(1) Background: Most of the clinical literature dealing with dental implants has been issued by experienced teams working either in university settings or in private practice. The purpose of this study was to identify contributing covariates to implant failure and marginal bone loss (MBL) at the 1-year follow-up of a novel triangular-neck implant design when placed by inexperienced post-graduate students. (2) Methods: A prospective cohort study was conducted on study participants eligible for implant placement at the UIC (International University of Catalonia), Barcelona, Spain. Implant failure rate and contributors to implant failure and MBL were investigated among 24 implant and patient variables. (3) Results: One hundred and twenty implants (V3, MIS) were placed and rehabilitated by the students. The mean insertion torque was 37.1 Ncm. Survival and success rates were 97.5% and 96.7%, respectively. Implants placed in patients with smoking habits displayed a tendency of higher failure risk (OR = 5.31, p = 0.17) when compared to non-smokers. The mean (SD) MBL was 0.51 (0.44) mm. Gender significantly affected the MBL (p = 0.020). Bleeding on probing (BoP) on the buccal sites proved to be a good predictor of proximal MBL (p = 0.030). (4) Conclusions: The survival and success rates of the V3 triangular-neck implant placed by inexperienced post-graduate students at the 1-year follow-up were high and similar to the ones published in the literature by experienced teams on other implants.

Benefits of Residual Aluminum Oxide for Sand Blasting Titanium Dental Implants: Osseointegration and Bactericidal Effects

OBJECTIVES

The purpose of this work was to determine the influence of residual alumina after sand blasting treatment in titanium dental implants. This paper studied the effect of alumina on physico-chemical surface properties, such as: surface wettability, surface energy. Osseointegration and bacteria adhesion were determined in order to determine the effect of the abrasive particles.

MATERIALS AND METHODS

Three surfaces were studied: (1) as-received, (2) rough surface with residual alumina from sand blasting on the surface and (3) with the same roughness but without residual alumina. Roughness was determined by white light interferometer microscopy. Surface wettability was evaluated with a contact angle video-based system and the surface free energy by means of Owens and Wendt equation. Scanning electron microscopy equipped with microanalysis was used to study the morphology and determine the chemical composition of the surfaces. Bacteria (Lactobacillus salivarius and Streptococcus sanguinis) were cultured in each surface. In total, 110 dental implants were placed into the bone of eight minipigs in order to compare the osseointegration. The percentage of bone-to-implant contact was determined after 4 and 6 weeks of implantation with histometric analysis.

RESULTS

The surfaces with residual alumina presented a lower surface free energy than clean surfaces. The in vivo studies demonstrated that the residual alumina accelerated bone tissue growth at different implantation times, in relation to clean dental implants. In addition, residual alumina showed a bactericidal effect by decreasing the quantity of bacteria adhering to the titanium.

CONCLUSIONS

It is possible to verify the benefits that the alumina (percentages around 8% in weight) produces on the surface of titanium dental implants.

CLINICAL RELEVANCE

Clinicians should be aware of the benefits of sand-blasted alumina due to the physico-chemical surface changes demonstrated in in vivo tests.

Effect of Implant Surface Roughness and Macro- and Micro-Structural Composition on Wear and Metal Particles Released

Background: Considerations about implant surface wear and metal particles released during implant placement have been reported. However, little is known about implant surface macro- and microstructural components, which can influence these events. The aim of this research was to investigate accurately the surface morphology and chemical composition of commercially available dental implants, by means of multivariate and multidimensional statistical analysis, in order to predict their effect on wear onset and particle release during implant placement. Methods: The implant surface characterization (roughness, texture) was carried out through Confocal Microscopy and SEM-EDS analysis; the quantitative surface quality variables (amplitude and hybrid roughness parameters) were statistically analyzed through post hoc Bonferroni’s test for pair comparisons. Results: The parameters used by discriminant analysis evidenced several differences in terms of implant surface roughness between the examined fixtures. In relation to the observed surface quality, some of the investigated implants showed the presence of residuals due to the industrial surface treatments. Conclusions: Many structural components of the dental implant surface can influence the wear onset and particles released during the implant placement.

Critical Role of Etching Parameters in the Evolution of Nano Micro SLA Surface on the Ti6Al4V Alloy Dental Implants

The surface of dental implants plays a vital role in early and more predictable osseointegration. SLA (sandblasted large grit and acid-etched) represents the most widely accepted, long-term clinically proven surface. Primarily, dental implants are manufactured by either commercially pure titanium (CP-Ti) or Ti6Al4V ELI alloy. The acid etch behavior of CP-Ti is well known and its effects on the surface microstructure and physicochemical properties have been studied by various researchers in the past. However, there is a lack of studies showing the effect of acid etching parameters on the Ti6Al4V alloy surface. The requirement of the narrow diameter implants necessitates implant manufacturing from alloys due to their high mechanical properties. Hence, it is necessary to have an insight on the behavior of acid etching of the alloy surface as it might be different due to changed compositions and microstructure, which can further influence the osseointegration process. The present research was carried out to study the effect of acid etching parameters on Ti6Al4V ELI alloy surface properties and the optimization of process parameters to produce micro- and nanotopography on the dental implant surface. This study shows that the Ti6Al4V ELI alloy depicts an entirely different surface topography compared to CP-Ti. Moreover, the surface topography of the Ti6Al4V ELI alloy was also different when etching was done at room temperature compared to high temperature, which in turn affected the behavior of the cell on these surfaces. Both microns and nano-level topography were achieved through the optimized parameters of acid etching on Ti6Al4V ELI alloy dental implant surface along with improved roughness, hydrophilicity, and enhanced cytocompatibility.