Characterisation of electrospun PS/PU polymer blend fibre mat for oil sorption

Thermal conversion of irradiated LLDPE waste into sustainable sponge-like compounds: a novel approach for efficient trace-level oil-water removal

The newest method for recycling waste linear low-density polyethylene (LLDPE) is the thermo-catalytic degradation technique known as catalytic pyrolysis. Typically, it is limited by 500-800 °C high temperatures. Catalytic pyrolysis releases toxins and forms harmful carbonized char. The current study is based on exposing wasted LLDPE to different gamma irradiation doses and then pyrolysis in castor oil (150-300 °C). The output product of Ir-(rLLDPE) is turned into another compound with a new structural architecture (sponge-like). SEM analysis confirms conversion, showing sponge-like spicules and layers. Ir-(rLLDPE) is sponge-like with a soft, malleable, absorbent texture. The DSC demonstrates altered thermal properties, with a melting point at 121 °C splitting into two peaks (endothermic at 117 °C and exothermic at 160 °C). The exothermic peaks signify the curing process of the sponge-like material. Ir-(rLLDPE) is assessed as an adsorbent for aqueous oils and solvents. The study examines irradiation doses, pyrolysis temperature, and time on adsorbent capacity. The oil removal obeys the Langmuir isotherm with monolayer adsorption, with a maximum adsorption capacity of 24.75 g/g of waste oil and 43 g/g of 1,1,2,2-tetrachloroethane. Squashing maintains adsorption after 20 reuses. Data shows sponges effectively clean marine oil spills and solvents.

Hollow polyester/kapok/hollow polyester fiber-based needle punched nonwoven composite materials for rapid and efficient oil sorption

Nowadays oil pollution poses a serious threat to the environment and people's daily life. As reusable and environmentally friendly materials, fiber-based oil sorption materials can effectively alleviate this phenomenon. However, maintaining a high sorption rate along with improved mechanical properties remains a challenge for oil sorption materials. Herein, we report a novel hollow PET/kapok/hollow PET nonwoven with high porosity and oil retention, outstanding cyclic oil sorption rate and improved mechanical performance using kapok as the oil preserver and hollow PET as the conductor and structure enhancer. Benefiting from the three-layer composite structure fabricated by carding and needle punching reinforcement, the resulting oil sorption materials, with kapok proportion more than or equal to 60%, exhibited high oil sorption rate and oil sorption speed. The materials of 20HP/60K/20HP component content present a high initial oil sorption rate of 28.22 g g-1, a maximum oil sorption rate of 31.17 g g-1 and a sorption rate constant of the Quasi second-order kinetic equation of 0.067 in plant oil. On the other hand, when the proportion of kapok fiber in the material was below 60%, due to the introduction of hollow PET, the mechanical properties were significantly boosted, and its oil retention and reusability were distinguished, with a reuse rate stabilizing at a relatively high level (>93%) in plant oil after undergoing three oil sorption cycles. The successful fabrication of hollow PET/kapok/hollow PET nonwovens could provide a new approach for the design and development of oil sorption materials.