Spectral properties of Er3+/Yb3+ codoped tungsten-tellurite glasses

Thermal stability and spectroscopic properties of Er3+-doped antimony-borosilicate glasses

This paper reports on the optical spectroscopic properties and thermal stability of Er3+-doped antimony-borosilicate glasses for developing 1.5 microm optical amplifiers. Upon excitation at 980 nm laser diode, an intense 1.5 microm infrared fluorescence has been observed with the maximum full width at half maximum (FWHM) of 90 nm for Er3+-doped antimony-borosilicate glasses. The emission cross-section and the lifetime of the 4I13/2 level of Er3+ ions are 6.3 x 10(-21) cm2 and 0.30 ms, respectively. It is noted that the product of the emission cross-section and FWHM of the glass studied is as great as 567 x 10(-21) cm2 nm, which is comparable or higher than that of bismuthate and tellurite glasses.

Spectroscopic properties of Nd3+ doped transparent oxyfluoride glass ceramics

In this paper, the spectroscopic properties of Nd(3+) doped transparent oxyfluoride glass ceramics containing LaF(3) nano-crystals were systematically studied. The formation and distribution of LaF(3) nano-crystals in the glass matrix were investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Based on Judd-Ofelt theory, the intensity parameters Omega(t) (t=2, 4, 6), spontaneous emission probability, radiative lifetime, radiative quantum efficiency, width of the emission line and stimulated emission cross-section of Nd(3+) were evaluated. Particularly, the effect of Nd(3+) doping level on them was discussed. With the increase of Nd(3+) concentration in the glass ceramic, the experimental luminescence lifetime, radiative quantum efficiency and stimulated emission cross-section vary from 353.4 micros, 78.3% and 1.86 x 10(-20)cm(2) to 214.7 micros, 39.9% and 1.52 x 10(-20)cm(2), respectively. The comparative study of Nd(3+) spectroscopic parameters in different hosts suggests that the investigated glass ceramic system is potentially applicable as laser materials for 1.06 microm emission.

Spectroscopic properties of Er(3+)/Yb(3+) co-doped Bi(2)O(3)-B(2)O(3)-GeO(2) glasses

Er(3+)/Yb(3+) co-doped 60Bi(2)O(3)-(40 - x)B(2)O(3)-xGeO(2) (BBG; x=0, 5, 10, 15 mol%) glasses that are suitable for fiber lasers, amplifiers have been fabricated and characterized. The absorption spectra, emission spectra, and lifetime of the (4)I(13/2) level and quantum efficiency of Er(3+):(4)I(13/2) --> (4)I(15/2) transition were measured and calculated. With the substitution of GeO(2) for B(2)O(3), both Delta lambda(eff) and sigma(e) decrease from 75 to 71 nm and 9.88 to 8.12 x 10(-21) cm(2), respectively. The measured lifetime of the (4)I(13/2) level and quantum efficiency of Er(3+):(4)I(13/2) --> (4)I(15/2) transition increase from 1.18 to 1.5 ms and 36.2% to 43.2%, respectively. The emission spectra of Er(3+):(4)I(13/2) --> (4)I(15/2) transition was also analyzed using a peak-fit routine, and an equivalent four-level system was proposed to estimate the stark splitting for the (4)I(15/2) and (4)I(13/2) levels of Er(3+) in the BBG glasses. The results indicate that the (4)I(13/2) --> (4)I(15/2) emission of Er(3+) can be exhibit a considerable broadening due to a significant enhance the peak A, and D emission.