Use of a light-polymerized composite removable partial denture base for a patient hypersensitive to poly(methyl methacrylate), polysulfone, and polycarbonate: a clinical report

Bonding Efficiency between Artificial Teeth and Denture Base in CAD/CAM and Conventional Complete Removable Dentures

A common challenge encountered with both traditional and digitally produced dentures involves the extraction of artificial teeth from the denture base. This narrative review seeks to present an updated perspective on the adherence of synthetic teeth for denture base materials, employing diverse methods. Dental technicians often employ chemical approaches and mechanical techniques (including abrasion, laser treatment, and abrasive blasting) to augment the retention of denture teeth. However, the efficacy of these treatments remains uncertain. In certain instances, specific combinations of Denture Base Resin (DBR) materials and artificial teeth exhibit improved performance in conventional heat-cured dentures following these treatments. The primary reasons for failure are attributed to material incompatibility and inadequate copolymerization. As new denture fabrication techniques and materials continue to emerge, further research is imperative to identify optimal tooth-DBR combinations. Notably, 3D-printed tooth-DBR combinations have demonstrated reduced bond strength and less favorable failure patterns, while utilizing milled and traditional combinations appears to be a more prudent choice until advancements in additive manufacturing enhance the reliability of 3D-printing methods.

Adhesion of Conventional, 3D-Printed and Milled Artificial Teeth to Resin Substrates for Complete Dentures: A Narrative Review

BACKGROUND

One type of failure in complete or partial dentures is the detachment of resin teeth from denture base resin (DBR). This common complication is also observed in the new generation of digitally fabricated dentures. The purpose of this review was to provide an update on the adhesion of artificial teeth to denture resin substrates fabricated by conventional and digital methods.

METHODS

A search strategy was applied to retrieve relevant studies in PubMed and Scopus.

RESULTS

Chemical (monomers, ethyl acetone, conditioning liquids, adhesive agents, etc.) and mechanical (grinding, laser, sandblasting, etc.) treatments are commonly used by technicians to improve denture teeth retention with controversial benefits. Better performance in conventional dentures is realized for certain combinations of DBR materials and denture teeth after mechanical or chemical treatment.

CONCLUSIONS

The incompatibility of certain materials and lack of copolymerization are the main reasons for failure. Due to the emerging field of new techniques for denture fabrication, different materials have been developed, and further research is needed to elaborate the best combination of teeth and DBRs. Lower bond strength and suboptimal failure modes have been related to 3D-printed combinations of teeth and DBRs, while milled and conventional combinations seem to be a safer choice until further improvements in printing technologies are developed.

Determination of Polyetheretherketone (PEEK) mechanical properties as a denture material

Purpose

To optimize the gypsum mold temperatures for pressed PEEK, and to estimate the impact, tensile strength and flexural properties of pressed and milled PEEK. Where appropriate, these properties were compared with those of PMMA.

Materials and Methods

Since the mold temperature could affect the properties of the injected parts, the temperature of 20 gypsum specimens was monitored using the multi-thermocouple system (n = 5). A total of 210 specimens were prepared for mechanical tests according to the ISO standard for denture base polymer (n = 10). The Izod impact, tensile strength, and flexural behavior were assessed. PEEK-OptimaNI1 (PEEK-pressed) was tested after processing via the pressing method at4 different mold temperatures. Machining PEEK-Juvora (PEEK-milled) specimens were prepared using the CAD-CAM production method. Data were analyzed via one-way ANOVA performed at a confidence level of 95% and a significant P-value of (P ≤ 0.05).

Results

In comparison to the furnace temperature more heat was required to preheat the gypsum mold up to 100, 150, 175 and 200 °C for pressing purposes. The highest impact strength was 5.7 kJ/m² for PEEK-pressed at 100 °C mold temperature and 4 kJ/m² for PEEK-milled. The latter had a higher tensile strength of 118 MPa. The best result for PEEK-pressed was 97 MPa at 200 °C mold temperature. Under a 4-point bending test, Young’s modulus of PEEK-milled was 5591 MPa, while the highest for PEEK-pressed was 4936 MPa at 200 °C mold temperature.

