Study and Optimization on graft polymerization under normal pressure and air atmospheric conditions, and its application to metal adsorbent

Recent progress in environmental applications of functional adsorbent prepared by radiation techniques: A review

Environmental pollution has been accelerated due to fast urbanization and industrialization, and thus hazardous contaminants removal and valuable metal recovery have become urgent. Adsorption has become a promising technology for water treatment because of its advantages of low-cost, good reusability, low energy consumption, high capacity and high selectivity. Particularly, radiation techniques including radiation induced graft copolymerization and radiation crosslinking have been found to be widely utilized to exploit adsorbents for water treatment. In this review, the current status and progress of adsorbents in environmental pollution in the past decade are summarized, including adsorbents (in form of particles, fiber and fabric, membrane, novel nanomaterials) synthesized by radiation induced graft copolymerization and hydrogel-based adsorbents fabricated by radiation crosslinking. Finally, further perspective on the development and challenge of adsorbents by radiation techniques is also suggested.

Synthesis of Fibrous Metal Adsorbent with a Piperazinyl-Dithiocarbamate Group by Radiation-Induced Grafting and Its Performance

A fibrous grafted metal adsorbent with a piperazinyl-dithiocarbamate (PZ-DTC) group was synthesized by radiation-induced emulsion grafting of glycidyl methacrylate onto a polyethylene-coated polypropylene nonwoven fabric (PE/PP-NF) and subsequent three-step chemical modifications consisting of amination with N-(tert-butoxycarbonyl)piperazine (N-Boc-piperazine, NBPZ), deprotection of the Boc group with HCl, and dithiocarbamation with carbon disulfide (CS2). By using the NBPZ reagent in the amination step, the self-cross-linking of piperazine (PZ) could be completely suppressed, unlike using the PZ reagent. Consequently, the PZ-DTC group density of the fibrous grafted metal adsorbent synthesized through NBPZ attained 2.122 mmol-PZ-DTC/g-adsorbent, which was approximately 6 times higher than that of the metal adsorbent synthesized through PZ. The fibrous grafted metal adsorbent with the PZ-DTC group selectively adsorbed heavy metal ions over light metal ions. Furthermore, it exhibited high adsorption capacity, particularly for Cu2+. The Cu2+ adsorption capacity was determined to be 1.903 mmol-Cu2+/g-adsorbent by a batchwise adsorption test using a single-metal-ion aqueous solution at pH 6. The order of metal ion selectivity of the fibrous grafted metal adsorbent with the PZ-DTC group was Na+ < Mg2+, Ca2+, Co2+, Cd2+ < Pb2+ ≪ Cu2+, and Co2+ ≈ Ni2+ < Zn2+ ≪ Cu2+. In addition, the fibrous grafted metal adsorbent with the PZ-DTC group did not lose its metal adsorption function even under highly alkaline conditions (pH 15). It could recover Cu2+ efficiently and selectively from a high-concentration Na+ aqueous solution at this pH. The Cu2+ adsorption capacity of the fibrous grafted metal adsorbent with the PZ-DTC group was 0.754 mmol-Cu2+/g-adsorbent under a highly alkaline condition, a 10 M NaOH aqueous solution at pH 15. This value was approximately 2.4 times higher than that of the other grafted adsorbent with an amine-type functional group.

Development of a Simplified Radiation-Induced Emulsion Graft Polymerization Method and Its Application to the Fabrication of a Heavy Metal Adsorbent

A simplified radiation-induced emulsion graft polymerization (SREG) method is proposed. This method involves a convenient and easy degassing process of a monomer solution using a commercially available sealed glass jar. A loaded weight on the lid of the jar was used to control the jar's internal pressure as the degassing of the monomer solution took place using a vacuum pump. The degassing method was highly reproducible, resulting from no bumping of the monomer solution. The initial grafting velocity was proportional to the absorbed doses of pre-irradiation between 5 and 20 kGy. This result indicates that dissolved oxygen was sufficiently eliminated from the monomer solution at such a level where the remaining oxygen had little effect on the grafting reaction at a dose of 5 kGy. The method was then applied to the fabrication of a heavy metal adsorbent that possessed a sufficient adsorption capacity of Co(II) ions. The SREG method is applicable to the fabrication of a wide variety of functional graft polymers because high-dose-rate gamma-ray radiation and expensive experimental equipment are not necessary.