In situ formation of Ca(OH)2 coating shell to extend the longevity of zero-valent iron biochar composite derived from Fe-rich sludge for aqueous phosphorus removal

Efficient Adsorption of Nitrogen and Phosphorus in Wastewater by Biochar

Nitrogen and phosphorus play essential roles in ecosystems and organisms. However, with the development of industry and agriculture in recent years, excessive N and P have flowed into water bodies, leading to eutrophication, algal proliferation, and red tides, which are harmful to aquatic organisms. Biochar has a high specific surface area, abundant functional groups, and porous structure, which can effectively adsorb nitrogen and phosphorus in water, thus reducing environmental pollution, achieving the reusability of elements. This article provides an overview of the preparation of biochar, modification methods of biochar, advancements in the adsorption of nitrogen and phosphorus by biochar, factors influencing the adsorption of nitrogen and phosphorus in water by biochar, as well as reusability and adsorption mechanisms. Furthermore, the difficulties encountered and future research directions regarding the adsorption of nitrogen and phosphorus by biochar were proposed, providing references for the future application of biochar in nitrogen and phosphorus adsorption.

Performance of novel Ca-biocomposites produced from banana peel and eggshell for highly efficient removal and recovery of phosphate from domestic wastewater

Using biowaste-based adsorbents to remove phosphorus (P) from wastewater offers significant benefits concerning eutrophication mitigation and addressing waste management challenges. In this work, Ca-biocomposites were prepared by pyrolysis (700 °C) of a mixture of banana peel (BP) and eggshell (ES). The mass ratio of BP to ES was varied in 2:1, 1:1, and 1:2 ratios. Among the tested mixtures, the BPES-1:2 sample exhibited excellent P removal performance, reaching a maximum P adsorption capacity (Qmax) of 214 ± 5 mg P/g. The adsorption process fitted well with the Avrami order kinetic model (R2 > 0.996) and the Liu isotherms model (R2 > 0.997). The excellent fit of the experimental data to the Avrami model suggests that chemisorption is the dominant interaction mechanism, leading to precipitation through the formation of calcium phosphates. Additionally, the Liu model anticipates that the energetic characteristics of the adsorbent's active sites cannot be identical. This is in agreement with the presence of Ca(OH)2 and CaCO3 in the adsorbent material, where the Ca(OH)2 active sites are preferred by the adsorbate molecules (PO43-) for occupation. Furthermore, thermodynamic analysis revealed that P adsorption is a spontaneous process of exothermic nature (ΔH° < 0). The calculated activation energy for the process (72.81 kJ/mol) suggests the P adsorption mechanism involves strong chemical bonding between the adsorbent and P species. In addition, precipitation of apatite (Ca5(PO4)3OH), a vital component in fertilizer production, was observed during the adsorption process. In tertiary treated wastewater applications, the BPES-1:2 biocomposite demonstrated a P removal efficiency of 90%. The solubility of P in a 2% formic acid solution was 100%, while the water-soluble P content was measured at 5.6%. These findings highlight the product's sustainable and environmentally beneficial nature by demonstrating its potential as a slow-release fertilizer, contributing to the application of the 3R slogan: Reduce, Reuse, Recycle. This value-added product is promising in supplying nutrients to plants over an extended period while minimizing the risk of nutrients leaching into the environment.