An insight into formation of nanostructured coatings on metallic substrates by planetary ball milling

Microstructure of Coatings on Nickel and Steel Platelets Obtained by Co-Milling with NiAl and CrB2 Powders

Metal matrix composite coatings are developed to protect parts made from materials susceptible to wear, like nickel alloys or stainless steel. The industry-established deposition method is presently an atmospheric plasma spraying method since it allows the production of both well-adhering and thick coatings. Alternatively, similar coatings could be produced by co-milling of ceramic and alloyed powders together with metallic plates serving as substrates. It results in mechanical embedding of the powder particles into exposed metallic surfaces required coatings. The present experiment was aimed at the analysis of microstructure of such coatings obtained using NiAl and CrB₂ powders. They were loaded together with nickel and stainless steel platelets into ball mill vials and rotated at 350 rpm for up to 32 h. This helped to produce coatings of a thickness up to ~40 µm. The optical, scanning, and transmission electron microscopy observations of the coatings led to conclusion that the higher the rotation speed of vials, the wider the intermixing zone between the coating and the substrate. Simultaneously, it was established that the total thickness of the coating deposited at specified conditions is limited by the brittleness of its nanocrystalline matrix. An increase in the hardness of the substrate results in a decrease of the intermixing zone. The above results indicate that even as the method based on mechanical embedding could so far produce thinner coatings than the plasma spraying, in the former case they are characterized by a more uniform nanocrystalline matrix with homogenously distributed fine ceramic particles.

Powder Metallurgy Processing of a WxTaTiVCr High-Entropy Alloy and Its Derivative Alloys for Fusion Material Applications

The W_xTaTiVCr high-entropy alloy with 32at.% of tungsten (W) and its derivative alloys with 42 to 90at.% of W with in-situ TiC were prepared via the mixing of elemental W, Ta, Ti, V and Cr powders followed by spark plasma sintering for the development of reduced-activation alloys for fusion plasma-facing materials. Characterization of the sintered samples revealed a BCC lattice and a multi-phase structure. The selected-area diffraction patterns confirmed the formation of TiC in the high-entropy alloy and its derivative alloys. It revealed the development of C15 (cubic) Laves phases as well in alloys with 71 to 90at.% W. A mechanical examination of the samples revealed a more than twofold improvement in the hardness and strength due to solid-solution strengthening and dispersion strengthening. This study explored the potential of powder metallurgy processing for the fabrication of a high-entropy alloy and other derived compositions with enhanced hardness and strength.