The effect of nanocoatings of SiO2, TiO2, and ZrO2 on titanium-porcelain bonding

Duplex Fluorinated and Atomic Layer Deposition-Derived ZrO2 Coatings Improve the Corrosion Resistance and Mechanical Properties of Mg-2Zn-0.46Y-0.5Nd (wt.%) Alloy Plates and Screws

This study investigated the corrosion resistance and mechanical properties of Mg-2Zn-0.46Y-0.5Nd (wt.%) alloy plates and screws with fluorinated coatings and atomic layer deposition (ALD)-derived zirconia (ZrO2) coatings in vitro under physiological stress conditions. Synthetic polyurethane hemimandible replicas were split and fixed as the following three groups of magnesium alloy plates and screws: no additional surface coating treatment (Group A), with fluorinated coatings (Group B), and with duplex fluorinated and ALD-derived 100 nm ZrO2 coatings (Group C). A circulating stress of 1-10 N was applied to the distal bone segment, and a 4-week simulated body fluid immersion test was employed to study the remaining material volume and the mechanical properties of the different groups. Compared with Group A and Group B, the degradation rate of magnesium alloy plates and screws' head regions was significantly slowed down under the protection of duplex MgF2/ZrO2 coatings (p < 0.01). There was no significant difference in the degradation rate of the screw shaft region between groups (p = 0.077). In contrast to fluoride coatings, duplex MgF2/ZrO2 coatings maintained the mechanical strength of magnesium alloy plates and screws after a 14 day in vitro SBF immersion test. We conclude that duplex MgF2/ZrO2 coatings exhibited a certain protective effect on the Mg alloy plates and screws under physiological stress conditions.

Effect of different production techniques on the color of porcelain-fused-to-titanium restorations

In dentistry, the shade selection of the restoration affects the success of the restoration. For this reason, it may be decisive for clinicians to determine whether the difference in framework production influences color in metal-ceramic restorations. The study examined the effects of different framework production techniques used in porcelain-fused-to-titanium restorations on color changes. 45 square-shaped samples were manufactured using cast, milling, and laser-sintering techniques. Opaque and dentin porcelain were performed, and all samples were glazed. A spectrophotometer was used for color measurements. Before opaque application, after opaque application, and after porcelain + glaze application, it was obtained L*, a*, and b* values. Color differences (ΔE00) were calculated with the CIEDE2000 formula. ANOVA (Post Hoc: Bonferroni) and Shapiro Wilks (Normality) tests were used for statistical analysis (p < 0.05). At the different laboratory steps, the difference between cast&laser-sintered groups and between milled&laser-sintered groups was statistically significant (p < 0.05). Before and after opaque application, the differences in L*, a*, and b* values between cast, milled, and laser-sintered groups were statistically significant (p < 0.05). Different framework production methods influenced the color of porcelain-fused-to-titanium restorations.

Marginal fit and fracture resistance of polyetheretherketone, zirconia, and titanium implant-supported prosthesis frameworks for a partially edentulous arch after thermomechanical aging

STATEMENT OF PROBLEM

Although polyetheretherketone (PEEK) and zirconia (Zir) have been used as implant-supported prosthesis (ISP) frameworks, the long-term effects of thermomechanical aging on the marginal fit and fracture resistance of PEEK and Zir ISP frameworks with titanium (Ti) bases for patients with a partially edentulous arch are not clear.

PURPOSE

The purpose of this in vitro study was to determine the marginal fit and fracture resistance of PEEK and Zir ISP frameworks with Ti bases and Ti ISP frameworks for partially edentulous arches after aging.

MATERIAL AND METHODS

A total of 30 ISP epoxy resin casts were obtained from a typodont with 1 straight implant (Nobel Biocare) in the mandibular right canine region and 1 implant with a 30-degree distal tilt in the mandibular right first molar region. All frameworks (n=10) were fabricated on their own epoxy resin cast with multiunit abutment replicas by using a computer-aided design and computer-aided manufacturing system (exocad-Yenadent). The PEEK and Zir frameworks were fabricated with Ti-bases. Primer (MKZ) and resin cement (DTK adhesive) were used to cement the frameworks to the Ti-bases under a static load of 10 N. After thermomechanical aging (1.2×106 cycles, 120 N, 5 °C-55 °C), marginal gaps between the Ti-bases and cemented frameworks and vertical and passive fits between the Ti-bases and framework and multi-unit abutments were measured by using a stereomicroscope (Euromex) at ×100 magnification. Fracture resistances and types were then determined by using a universal test machine and a stereomicroscope at ×40 magnification. Data were analyzed by using 1-way analysis of variance (ANOVA) and the Tukey HSD and Fisher-Freeman-Halton tests (α=.05).

RESULTS

The marginal gaps of the PEEK and Zir frameworks were respectively 83.5 ±27.1 and 81.8 ±17.8 µm. PEEK (23.7 ±4.6) and Zir (32.9 ±8.7) had a better vertical fit (µm) than Ti (52.5 ±10.6) (P<.001). Zir (49.3 ±16.2) (P<.001) and PEEK (70.9 ±19.6) (P>.05) frameworks had better passive fit (µm) than Ti (91.3 ±24.2). Ti had the highest mean fracture resistance (N) (14800.2 ±3442.3) followed by Zir (7318.7 ±1385.1) and PEEK (3448.9 ±486.6) (P<.001). Fracture types were different in different groups (P<.001).

CONCLUSIONS

The PEEK and Zir frameworks with Ti bases had better vertical and passive fit than the Ti frameworks. All ISP frameworks represented mean marginal fit below 92 µm and withstood physiologic occlusal forces after thermomechanical aging.