Conclusions

Compared to PMMA, given the superior mechanical properties of PEEK, it may become the material of choice for future use. Dentures constructed from PEEK polymer could well be routinely constructed in the near future.

Anaphylactic cardiovascular collapse during hemodialysis: Kounis syndrome in the dialysis room

Kounis syndrome seems to be not a rare disease but a rarely diagnosed disorder. Multiple causes can join forces and trigger the development of this syndrome. We report the first case of Kounis syndrome manifesting as myocardial infarction with cardiovascular collapse that occurred in the dialysis room following an allergic reaction. The dialysis apparatus material of polyurethane, polyamide, polycarbonate, silicon rubber and polypropylene were incriminated causes. Physicians should be aware of the causality and existence of this disorder in order to achieve early and correct diagnosis and apply the appropriate therapeutic measures.

Bonding of acrylic denture teeth to MMA/PMMA and light-curing denture base materials: the role of conditioning liquids

OBJECTIVES

The connection between resin denture teeth and the denture base is essential for the integrity of partial and full dentures. The aim of the present study was to analyse the bond strength of acrylic denture teeth to two light curing denture base materials compared to the gold-standard (MMA/PMMA) using different conditioning liquids.

METHODS

The ridge laps of 220 identical denture teeth were ground and pre-treated using different conditioning liquids (MMA, an experimental conditioning liquid as well as the two commercially available liquids Palabond and Versyo.bond). The denture base materials (PalaXpress, Versyo.com, Eclipse) were applied using a split mould to obtain tensile bond strength specimens of identical shape. Ten specimens per test group were either stored in water for 24h or thermocycled (5000×, 5-55°C) prior to tensile bond strength testing (cross-head speed 10mm/min). Data was subjected to parametric statistics (α=0.05).

RESULTS

The three-way ANOVA revealed a significant influence of the material, pre-treatment as well as the storage. PalaXpress showed the highest bond strength (24.3MPa) of all materials tested after TC, whereas the use of MMA led to the most constant results. Lower values were recorded for Versyo.com (17.5MPa) and Eclipse (10.4MPa) bonded with Versyo.bond.

CONCLUSIONS

The results indicate that MMA/PMMA based denture base resins provide reliable and durable bond strength to acrylic denture teeth. Using light-curing denture base materials requires the application of appropriate conditioning liquids to obtain acceptable bond strength. The use of MMA affects bond strength to light-curing denture base materials.

CLINICAL SIGNIFICANCE

The pre-treatment of denture teeth is critical regarding their bond-strength to denture base materials and in turn for the integrity of removable full and partial dentures. Light-curing denture base resins are more sensitive to the correct tooth pre-treatment compared to conventional MMA/PMMA materials, requiring specific conditioning liquids.

Biocompatibilidade dos materiais em Ortodontia: mito ou realidade?

O objetivo deste trabalho é apresentar uma revisão sobre os conceitos relacionados à biocompatibilidade dos materiais empregados em Ortodontia. Fatos relacionados às reações de hipersensibilidade aos diversos materiais ortodônticos são discutidos, sendo apresentadas as condutas recomendáveis nestas situações.

Allergy to auto-polymerized acrylic resin in an orthodontic patient

This article reports on a 60-year-old woman who had an allergic reaction to methylmethacrylate self-curing acrylic resin during orthodontic treatment. A localized hypersensitive reaction appeared on the palate after an orthodontic retainer was placed. Samples of the acrylic were removed and analyzed with gas chromatography to evaluate the residual monomer level. The residual monomer content was between 0.745% and 0.78%, which did not exceed international standards for this material. Patch tests were performed with several methylmethacrylate resin samples and processed with various techniques; they showed positive reactions. Despite the many alternative products available, self-curing acrylic resin remains widely used because of its low cost, ease of use, and diversity of indications. Orthodontists should be aware that allergic reactions can occur.