Effects of long-term cinnamaldehyde immersion on the surface roughness and color of heat-polymerized denture base resin

Effect of post-curing conditions on surface characteristics, physico-mechanical properties, and cytotoxicity of a 3D-printed denture base polymer

OBJECTIVE

This study aims to investigate the influence of post-polymerization (post-curing) conditions on surface characteristics, flexural properties, water sorption and solubility, and cytotoxicity of additively manufactured denture base materials.

METHODS

The tested specimens were additively manufactured using digital light processing and classified into different post-curing condition groups: submerged in water (WAT), submerged in glycerin (GLY), and air exposure (AIR). An uncured specimen (UNC) was used as a control. The surface topography and roughness were observed. The flexural strength and modulus were determined via a three-point bending test. The water sorption and solubility were subsequently tested. Finally, an extract test was performed to assess cytotoxicity.

RESULTS

Different post-curing conditions had no significant effects on the surface topography and roughness (Sa value). Various post-curing conditions also had no significant effects on the flexural strength. Notably, the flexural modulus of the WAT group (2671.80 ± 139.42 MPa) was significantly higher than the AIR group (2197.47 ± 197.93 MPa, p = 0.0103). After different post-curing conditions, the water sorption and solubility of the specimens met the ISO standards. Finally, all post-curing conditions effectively reduced cytotoxic effects.

SIGNIFICANCES

Post-curing with different oxygen levels improved flexural properties, and flexural modulus significantly increased after the specimens were submerged in water. In addition, water sorption and solubility, and cytocompatibility were optimized by post-curing, irrespective of the post-curing conditions. Therefore, the water-submerged conditions optimized the flexural modulus of the 3D-printed denture base materials.

The Effect of Aging on Artificial Saliva at Different pH Values on the Color Stability of New Generation Denture Base Materials

STATEMENT OF PROBLEM

New-generation denture base materials are used successfully in denture fabrication; however, the effect of saliva pH change on the color stability of materials is unknown.

PURPOSE

The purpose of this in vitro study is to evaluate the color stability of new-generation denture base materials after immersion in artificial saliva with different pH values (3,7,14).

MATERIAL AND METHODS

Disc-shaped samples (Ø 10 mm x 2 mm) were prepared from three different denture base materials (1 pre-polymerized polymethylmethacrylate [PMMA], 1 graphene-reinforced PMMA, and heat-cure polymethyl methacrylate resin) (n=10). After polishing, color coordinates were measured using a PCE-CSM 5 colorimeter programmed in the CIE system (L* a* b*). The samples were kept in artificial saliva at different pH values and 37°C for 21 days. At the end of 21 days, color coordinates were measured again. The suitability of the measurements for a normal distribution was examined with the Kolmogro-Smirnov test. Whether color measurements obtained at different pH levels differed according to groups was examined with the Kruskal-Wallis test. The correlation between the CIEDE2000 and CIELab color difference formulas was examined by correlation analysis.

RESULTS

The highest color difference occurred in heat-cure samples at pH 3 (p<0.001). The color difference at different pH values was least observed in pre-polymerized PMMA samples. Significant color differences occurred in the graphene-reinforced pre-polymerized PMMA group at pH 7 (p<0.001).

CONCLUSIONS

It was observed that color differences occurred in all groups. Dentures made of new-generation CAD/CAM PMMA, which are less exposed to color differences, can be recommended for elderly patients with systemic diseases who are frequently exposed to pH changes in the oral cavity.

CLINICAL IMPLICATIONS

Color differences on denture surfaces over time negatively affect aesthetics. Since pH changes cause changes on the prosthesis surface, it may be recommended for these patients to fabricate dentures from new-generation CAD/CAM PMMA resins, which are less deformable.