Investigation of gamma ray shielding, structural and dissolution rate properties of Bi 2 O 3 -BaO-B 2 O 3 -Na 2 O glass system

Impact of bismuth oxide on structural, optical and gamma-ray shielding properties of calcium-sodium-borate glasses

In the present study, we have prepared six glass samples of bismuth borate using the melt-quenching method with the composition (70-x)B2O3-10CaO-20Na2O-xBi2O3; x = 0, 3, 6, 9, 12 and 15 mol%. The density of the prepared glasses was determined using Archimedes principle. The X-ray diffraction patterns provide confirmation of the amorphous nature of the prepared samples, whereas the Fourier transform infrared measurements pointed to the existence of structural units like BO3, BO4, BiO3 and BiO6 within the glass network. An assessment of the optical absorption spectra unveiled that with the increase in the bismuth oxide content, there was a decrease observed in both the direct and indirect band gap energies. Specifically, they decreased from 3.40 to 2.79 eV and from 3.10 to 2.46 eV, respectively. The properties related to gamma ray attenuation, including the mass attenuation coefficient (μm), effective atomic number (Zeff), half-value layer (HVL) and mean free path (MFP), were examined for all the glass samples. This investigation was carried out using the Phy-X/PSD software, covering the energy range from 0.511 to 1.332 MeV. Out of all the samples, Bi-15, featuring the highest Bi2O3 content, demonstrated the highest μm, Zeff, the smallest HVL and MFP. These results suggest that the glass with 15 mol% of Bi2O3 offers the most effective gamma radiation shielding performance. Moreover, the glasses examined in this study exhibit superior radiation shielding characteristics compared with specific concrete types, namely, ordinary concrete, Hematite serpentine concrete and barite concrete, as well as commercial glasses such as RS-360 and RS-253.

Investigations on Structural and Optical Properties of Various Modifier Oxides (MO = ZnO, CdO, BaO, and PbO) Containing Bismuth Borate Lithium Glasses

Bismuth based quaternary glasses with compositions BiBLM: 50Bi2O3–20B2O3–15Li2O–15MO (where MO = ZnO, CdO, BaO, and PbO) were processed by conventional melt quenching. The effectiveness of various modifier oxides on the optical and structural properties of the developed glasses was studied systematically by XRD, DSC, FTIR, Raman, and optical absorption (OA) measurements. The synthesized glass specimens were characterized by XRD and the patterns demonstrated an amorphous nature. The physical characteristics such as molar mass, density, and OPD values were found to increase with an increase in the molar mass of the modifier oxides, while there was a decrement in oxygen molar volume, thus resulting in decrement of complete molar volume of the prepared glasses. From DSC analysis, incorrigible reduction and enhancement of Tg and thermal stability among various modifier oxides in the glass network was noticed. Optical absorption data for glass specimens have confirmed the decrease in both direct and indirect optical band gap values among various modifier oxides incorporation. These investigations support the obtained Urbach energy (UE) and metallization criteria of synthesized glasses. The ionic characteristic for the glass specimens were confirmed by the values of electronic polarizability and electronegativity. The Raman and FT-IR spectra of the glass specimens displayed the existence of BiO3, BiO6, ZnO4, CdO4, BaO4, BO3, PbO4, and BO4 structural units within the glass matrix. These structural results can support the applications of as-developed glasses in the area of photonics.