Appropriate pore size for bone formation potential of porous collagen type I-based recombinant peptide

3D printed polycaprolactone scaffold incorporated with tragacanth gum/bioactive glass and cellulose nanocrystals for bone tissue engineering

Biomimetic organic-inorganic nanocomposite scaffolds hold tremendous potential to accelerate bone regeneration due to their ability to provide excellent structural and biological cues. Therefore, we employed a 3D-printed polycaprolactone host component as a mechanical support that was filled with a tragacanth gum-45S5 bioactive glass-cellulose nanocrystal guest component. The designed host-guest scaffolds were evaluated via physical, chemical, mechanical, and biological properties. Owing to the successful integration between host and guest components, the scaffolds showed enhanced physical and swelling properties (approximately 100 %) for nutrient transfer and cell proliferation. Furthermore, the host-guest scaffolds exhibited improved surface apatite formation and increased strength (3.35-16.55 MPa) within the ideal range for bone tissue engineering applications. It was verified in vitro that the host-guest scaffolds offer a highly desirable microenvironment for cell proliferation and attachment. Importantly, the host-guest scaffolds exhibited remarkable calcium deposition (4-56 %) and matrix formation. However, it was found that the proportion of cellulose nanocrystals can affect the properties of fabricated host-guest scaffolds. These results highlight the importance of optimizing the cellulose nanocrystal content in the scaffold composition to achieve the desired balance of properties for effective bone tissue engineering applications. The incorporation of cellulose nanocrystals at lower concentrations, particularly 3 wt%, represents a promising approach for developing biomimetic scaffolds that can enhance bone regeneration. Notably, the results of this study confirmed that incorporating cellulose nanocrystals at lower concentrations into the host-guest scaffolds is a viable strategy for fabricating a suitable biomaterial that enhances bone tissue engineering applications.

Teicoplanin-Decorated Reduced Graphene Oxide Incorporated Silk Protein Hybrid Hydrogel for Accelerating Infectious Diabetic Wound Healing and Preventing Diabetic Foot Osteomyelitis

Developing hybrid hydrogel dressings with anti-inflammatory, antioxidant, angiogenetic, and antibiofilm activities with higher bone tissue penetrability to accelerate diabetic wound healing and prevent diabetic foot osteomyelitis (DFO) is highly desirable in managing diabetic wounds. Herein, the glycopeptide teicoplanin is used for the first time as a green reductant to chemically reduce graphene oxide (GO). The resulting teicoplanin-decorated reduced graphene oxide (rGO) is incorporated into a mixture of silk proteins (SP) and crosslinked with genipin to yield a physicochemically crosslinked rGO-SP hybrid hydrogel. This hybrid hydrogel exhibits high porosity, self-healing, shear-induced thinning, increased cell proliferation and migration, and mechanical properties suitable for tissue engineering. Moreover, the hybrid hydrogel eradicates bacterial biofilms with a high penetrability index in agar and hydroxyapatite disks covered with biofilms, mimicking bone tissue. In vivo, the hybrid hydrogel accelerates the healing of noninfected wounds in a diabetic rat and infected wounds in a diabetic mouse by upregulating anti-inflammatory cytokines and downregulating matrix metalloproteinase-9, promoting M2 macrophage polarization and angiogenesis. The implantation of hybrid hydrogel into the infected site of mouse tibia improves bone regeneration. Hence, the rGO-SP hybrid hydrogel can be a promising wound dressing for treating infectious diabetic wounds, providing a further advantage in preventing DFO.

Bioactive gelatin-sheets as novel biopapers to support prevascularization organized by laser-assisted bioprinting for bone tissue engineering

Despite significant advances in the management of patients with oral cancer, maxillofacial reconstruction after ablative surgery remains a clinical challenge. In bone tissue engineering, biofabrication strategies have been proposed as promising alternatives to solve issues associated with current therapies and to produce bone substitutes that mimic both the structure and function of native bone. Among them, laser-assisted bioprinting (LAB) has emerged as a relevant biofabrication method to print living cells and biomaterials with micrometric resolution onto a receiving substrate, also called 'biopaper'. Recent studies have demonstrated the benefits of prevascularization using LAB to promote vascularization and bone regeneration, but mechanical and biological optimization of the biopaper are needed. The aim of this study was to apply gelatin-sheet fabrication process to the development of a novel biopaper able to support prevascularization organized by LAB for bone tissue engineering applications. Gelatin-based sheets incorporating bioactive glasses (BGs) were produced using various freezing methods and crosslinking (CL) parameters. The different formulations were characterized in terms of microstructural, physical, mechanical, and biological properties in monoculture and coculture. Based on multi-criteria analysis, a rank scoring method was used to identify the most relevant formulations. The selected biopaper underwent additional characterization regarding its ability to support mineralization and vasculogenesis, its bioactivity potential andin vivodegradability. The biopaper 'Gel5wt% BG1wt%-slow freezing-CL160 °C 24 h' was selected as the best candidate, due to its suitable properties including high porosity (91.69 ± 1.55%), swelling ratio (91.61 ± 0.60%), Young modulus (3.97 × 104± 0.97 × 104Pa) but also its great cytocompatibility, osteogenesis and bioactivity properties. The preorganization of human umbilical vein endothelial cell using LAB onto this new biopaper led to the formation of microvascular networks. This biopaper was also shown to be compatible with 3D-molding and 3D-stacking strategies. This work allowed the development of a novel biopaper adapted to LAB with great potential for vascularized bone biofabrication.

