The Design of Mini-Rotary Forcespinning System for Nanofiber Synthesis

Preparation and modification of forcespun polypropylene nanofibers for adsorption of uranium (VI) from simulated seawater

In this paper, polypropylene (PP) nanofibers were prepared using the melt forcespinning technology by a handmade device. Then, the surface of PP nanofibers was grafted through the high energy electron beams (EB) pre-irradiation method by acrylonitrile and methacrylic acid monomers with grafting percentage of 145.55%. The 92% of grafted cyano functional groups on nanofibers were converted to amidoxime groups, then modified by an alkaline solution. Characterization and surface morphology of nanofibers were investigated by Fourier Transform Infrared (FTIR) spectroscopy and scanning electron microscopy (SEM). The produced adsorbent was used to adsorb U(VI) ions from simulated seawater. The maximum adsorption was 83.24 mg/g in the optimal time of 60 min and optimal pH of 4. The optimum desorption efficiency was 80% in HCl 0.5 M. The kinetic data in optimum conditions showed that the adsorption followed an S-shaped kinetic model. The Adsorption equilibrium studies presented S-shape isotherm model that confirmed the adsorption occurs both on the adsorbent surface and in its pores The thermodynamic studies indicated spontaneous adsorption of uranyl ions and the higher efficiency adsorption at higher temperatures. The selectivity of adsorbent for metal ions followed the order V(V)>U(VI)>CO(II)>Ni(II)>Fe(II). These results shows that the prepared and modified nanofibers in this work can be considered as an effective and promising adsorbents for removal of uranium ions from seawater with high efficiency.

Continuous Dual-Track Fabrication of Polymer Micro-/Nanofibers Based on Direct Drawing

This manuscript proposes a continuous and straightforward method for fabricating suspended micro- and nanodiameter polymer fibers using an automated single-step drawing system. Termed track spinning, the system is based on a simple manual fiber drawing process that is automated by using two oppositely rotating tracks. Fibers are continuously spun by direct contact of polymer solution coated tracks followed by mechanical drawing as the distance between the tracks increases. The device can draw single or multifilament arrays of micro- and nanofibers from many kinds of polymers and solvent combinations. To demonstrate, fibers were pulled from polymer solutions containing polyvinyl acetate (PVAc) and polyurethane (PU). Fiber morphology was smooth and uniform, and the diameter was sensitive to draw length and polymer solution/melt properties. Polymer nanofibers with diameters as small as 450 nm and length of 255 mm were produced. The track spinning method is able to form fibers from high viscosity solutions and melts that are not compatible with some other nanofiber fabrication methods. Further, the setup is simple and inexpensive to implement and nozzleless and does not require an electric field or high-velocity jets, and the tracks can be widened and patterned/textured to enhance fiber yield and manufacturing precision.