional and contemporary treatments

AIM

The aim of present ex-vivo study was to assess and evaluate the influence of alternative dentinal conditioning methods- Er,Cr:YSGG (ECL) and Photodynamic therapy (PDT) in comparison to traditional etching regimes- Self Etch Resin (SER) and total etch and rinse (TER) on the bond values of Bioactive restorative material (BA) and Multicore (MC) bulk filled resin composite restorations.

MATERIAL AND METHODS

Eighty caries free mandibular molars were disinfected and embedded in acrylic resin up to Cemento enamel junction (CEJ). Buccal surfaces of all samples were grounded to depth of 2 mm. Specimens were divided into eight groups (n = 20) based on surface treatment received. Samples in group 1 and 2 conditioned with ECYL, group 3 and 4 pre-treated with methylene blue photosensitizer (MBP), group 5 and 6 surfaces conditioned with TER and samples in group 7 and 8 conditioned with SER. Dentin bonding agent was applied and samples of group 1, 3, 5 and 7 were bonded with BA and 2,4,6,8 bonded to MC. Samples were placed in universal testing machine for SBS testing. Data was assessed using analysis of variance (ANOVA) and Tukey multiple comparisons test.

RESULTS

Specimens in group 6 treated with TER and bonded with MC demonstrated maximum SBS (19.61 ± 0.587 MPa). Whereas, group 3 dentin conditioned to MBP and bonded to BA displayed lowest bond values (12.01 ± 0.892 MPa). Samples in group 3 and group 4 dentin treated with MBP bonded to MC (13.68 ± 0.221 MPa) and BA (12.01 ± 0.892 MPa) displayed comparable bond integrity (p > 0.05) CONCLUSION: Dentin pre-treated with TER still remains the gold standard. ECYL as an alternative approach to condition dentin has shown potential and can be recommended in clinical settings. MC as bulk fill composite is recommended over BA irrespective of dentine conditioning technique. MBP as dentin conditioner needs further investigation.

Photodynamic activation of irrigation (using different laser prototypes) on push out bond strength of fiber posts

BACKGROUND

To evaluate the influence of photodynamic therapy (PDT) and light activated irrigation (LAI) using different laser prototypes Er,Cr:YSGG (ECYL), Er:Yag (EYL), Nd-Yag (NYL) on pushout bond strength of Pre-fabricated fiber reinforced composite (PFRC) post to radicular dentin.

MATERIAL AND METHOD

Fifty maxillary and mandibular teeth were collected, cleaned and decoronated. Canals were instrumented using crown-down technique. Flaring of canals was performed using protaper S1, SX files. F1, F2 and F3 files were utilized for finishing of canal preparations. Prepared root canals were dried and obturated with gutta percha. Teeth were placed vertically within the section of polyvinyl pipes using acrylic resin. Post space preparation was completed using peso-reamers. Based on the PDT and laser activated irrigation (LAI) with different laser prototypes, samples were divided into five groups of 10 specimens each. Group 1- PDT, group 2-5.25 % NaOCl (sodium hypochlorite) and 17 % EDTA (ethylene diamine tetra acetic acid), group 3-5.25 % NaOCl with 17 % EDTA and NYL, group 4-5.25 % NaOCl with 17 % EDTA and EYL ; and group 5-5.25 % NaOCl +17 % EDTA and ECYL. Fiber post were luted in root canals with self-etch dual cure cement and teeth were sectioned at three levels (apical, middle and coronal). Push-out test was performed by placing the specimens in universal testing machine. Failure analysis of debonded surfaces was evaluated using stereomicroscope at 40× magnification. Means and standard deviations of push out bond strength were assessed by one-way analysis of variance (ANOVA). Comparison between means of push out bond strength was evaluated using Tukey multiple comparison tests (p = 0.05).

RESULT

The highest push out bond strength was observed in group 5 at all three levels, coronal (10.08 ± 0.74 MPa), middle (8.95 ± 0.94 MPa) and apical (6.00 ± 0.88 MPa). The lowest push out bond strength was demonstrated by group 2 at all levels, coronal (6.15 ± 1.22 MPa), middle (5.65 ± 0.95 MPa) and apical (2.25 ± 0.55 MPa). Intra-group comparison showed decrease in push out bond strength in the coronal to apical direction among all investigated groups. Inter-group comparison exhibited comparable push out bond strength at all three levels of root for group 1 and group 2 specimens (p > 0.05).

CONCLUSION

LAI with different laser prototypes improved push out bond values of PFRC post to root dentin as an adjunct to NaOCl and EDTA treatment. PDT improved push out strength compared to conventional canal cleaning regime.