Ca-AlN MOFs-loaded chitosan/gelatin scaffolds; a dual-delivery system for bone tissue engineering applications

Creating a scaffold for bone tissue engineering that is bioactive and capable of acting as a local-dual delivery system, releasing bioactive molecules and regulating the bone remodeling process to achieve balanced bone resorption and formation, is a significant challenge. The objective of this research is to create a composite scaffold using chitosan/gelatin (CHS/Gel) and the calcium (Ca)-alendronate (ALN) metal-organic frameworks (MOFs). The scaffold will act as a dual-delivery system, releasing Ca ions and ALN to regulate bone formation. Ca-ALN MOF nanoparticles (NPs) were prepared in mild conditions and studied by FTIR, XRD, FESEM, and TGA. Ca-ALN NPs-loaded CHS/Gel scaffolds were opportunely fabricated through freeze-drying approach. Physicochemical features of the scaffolds after incorporating NPs equated by CHS/Gel scaffold changed, therefore, the attendance of NPs caused a decreasing porosity, decreased swelling, and low rate of degradation. The release profile results showed that the NPs-loaded CHS/Gel scaffolds were able to simultaneously release ALN and Ca ions due to the decomposition of NPs. Additionally, the loading of NPs in the CHS/Gel scaffold led to an increment in alkaline phosphatase (ALP) activity and the quantity of deposited Ca along with osteogenesis gene markers. These findings suggest that the NPs-loaded CHS/Gel scaffold has the potential to enhance the differentiation of human adipose tissue-derived mesenchymal stem cells, making it a promising approach for bone repair.

Collagen type I-based recombinant peptide promotes bone regeneration in rat critical-size calvarial defects by enhancing osteoclast activity at late stages of healing

Introduction

We recently demonstrated the bone-forming potential of medium-cross-linked recombinant collagen peptide (mRCP) in animal models of bone defects. However, these studies were limited to a 4-week observation period; therefore, in the present study, we aimed to further evaluate mRCP as a suitable bone graft material for the alveolar cleft by analyzing its bone-forming potential, osteogenic-inducing ability, and biodegradation over an extended period of 12 weeks, using a rat critical-size calvarial defect model.

Methods

Using Sprague-Dawley rats, we created critical-size calvarial defects through a surgical procedure. The defects were then filled with 3 mg of mRCP (mRCP group) or 18 mg of Cytrans® (CA) granules, which has a carbonate apatite-based composition resembling natural bone, was used as a reference material (CA group). For negative control, the defects were left untreated. Bone volume, total bone volume (bone volume including CA granules), and bone mineral density (BMD) in the defect were assessed using micro-computed tomography (μ-CT) at 0, 4, 8, and 12 weeks after implantation. Using histomorphometric analyses of hematoxylin and eosin (H&E)-stained sections, we measured the amount of newly formed bone and total newly formed bone (new bone including CA granules) in the entire defect site, as well as the amount of newly formed bone in the central side, two peripheral sides (left and right), periosteal (top) side, and dura mater (bottom) side. In addition, we measured the amount of residual bone graft material in the defect. Osteoclasts and osteoblasts in the newly formed bone were detected using tartrate-resistant acid phosphatase (TRAP) and alkaline phosphatase (ALP) staining, respectively.

Results

Bone volume in the mRCP group increased over time and was significantly larger at 8 and 12 weeks after surgery than at 4 weeks. The bone volume in the mRCP group was greater than that of the CA and control groups at 4, 8, and 12 weeks after implantation, and while the total bone volume was greater in the CA group after 4 and 8 weeks, the mRCP group had comparable levels of total bone volume to that of the CA group at 12 weeks after implantation. The BMD of the mRCP group reached similar levels to native calvaria bone at the same time point. H&E-stained sections revealed a larger amount of newly formed bone 12 weeks after implantation in the mRCP group compared to that of the CA and control groups. The total newly formed bone at 12 weeks after implantation was on par with that in the CA group. Furthermore, at the defect site, the area of newly formed bone was larger on the peripheral and dura mater sides. Notably, the number of osteoclasts in the mRCP group was higher than in the CA and control groups and peaked 8 weeks after implantation, which coincided with the timing of the greatest resorption of mRCP. Although the ALP-positive area was greater in the mRCP group compared to other groups, we did not detect any significant changes in the number of osteoblasts over time.

Conclusion

This study demonstrated the bone-forming potential of mRCP over an extended period of 12 weeks, suggesting that mRCP sufficiently resists resorption to promote bone formation through induction of osteoclast activation in the late stages of the healing period.